Method of preparing silicon compositions
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1989-04-21
•
Granted: 1991-01-22
•
Expires: 2009-04-21
Abstract
Abstract A method of preparing a uniform silicone composition, comprising treating under the application of a shearing force a polymeric product obtained by addition polymerization of (A) an organhydrogenpolysiloxane containing in its molecule from 1.5 to 5 silicon-bonded hydrogen atoms on average, said silicon-bonded hydrogen atoms being in an amount of from 1 to 20 mol %, based on the total of the silicon-bonded hydrogen atoms and silicon-bonded organic groups in the molecule; and (B) an organopolysiloxane containing in its molecule from 1.5 to 5 silicon-bonded aliphatic unsaturated groups on average; in the presence of from 10 to 1,000 parts by weight of low-viscosity silicone oil having a viscosity of not more than 100 cSt at 25 DEG C. based on 100 parts by weight of the total amount of said (A) and (B).
Inventors
- 👤 Satoshi Kuwata
- 👤 Koji Sakuta
- 👤 Shigeru Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 02:09
CPC Classifications
A; A61; A61K; A61K8/00; A61K8/18; A61K8/72; A61K8/84; A61K8/89; A61K8/891; A61K47/00; A61K47/30; A61K47/34; A61Q; A61Q19/00; C; C08; C08L; C08L83/00; C08L83/04; C10; C10M; C10M119/00; C10M119/30; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/70; C10M2229/00; C10M2229/006; C10N; C10N2040/00; C10N2040/50; C10N2050/00; C10N2050/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
132 words
A method of preparing a uniform silicone composition, comprising treating under the application of a shearing force a polymeric product obtained by addition polymerization of (A) on organohydrogenpolysiloxane containing in its molecule from 1.5 to 5 silicon-bonded hydrogen atoms on average, said silicon-bonded hydrogen atoms being in an amount of from 1 to 20 mol %, based on the total of the silicon-bonded hydrogen atoms and silicon-bonded organic groups in the molecule; and (B) an organopolysiloxane containing in its molecule from 1.5 to 5 silicon-bonded aliphatic unsaturated groups on average; in the presence of from 10 to 1,000 parts by weight of low-viscosity silicone oil having a viscosity of not more than 100 cSt at 25° C. based on 100 parts by weight of the total amount of said (A) and (B).
Claim 2
Independent Claim
132 words
A method of preparing a uniform silicone composition, comprising treating under the application of a shearing force a polymeric product obtained by addition polymerization of (A) on organohydrogenpolysiloxane containing in its molecule from 1.5 to 5 silicon-bonded hydrogen atoms on average, said silicon-bonded hydrogen atoms being in an amount of from 1 to 20 mol %, based on the total of the silicon-bonded hydrogen atoms and silicon-bonded organic groups in the molecule; and (B) an organopolysiloxane containing in its molecule from 1.5 to 5 silicon-bonded aliphatic unsaturated groups on average; in the presence of from 10 to 1,000 parts by weight of low-viscosity silicone oil having a viscosity of not more than 100 cSt at 25° C. based on 100 parts by weight of the total amount of said (A) and (B).
Claim 3
Dependent Claim
48 words
The method according to claim 1, wherein said polymeric product is treated under said application of shearing force, together with from 10 to 1,000 parts by weight of the same low-viscosity silicone oil as the above (C), and said silicone composition is obtained in the form of paste.
Claim 4
Dependent Claim
44 words
The method according to claim 1, wherein said addition polymerization is carried out with stirring, in the presence of from 10 to 200 parts by weight of said component (C) low-viscosity silicone oil, and said silicone composition is obtained in the form of powder.
Claim 5
Dependent Claim
59 words
The method according to claim 1, wherein said organohydrogenpolysiloxane (A) has the formula. [(CH.sub.3).sub.3 SiO.sub.0.5 ].sub.a [(CH.sub.3).sub.2 HSi.sub.0.5 ].sub.b [(CH.sub.3).sub.2 SiO].sub.c [(CH.sub.3 HSiO].sub.d wherein a and b are each an integer of from 0 to 2, provided that a+b=2, small c is an integer of from 0 to 500 and d is an integer of from 0 to 50.
Claim 6
Dependent Claim
59 words
The method according to claim 1, wherein said organopolysiloxane (B) has the formula: [(CH.sub.2 ═CH)(CH.sub.3).sub.2 SiO.sub.0.5 ].sub.e [(CH.sub.3).sub.3 SiO.sub.0.5 ].sub.f [(CH.sub.3).sub.2 SiO].sub.g [(CH.sub.2 ═CH)CH.sub.3 SiO].sub.h wherein, e and f are each an integer of from 0 to 2, provided that e+f=2, g is an integer from 0 to 500 and h is an integer of from 0 to 50.
Claim 7
Dependent Claim
23 words
The method according to claim 1, wherein said low-viscosity silicone oil has a viscosity of not more than 50 cSt at 25° C.
Claim 8
Dependent Claim
23 words
The method according to claim 1, wherein said low-viscosity silicone oil has a viscosity of not more than 10 cSt at 25° C.
Claim 9
Dependent Claim
19 words
The method according to claim 1, wherein said organohydrogenpolysiloxane (A) is in the form of a mixture of compounds.
Claim 10
Dependent Claim
19 words
The method according to claim 1, wherein said organopolysiloxane (B) is in the form of a mixture of compounds.
Claim 11
Dependent Claim
29 words
The method according to claim 1, wherein a molar ratio of silicon-bonded hydrogen atoms of (A) to the silicon-bonded aliphatic unsaturated groups of (B) is from 1/3 to 3/1.
Claim 12
Dependent Claim
37 words
The method according to claim 1, wherein said low-viscosity silicone oil is a siloxane having a low degree of polymerization selected from the group of methylpolysiloxane, dimethylpolysiloxane, methylphenylpolysiloxane, ethylpolysiloxane, ethylmethylpolysiloxane, ethylphenylpolysiloxane, octamethylcyclotetrasiloxane and decamethylcyclopentasiloxane and mixtures thereof.
Claim 13
Dependent Claim
29 words
The method according to claim 1, which further comprises effecting said reaction in the presence of a platinum compound or a rhodium compound, as a catalyst, in a solvent.
Claim 14
Dependent Claim
24 words
The method according to claim 1, wherein said compound (A) is selected from the group consisting of trimethylsilyl-terminated dimethylmethylhydrogenpolysiloxane, dimethylhydrogensilyl-terminated dimethylpolysiloxane and trimethylsilyl-terminated dimethylmethylhydrogenpolysiloxane.
Claim 15
Dependent Claim
22 words
The method according to claim 1, wherein said compound (B) is selected from the group consisting of dimethylvinylsilyl-terminated dimethylpolysiloxane and trimethylsilyl-terminated dimethylmethylvinylpolysiloxane.
Claim 16
Dependent Claim
22 words
The method according to claim 1, wherein said low-viscosity silicone oil is selected from the group consisting of phenyltris(trimethylsiloxy) silane and octamethyltrisiloxane.
Claim 17
Dependent Claim
11 words
The method according to claim 1, wherein said catalyst is chloroplatinate.
References Cited (Backward Citations)
US4806430A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-21 | 1994-07-23 | 1995-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-21 | 1998-07-23 | 1999-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-21 | 2002-07-23 | 2003-01-22 | $7700.00 | Window Closed / Lapsed |