Abstract An oxidation process for stabilization of pitch-based matrices in the fabrication of carbon-carbon composites. By oxidizing a fiber preform impregnated with petroleum-derived mesophase pitch at temperatures in the range of 190° to 300° C. for periods of the order of ten hours, the matrix is fixed in place within the preform so that softening, bloating, and expulsion of the matrix are avoided when the body is carbonized. The invention can also be practiced to increase the carbon yield upon carbonization. Sufficient access porosity must exist in the matrix to permit oxidation throughout the composite body; this is normally formed in a preform due to the mismatch in thermal expansivities of fiber and matrix. Also, the softening point of the pitch must be above the oxidation temperature; this need can be met for most mesophase pitches. The process of oxidation stabilization can also be applied to isotropic pitches if these requirements are met, and to pitch derived from coal tar or other sources if the pitch is susceptible to oxidation. This invention may be practiced to reduce the time and cost of pitch-based composite fabrication, to eliminate the need for high-pressure carbonization, and thus to make pitch-based fabrication practical for large composite structures.
A process for the fabrication of carbon fiber reinforced carbon matrix composites to a desired shape comprising the steps of: a. configuring a lattice-work of carbon fibers to the desired shape of a reinforced composite; b. infiltrating the lattice-work with a pitch based matrix precursor; c. oxidizing the infiltrated lattice-work to stabilize the matrix during subsequent carbonization; and, d. carbonizing the infiltrated, oxidized lattice-work.
Claim 2
Dependent Claim
64 words
A process for the fabrication of carbon fiber reinforced carbon matrix composites to a desired shape comprising the steps of: a. configuring a lattice-work of carbon fibers to the desired shape of a reinforced composite; b. infiltrating the lattice-work with a pitch based matrix precursor; c. oxidizing the infiltrated lattice-work to stabilize the matrix during subsequent carbonization; and, d. carbonizing the infiltrated, oxidized lattice-work.
Claim 3
Dependent Claim
45 words
The process as defined in claim 1 wherein the oxidation of the pitch based precursor is performed at a temperature from about 190° to 300° C. and at ambient pressure, thereby minimizing dimensional change of the shaped composite and maximizing carbon yield of the precursor.
Claim 4
Dependent Claim
44 words
The process as defined in claim 2 wherein the oxidation of pitch based precursor is carried out for a time whereas the dimensional change of the shaped composite and carbon yield of the precursor after carbonization are optimized, said time being approximately ten hours.
Claim 5
Dependent Claim
47 words
The process as defined in claim 1 wherein the lattice-work is impregnated by a series of partial impregnations and each of said series is oxidized in sequence; and the carbonization of the matrix precursor is performed after the last of said series of partial impregnations is oxidized.
Claim 6
Dependent Claim
20 words
The process as defined in claim 1 wherein exposure to oxygen is controlled to maximize the carbon yield in carbonization.
Claim 7
Dependent Claim
27 words
The process of claim 1 wherein the time and temperature of exposure to oxygen is controlled to minimize the dimensional change of the shaped composite during carbonization.