Joined metal composite and method for production thereof
Assignee: Toshiba Corp
•
Filing: 1989-06-16
•
Granted: 1991-01-15
•
Expires: 2009-06-16
Abstract
Abstract Disclosed is a joined ceramic-metal composite having a copper sheet directly joined to a ceramic substrate and a method for the production thereof. This composite is characterized by having a plurality of parallel grooves formed on the surface of the copper sheet to be joined to the ceramic substrate. The products of this invention show substantially none of the defects such as blisters inflicated on the copper sheet during the course of union by heating and, therefore, serve advantageously as ceramic circuit substrates for use in transistor modules, for example.
Inventors
- 👤 Kazuo Matsumura
- 👤 Mitsuhiro Nagata
- 👤 Tadashi Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:41
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/02; C04B37/021; H; H05; H05K; H05K3/00; H05K3/38; H10; H10W; H10W70/00; H10W70/01; H10W70/04; H10W70/047; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6565; C04B2235/658; C04B2235/6583; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/36; C04B2237/366; C04B2237/40; C04B2237/402; C04B2237/407; C04B2237/50; C04B2237/52; C04B2237/54; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1062; Y10T156/1064
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
150 words
A method for the production of a joined ceramic-copper composite substrate comprising a ceramic substrate and a copper sheet directly joined to one or each of opposite surfaces of said ceramic substrate and containing no gap in an interface between said ceramic substrate and said copper sheet, which method comprises the steps of preparing said copper sheet by forming on the surface thereof for contact with said ceramic substrate a plurality of grooves produced by plastic deformation, whereby said grooves may be subsequently recovered and flattened out at an elevated temperature, superposing said ceramic-copper composite substrate with the grooved surface of said copper sheet held contiguously to said ceramic substrate, heating the superposed layers at a temperature in the range of 1,065° to 1,083° C. thereby joining said ceramic substrate and said copper sheet by fusion and recovering and flattening out said grooves, and cooling the hot composite consequently formed.
Claim 2
Independent Claim
150 words
A method for the production of a joined ceramic-copper composite substrate comprising a ceramic substrate and a copper sheet directly joined to one or each of opposite surfaces of said ceramic substrate and containing no gap in an interface between said ceramic substrate and said copper sheet, which method comprises the steps of preparing said copper sheet by forming on the surface thereof for contact with said ceramic substrate a plurality of grooves produced by plastic deformation, whereby said grooves may be subsequently recovered and flattened out at an elevated temperature, superposing said ceramic-copper composite substrate with the grooved surface of said copper sheet held contiguously to said ceramic substrate, heating the superposed layers at a temperature in the range of 1,065° to 1,083° C. thereby joining said ceramic substrate and said copper sheet by fusion and recovering and flattening out said grooves, and cooling the hot composite consequently formed.
Claim 3
Dependent Claim
74 words
The method according to claim 1, wherein said copper sheet containing said plurality of grooves is formed with a wall thickness in the range of 0.03 to 0.5 mm with tough pitch copper having an oxygen content in the range of 200 to 500 ppm and possesses tensile strength of not more than 30 kgf/mm 2 , an elongation of not less than 20%, and a Vickers hardness of not more than 105 Hv.
Claim 4
Independent Claim
61 words
The method according to claims 1 or 2, wherein said plurality of grooves on the surface of said copper sheet are disposed substantially parallel to one another and possess a width in the range of 0.01 to 3 mm and a depth in the range of 0.1 to 0.01 mm and are separated by a distance of 1 to 25 mm.
Claim 5
Dependent Claim
15 words
The method according to claim 1, wherein said plurality of grooves are produced by stamping.
References Cited (Backward Citations)
US2638430A
Cited
US3994430A
Cited
US4505418A
Cited
US4409278A
Cited
GB2099742A
Cited
US4591401A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-14 | 1994-07-16 | 1995-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-14 | 1998-07-16 | 1999-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-14 | 2002-07-16 | 2003-01-15 | $7700.00 | Window Closed / Lapsed |