Method for compensating for the E-beam proximity effect
Assignee: HP Inc
•
Filing: 1986-10-08
•
Granted: 1991-01-29
•
Expires: 2006-10-08
Abstract
Abstract A method to compensate for the E-beam proximity effect which includes a post exposure, pre-development baking of the photoresist layer. The baking of the photoresist layer causes a migration of small, photo-active compound (PAC) molecules to increase the size of peripheral exposed areas so as to compensate for the exposure size variations caused by the proximity effect.
Inventors
- 👤 Hua-yu Liu
- 👤 En-Den D. Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:14
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; G03F7/38
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
137 words
A method which helps compensate for the E-beam proximity effect during the production of a mask for a semiconductor substrate comprising the steps of: forming a reactive layer over a semiconductor substrate; exposing portions of said reactive layer with an electron beam to produce exposed portions, whereby the resultant dimensions of said exposed portions are dependent, at least in part, to their relative proximity to adjacent exposed portions due to the E-beam proximity effect; causing a molecular migration within said reactive layer from unexposed portions thereof to adjacent exposed portions thereof, whereby the magnitude of said molecular migration to a particular exposed portion is inversely related to the magnitude of the E-beam proximity effect on that particular exposed portion, thereby at least partially compensating for the effects of said E-beam proximity effect; and developing said reactive layer.
Claim 2
Independent Claim
137 words
A method which helps compensate for the E-beam proximity effect during the production of a mask for a semiconductor substrate comprising the steps of: forming a reactive layer over a semiconductor substrate; exposing portions of said reactive layer with an electron beam to produce exposed portions, whereby the resultant dimensions of said exposed portions are dependent, at least in part, to their relative proximity to adjacent exposed portions due to the E-beam proximity effect; causing a molecular migration within said reactive layer from unexposed portions thereof to adjacent exposed portions thereof, whereby the magnitude of said molecular migration to a particular exposed portion is inversely related to the magnitude of the E-beam proximity effect on that particular exposed portion, thereby at least partially compensating for the effects of said E-beam proximity effect; and developing said reactive layer.
Claim 3
Dependent Claim
36 words
A method for producing a mask as recited in claim 1 wherein said step of forming a reactive layer comprises: applying a reactive material to an upper surface of said substrate; and curing said reactive material.
Claim 4
Dependent Claim
36 words
A method for producing a mask as recited in claim 1 wherein said step of causing a molecular migration within said reactive layer comprises elevating the temperature of said reactive layer for a period of time.
Claim 5
Dependent Claim
25 words
A method for producing a mask as recited in claim 3 wherein said temperature of said reactive layer is raised to at least 100° C.
Claim 6
Dependent Claim
21 words
A method for producing a mask as recited in claim 5 wherein said period of time is at least 30 minutes.
Claim 7
Independent Claim
131 words
A method for at least partially compensating for the E-beam proximity effect comprising the steps of: applying a material having small, mobile photo-sensitizer molecules suspended in a polymer solution to a support surface; curing said material to for a reactive layer over said support surface; exposing portions of said reactive layer with an E-beam, whereby the resultant dimensions of said exposed portions are dependent, at least in part, to their relative proximity to adjacent exposed portions due to the E-beam proximity effect; baking said reactive layer to cause some of said photo-sensitizer molecules to migrate from unexposed portions to adjacent exposed portions of said reactive layer in substantially the inverse proportion to the degree that said exposed portions had been affected by said E-beam proximity effect; and developing said reactive layer.
Claim 8
Independent Claim
131 words
A method for at least partially compensating for the E-beam proximity effect comprising the steps of: applying a material having small, mobile photo-sensitizer molecules suspended in a polymer solution to a support surface; curing said material to for a reactive layer over said support surface; exposing portions of said reactive layer with an E-beam, whereby the resultant dimensions of said exposed portions are dependent, at least in part, to their relative proximity to adjacent exposed portions due to the E-beam proximity effect; baking said reactive layer to cause some of said photo-sensitizer molecules to migrate from unexposed portions to adjacent exposed portions of said reactive layer in substantially the inverse proportion to the degree that said exposed portions had been affected by said E-beam proximity effect; and developing said reactive layer.
Claim 9
Dependent Claim
38 words
A method for producing a mask as recited in claim 6 wherein said step of baking said reactive layer has the additional effect of converting said reactive layer from a positive reactive layer to a negative reactive layer.
Claim 10
Dependent Claim
29 words
A method for producing a mask as recited in claim 6 wherein said step of baking said reactive layer comprises heating said reactive layer to at least 100° C.
Claim 11
Dependent Claim
22 words
A method for producing a mask as recited in claim 6 wherein said reactive layer is baked for at least 30 minutes.
References Cited (Backward Citations)
US4929536A
Cited
US4931381A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-28 | 1994-07-30 | 1995-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-28 | 1998-07-30 | 1999-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-28 | 2002-07-30 | 2003-01-29 | $7700.00 | Window Closed / Lapsed |