Abstract
Abstract This invention relates to modified polyetheramide hotmelt adhesives showing reduced melt viscosity and, optionally, better adhesive properties and to their use as ingredients for hotmelt adhesives.
Inventors
- 👤 Hans-Detlef Heinz
- 👤 Eduard Hansel
- 👤 Rolf-Volker Meyer
- 👤 Gunter Arend
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:55
CPC Classifications
C; C09; C09J; C09J177/00; C08; C08G; C08G69/00; C08G69/40; C08G69/44; C08L; C08L101/00
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
287 words
Polyetheramide hotmelt adhesives having acid values in the range from 4 to 20, relative viscosities (1% by weight solutions in m-cresol at 25° C.) in the range from 1.3 to 2.5, softening points in the range from 100° to 200° C. and melt viscosities in the range from 100° to 190° C. at 200° C. wherein the polyetheramide hot melt adhesives are prepared from the reaction of (1) 40 to 75% by weight of polyamide-forming components comprising caprolactam, ε-amino-caproic acid or a mixture thereof, (2) 25 to 60% per weight of a mixture of components (a) to (c) in the stated equivalent ratios of (a) 0.95 to 1.05 equivalents comprising one or more compounds selected from the group of aliphatic and aromatic C 4 -C 34 dicarboxylic acids, (b) 0.2 to 0.9 equivalents comprising one or more compounds selected from the group of aliphatic and cycloaliphatic C 6 -C 25 -diamines (c) 0.1 to 0.8 equivalents of one or more polyoxyalkylene diols having molecular weights (Mn) in the range from 200 to 1000 g mol -1 , wherein the terminal groups are OH groups, terminal primary amine groups or a mixture thereof, where the sum of equivalents (b+c)=1, and (3) 0 to 15% by weight of a lactam and aminocarboxylic acids different from caprolactam and aminocaproic acid wherein chain terminators corresponding to general formula (1) R--Y (1) in which R is an optionally branched, saturated or unsaturated, optionally substituted alkyl radical having a length of 12 to 40 C atoms, and Y is one of the groups --NH.sub.2 (II) --COOH (III) are present in the reaction mixture during the synthesis in quantities of 0.1 to 4.0 mol-% in addition to the amount of the other polyamide-forming components.
Claim 2
Dependent Claim
287 words
Polyetheramide hotmelt adhesives having acid values in the range from 4 to 20, relative viscosities (1% by weight solutions in m-cresol at 25° C.) in the range from 1.3 to 2.5, softening points in the range from 100° to 200° C. and melt viscosities in the range from 100° to 190° C. at 200° C. wherein the polyetheramide hot melt adhesives are prepared from the reaction of (1) 40 to 75% by weight of polyamide-forming components comprising caprolactam, ε-amino-caproic acid or a mixture thereof, (2) 25 to 60% per weight of a mixture of components (a) to (c) in the stated equivalent ratios of (a) 0.95 to 1.05 equivalents comprising one or more compounds selected from the group of aliphatic and aromatic C 4 -C 34 dicarboxylic acids, (b) 0.2 to 0.9 equivalents comprising one or more compounds selected from the group of aliphatic and cycloaliphatic C 6 -C 25 -diamines (c) 0.1 to 0.8 equivalents of one or more polyoxyalkylene diols having molecular weights (Mn) in the range from 200 to 1000 g mol -1 , wherein the terminal groups are OH groups, terminal primary amine groups or a mixture thereof, where the sum of equivalents (b+c)=1, and (3) 0 to 15% by weight of a lactam and aminocarboxylic acids different from caprolactam and aminocaproic acid wherein chain terminators corresponding to general formula (1) R--Y (1) in which R is an optionally branched, saturated or unsaturated, optionally substituted alkyl radical having a length of 12 to 40 C atoms, and Y is one of the groups --NH.sub.2 (II) --COOH (III) are present in the reaction mixture during the synthesis in quantities of 0.1 to 4.0 mol-% in addition to the amount of the other polyamide-forming components.
Claim 3
Dependent Claim
23 words
Polyetheramide hotmelt adhesives according to claim 1, characterized in that the alkyl groups R of formula (I) have 16 to 35 C atoms.
Claim 4
Dependent Claim
25 words
Polyetheramide hotmelt adhesives according to claim 1, characterized in that the chain terminators R--Y are stearic acid, stearylamine, behenic acid, behenylamine, hexadecylamine or hexadecanoic acid.
Claim 5
Dependent Claim
27 words
Polyetheramide hotmelt adhesives according to claim 1, characterized in that from 0.2 to 3.0 mol% of chain terminators of formula (I) are present in the reaction mixture.
Claim 6
Dependent Claim
92 words
Polyetheramide hotmelt adhesives according to claim 1, characterized in that the dicarboxylic acids (2a) are adipic acid, isophthalic acid, terephthalic acid or sebacic acid, the diamines (2b) are hexamethylenediamine, trimethyl hexamethylenediamines, isophoroediamine or binuclear diamines corresponding to formula (V) ##STR2## in which R is an alkylene or alkylidene radical containing 1 to 10 C atoms and R 1 and R 2 are the same or different and represent H or C 1-3 alkyl, the polyoxyalkylenediols (2c) are polyoxyethylenediols, polyoxypropylenediols or ethyleneoxide/propyleneoxide copolymer diols, and component (3) is laurin lactam or aminoundecanoic acid.
Claim 7
Dependent Claim
18 words
Polyetheramide hotmelt adhesives according to claim 5 wherein R is a --CH 2 -group or a ##STR3## group.
Claim 8
Dependent Claim
36 words
Polyetheramide hotmelt adhesives according to claim 5 wherein the diamine (2b) is 4,4'-diamino-3,3'-dimethyl dicyclohexyl methane, 4,4'-diamino-3,3',5,5'-tetramethyl dicyclohexyl methane, 4,4'-diaminodicyclohexyl propane, 4,4'-diaminodicyclohexyl methane or diaminodicyclohexyl methane isomer mixtures of which at least 75% consist of the 4,4'-isomer.
Claim 9
Dependent Claim
145 words
Polyetheramide hotmelt adhesives according to claim 1, characterized in that 0.2 to 3.5 mol% of monoamines and monocarboxylic acids R--Y with an alkyl group R with 16 to 35 C atoms in the chain are present in the reaction mixture as chain terminators during the synthesis, together with (1) 40-75% by weight caprolactam, aminocaproic acid or a mixture thereof, (2) 25-60% of a mixture of (a) to (c) in the stated equivalent ratios of (a) one equivalent of at least one dicarboxylic acid, selected from adipic acid, sebacic acid, isophthalic acid and terephthalic acid, (b) 0.5 to 0.9 equivalents of at least one compound selected from hexamethylene diamine and 4,4-diaminodicyclohexyldiamine and its isomer mixtures and (c) 0.1 to 0.5 equivalents of polyalkylenediols having a molecular weight (Mn) in the range from 300 to 600 g.mol -1 , and where the sum of the equivalents (b+c)=1.
Claim 10
Dependent Claim
18 words
Polyetheramide hotmelt adhesives according to claim 8 wherein component (2b) comprises up to 10% by weight of triamines.
Claim 11
Dependent Claim
30 words
Polyetheramide hotmelt adhesives according to claim 1 wherein the dicarboxylic acids (2a) comprise at most 15% by weight dimer fatty acids containing at least 95% by weight dimeric fatty acids.
Claim 12
Dependent Claim
29 words
Polyetheramide hotmelt adhesives according to claim 1 further comprising pigments, flatting agents, nucleating additives, stabilizers, elastomer modifiers and flow aids that are added before, during or after the polycondensation.
Claim 13
Dependent Claim
229 words
A process for the production of the polyetheramide hotmelt adhesives of claim 1 comprising reacting (1) 40 to 75% by weight of polyamide-forming components comprising caprolactam, ε-amino-caproic acid or a mixture thereof, (2) 25 to 60% per weight of a mixture of components (a) to (c) in the stated equivalent ratios of (a) 0.95 to 1.05 equivalents comprising one or more compounds selected from the group of aliphatic and aromatic C 4 -C 34 dicarboxylic acids, (b) 0.2 to 0.9 equivalents comprising one or more compounds selected from the group of aliphatic and cycloaliphatic C 6 -C 25 -diamines (c) 0.1 to 0.8 equivalents of one or more polyoxyalkylene diols having molecular weights (Mn) in the range from 200 to 1000 g mol -1 , wherein the terminal groups are OH groups, terminal primary amine groups or a mixture thereof, where the sum of equivalents (b+c)=1, and (3) 0 to 15% by weight of a lactam and aminocarboxylic acids different from caprolactam and aminocaproic acid in the presence of chain terminators corresponding to general formula (1) R--Y (1) in which R is an optionally branched, saturated or unsaturated, optionally substituted alkyl radical having a length of 12 to 40 C atoms, and Y is one of the groups --NH.sub.2 (II) --COOH (III) in quantities of 0.1 to 4.0 mol-% in addition to the amount of the other polyamide-forming components.
Claim 14
Dependent Claim
142 words
A process for the production of polyetheramide hotmelt adhesives according to claim 8 comprising reacting (1) 40-75% by weight caprolactam, aminocaproic acid or a mixture thereof, (2) 25-60% of a mixture of (a) to (c) in the stated equivalent ratios of (a) one equivalent of at least one dicarboxylic acid, selected from adipic acid, sebacic acid, isophthalic acid and terephthalic acid, (b) 0.5 to 0.9 equivalents of at least one compound selected from hexamethylene diamine and 4,4-diaminodicyclohexyldiamine and its isomer mixtures and (c) 0.1 to 0.5 equivalents of polyalkylenediols having a molecular weight (Mn) in the range from 300 to 600 g.mol -1 , where the sum of the equivalents (b+c)=1 wherein the reaction takes place in the presence of 0.2 to 3.5 mol% of monoamines or monocarboxylic acids R--Y wherein R is an alkyl group having 16 to 35 C atoms.
Claim 15
Dependent Claim
229 words
Thermoplastic materials comprising polyetheramide prepared from the reaction of (1) 40 to 75% by weight of polyamide-forming components comprising caprolactam, γ-amino-caproic acid or a mixture thereof, (2) 25 to 60% per weight of a mixture of components (a) to (c) in the stated equivalent ratios of (a) 0.95 to 1.05 equivalents comprising one or more compounds selected from the group of aliphatic and aromatic C 4 -C 34 dicarboxylic acids, (b) 0.2 to 0.9 equivalents comprising one or more compounds selected from the group of aliphatic and cycloaliphatic C 6 -C 25 -diamines (c) 0.1 to 0.8 equivalents of one or more polyoxyalkylene diols having molecular weights (Mn) in the range from 200 to 1000 g mol -1 , wherein the terminal groups are OH groups, terminal primary amine groups or a mixture thereof, where the sum of equivalents (b+c)=1, and (3) 0 to 15% by weight of a lactam and aminocarboxylic acids different from caprolactam and aminocaproic acid wherein chain terminators corresponding to general formula (1) R--Y (1) in which R is an optionally branched, saturated or unsaturated, optionally substituted alkyl radical having a length of 12 to 40 C atoms, and Y is one of the groups --NH.sub.2 (II) --COOH (III) are present in the reaction mixture during the synthesis in quantities of 0.1 to 4.0 mol-% in addition to the amount of the other polyamide-forming components.
Claim 16
Dependent Claim
229 words
Thermoplastic materials comprising polyetheramide prepared from the reaction of (1) 40 to 75% by weight of polyamide-forming components comprising caprolactam, γ-amino-caproic acid or a mixture thereof, (2) 25 to 60% per weight of a mixture of components (a) to (c) in the stated equivalent ratios of (a) 0.95 to 1.05 equivalents comprising one or more compounds selected from the group of aliphatic and aromatic C 4 -C 34 dicarboxylic acids, (b) 0.2 to 0.9 equivalents comprising one or more compounds selected from the group of aliphatic and cycloaliphatic C 6 -C 25 -diamines (c) 0.1 to 0.8 equivalents of one or more polyoxyalkylene diols having molecular weights (Mn) in the range from 200 to 1000 g mol -1 , wherein the terminal groups are OH groups, terminal primary amine groups or a mixture thereof, where the sum of equivalents (b+c)=1, and (3) 0 to 15% by weight of a lactam and aminocarboxylic acids different from caprolactam and aminocaproic acid wherein chain terminators corresponding to general formula (1) R--Y (1) in which R is an optionally branched, saturated or unsaturated, optionally substituted alkyl radical having a length of 12 to 40 C atoms, and Y is one of the groups --NH.sub.2 (II) --COOH (III) are present in the reaction mixture during the synthesis in quantities of 0.1 to 4.0 mol-% in addition to the amount of the other polyamide-forming components.
References Cited (Backward Citations)
US4238582A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-14 | 1994-07-16 | 1995-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-14 | 1998-07-16 | 1999-01-15 | $3760.00 | Window Closed / Lapsed |