Process for making macromolecular monomers of polylactones with terminal acryloyl unsaturation and block copolymers thereof
Assignee: Noveon IP Holdings Corp
•
Filing: 1988-12-12
•
Granted: 1991-01-08
•
Expires: 2008-12-12
Abstract
Abstract Preparation of a macromolecular monomer of a lactone having an alpha-beta monoolefinically unsaturated "head" is effected at low temperature with a strong oxonium salt, such as a trialkyloxonium (TAO) hexafluorophosphate catalyst, with essentially no formation of cyclic oligomers and an insignificant amount of diacrylate. Cationic ring-opening polymerization of lactone monomer in conjunction with an unsaturated alcohol (propagator) having an acryloyl or methacryloyl double bond, produces a polylactone macromer having an ethylenic double bond at one end and a hydroxyl group at the other. The polymerization proceeds by polyaddition of the lactone to the OH group which is the propagating species. The macromer so formed allows the preparation of a macromer of block copolymer of the polylactone with a polyether such as epichlorohydrin, using the same TAO catalyst. In such a macromer of block copolymer, the polylactone ester block is next to the double bond, followed by the polyether block. This macromer of block copolymer, in turn, may be copolymerized with commonly available olefinically unsaturated monomers. There is no known method for the preparation of such copolymers with a homomacromer of polylactone, or, a macromer of polylactone-b-polyether. The propagator is a primary or secondary acryloyl or methacryloyl alcohol.
Inventors
- 👤 Simon H. Yu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:27
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/66; C08G63/664; C08G63/02; C08G63/06; C08G63/08
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
217 words
A process for the manufacture of a polylactone macromer having an ethylenically unsaturated functional group near one end and a hydroxyl group at the other, comprising, polymerizing (A) a cationically ring-openable lactone having the structure: ##STR13## wherein, n is an integer chosen from 1, 3, 4 and 5; R 1 is a group selected from hydrogen, C 1 -C 20 alkyl, cycloalkyl, alkoxy and phenyl, and the number of R 1 groups which are H is at least (n+2); and, (B) an ethylenically unsaturated primary or secondary (meth)acryloyl alcohol wherein the ethylenic unsaturation 3 is adjacent a carbonyl group as in the structure ##STR14## wherein R 2 is H or methyl; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; and, (C) an oxonium salt cationic initiator while maintaining a temperature in the range from about 10° C. to about 80°; so as to produce a macromer having the structure R--(M).sub.m --OH (LM) wherein R represents the residue of said alcohol having a (meth)acryloyl group, M represents the polyester repeating unit of at least one said lactone which is ring-opened, and, m represents an integer in the range from 2 to about 500.
Claim 2
Dependent Claim
217 words
A process for the manufacture of a polylactone macromer having an ethylenically unsaturated functional group near one end and a hydroxyl group at the other, comprising, polymerizing (A) a cationically ring-openable lactone having the structure: ##STR13## wherein, n is an integer chosen from 1, 3, 4 and 5; R 1 is a group selected from hydrogen, C 1 -C 20 alkyl, cycloalkyl, alkoxy and phenyl, and the number of R 1 groups which are H is at least (n+2); and, (B) an ethylenically unsaturated primary or secondary (meth)acryloyl alcohol wherein the ethylenic unsaturation 3 is adjacent a carbonyl group as in the structure ##STR14## wherein R 2 is H or methyl; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; and, (C) an oxonium salt cationic initiator while maintaining a temperature in the range from about 10° C. to about 80°; so as to produce a macromer having the structure R--(M).sub.m --OH (LM) wherein R represents the residue of said alcohol having a (meth)acryloyl group, M represents the polyester repeating unit of at least one said lactone which is ring-opened, and, m represents an integer in the range from 2 to about 500.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein said lactone is selected from the group consisting of epsilon-caprolactone, beta-propiolactone, beta-butyrolactone, and delta-valerolactone.
Claim 4
Dependent Claim
23 words
The process of claim 1 wherein said (meth)acryloyl alcohol is selected from the group consisting of 2-hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and 4-hydroxybutyl (meth)acrylate.
Claim 5
Dependent Claim
40 words
The process of claim 1 wherein said oxonium salt is a trialkyl oxonium salt selected from the group consisting of triethyloxonium hexafluorophosphate, triethyloxonium hexafluoroantimonate, triethyloxonium hexafluoroarsenate, triethyloxonium hexachloroantimonate, and triethyloxonium tetrafluoroborate, wherein alkyl is lower C 1 -C 6 alkyl.
Claim 6
Dependent Claim
148 words
The process of claim 1 including the additional step of polymerizing (a) said macromer (LM) functioning as a propagator, with (b) an alkylene oxide, in the presence of a sufficient amount for the purpose, of (c) an oxonium salt cationic initiator, while maintaining a temperature in the range from about 10° C. to about 80°; to form a macromer block copolymer of ester-b-ether as an essentially linear polylactone macromer blocked to a polyether, said macromer of a block copolymer having (meth)acrylic and OH chain ends as in the structure ##STR15## wherein, PolyLact represents a polymer chain of from 2 to about 300 ring-opened lactone units forming a polylactone; and, PolyEt represents a polymer chain of from 2 to about 300 alkylene oxide units forming a polyether; said macromer of block copolymer having substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not above about 5.0.
Claim 7
Dependent Claim
41 words
The process of claim 5 wherein said (PolyEt) in said macromer of block copolymer is the residue of a C 2 -C 6 alkylene oxide or haloalkylene oxide polymer selected from the group consisting of poly(ethylene oxide), poly(propylene oxide) and poly(epichlorohydrin).
Claim 8
Dependent Claim
20 words
The process of claim 5 wherein said lactone is selected from the group consisting of epsilon-caprolactone, beta-propiolactone, beta-butyrolactone, and delta-valerolactone.
Claim 9
Dependent Claim
23 words
The process of claim 5 wherein said (meth)acryloyl alcohol is selected from the group consisting of 2-hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and 4-hydroxybutyl (meth)acrylate.
Claim 10
Dependent Claim
40 words
The process of claim 5 wherein said oxonium salt is a trialkyl oxonium salt selected from the group consisting of triethyloxonium hexafluorophosphate, triethyloxonium hexafluoroantimonate, triethyloxonium hexafluoroarsenate, triethyloxonium hexachloroantimonate, and triethyloxonium tetrafluoroborate, wherein alkyl is lower C 1 -C 6 alkyl.
Claim 11
Dependent Claim
149 words
The process of claim 1 including the additional step of polymerizing (a) said macromer (LM) of a first lactone (L) functioning as a propagator, with (b) another lactone (L), in the presence of a sufficient amount for the purpose, of (c) an oxonium salt cationic initiator, while maintaining a temperature in the range from about 10° C. to about 80°; to form an essentially linear macromer of block copolymer of ester-b-ester, said macromer of block copolymer having (meth)acrylic and OH chain ends as in the structure ##STR16## wherein PolyLact1 represents a polymer chain of from 2 to about 300 ring-opened first lactone units forming a first polylactone; and, PolyLact2 represents a polymer chain of from 2 to about 300 ring-opened second lactone units forming a second polylactone; said macromer of block copolymer having substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not above about 5.0.
Claim 12
Dependent Claim
20 words
The process of claim 10 wherein said lactone is selected from the group consisting of epsilon-caprolactone, beta-propiolactone, beta-butyrolactone, and delta-valerolactone.
Claim 13
Dependent Claim
23 words
The process of claim 10 wherein said (meth)acryloyl alcohol is selected from the group consisting of 2-hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and 4-hydroxybutyl (meth)acrylate.
Claim 14
Dependent Claim
40 words
The process of claim 10 wherein said oxonium salt is a trialkyl oxonium salt selected from the group consisting of triethyloxonium hexafluorophosphate, triethyloxonium hexafluoroantimonate, triethyloxonium hexafluoroarsenate, triethyloxonium hexachloroantimonate, and triethyloxonium tetrafluoroborate, wherein alkyl is lower C 1 -C 6 alkyl.
Claim 15
Dependent Claim
117 words
The process of claim 1 including the additional step of polymerizing (a) said macromer (LM) functioning as a comonomer, with (b) an olefinically unsaturated monomer, in the presence of a sufficient amount for the purpose, of (c) a free radical polymerization initiator, while maintaining a temperature in the range from about 10° C. to about 80° C.; to form a random comb-shaped copolymer having the structure ##STR17## wherein M o represents the olefinically unsaturated monomer; n' represents an integer in the range from 1 to about 10 4 , preferably 1-10 3 and refers to the number of pendant OH-terminated polyester chains; and, n" represents an integer in the range from 1 to about 10 5 .
Claim 16
Dependent Claim
20 words
The process of claim 14 wherein said lactone is selected from the group consisting of epsilon-caprolactone, beta-propiolactone, beta-butyrolactone, and delta-valerolactone.
Claim 17
Dependent Claim
23 words
The process of claim 14 wherein said (meth)acryloyl alcohol is selected from the group consisting of 2-hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and 4-hydroxybutyl (meth)acrylate.
Claim 18
Dependent Claim
40 words
The process of claim 14 wherein said oxonium salt is a trialkyl oxonium salt selected from the group consisting of triethyloxonium hexafluorophosphate, triethyloxonium hexafluoroantimonate, triethyloxonium hexafluoroarsenate, triethyloxonium hexachloroantimonate, and triethyloxonium tetrafluoroborate, wherein alkyl is lower C 1 -C 6 alkyl.
Claim 19
Dependent Claim
117 words
The process of claim 1 including the additional step of polymerizing (a) said macromer (LM) functioning as a comonomer, with (b) an olefinically unsaturated monomer, in the presence of a sufficient amount for the purpose, of (c) a free radical polymerization initiator, while maintaining a temperature in the range from about 10° C. to about 80° C.; to form a macromer block copolymer having the structure ##STR18## wherein M o represents the olefinically unsaturated monomer; n' represents an integer in the range from 1 to about 10 4 , preferably 1-10 3 and refers to the number of pendant OH-terminated polyester chains; and, n" represents an integer in the range from 1 to about 10 5 .
Claim 20
Dependent Claim
158 words
The process of claim 18 wherein said olefinically unsaturated monomer is selected from the group consisting of (i) C 2 -C 12 vinyl monomers such as readily available vinyl chloride, vinyl acetate, acrylonitrile, ethylene, propylene, 4-vinyl pyridine, vinyl pyrrolidone, vinyl benzoic acid, ethyl vinyl ether, salts of vinyl sulfonate, vinyl toluene, vinylidene chloride, N-vinyl carbazole, and the like; (ii) C 8 -C 16 styryl monomers such as styrene, 4-chlorostyrene, alpha-methyl styrene, and the like; (iii) alpha,beta-ethylenically unsaturated carboxylic acids having from 3 to 8 carbon atoms, and derivatives thereof selected from the group consisting of esters of C 1 -C 20 alcohols such as ethyl acrylate, ethyl methacrylate, glycidyl acrylate, butyl acrylate; acrylamide and amides of C 1 -C 20 amines such as N,N-dimethylacrylamide; and, metal salts such as sodium acrylate; (iv) C 4 -C 8 diene monomers such as butadiene and isoprene; and, (v) C 5 -C 10 allylically unsaturated monomers such as allyl acetate, and diallylphthalate.
Claim 21
Dependent Claim
20 words
The process of claim 18 wherein said lactone is selected from the group consisting of epsilon-caprolactone, beta-propiolactone, beta-butyrolactone, and delta-valerolactone.
Claim 22
Dependent Claim
23 words
The process of claim 18 wherein said (meth)acryloyl alcohol is selected from the group consisting of 2-hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and 4-hydroxybutyl (meth)acrylate.
Claim 23
Dependent Claim
40 words
The process of claim 18 wherein said oxonium salt is a trialkyl oxonium salt selected from the group consisting of triethyloxonium hexafluorophosphate, triethyloxonium hexafluoroantimonate, triethyloxonium hexafluoroarsenate, triethyloxonium hexachloroantimonate, and triethyloxonium tetrafluoroborate, wherein alkyl is lower C 1 -C 6 alkyl.
Claim 24
Dependent Claim
228 words
A polylactone macromer having a (meth)acrylol group at one end and a hydroxyl group at the other, formed by polymerizing (A) a cationically ring-openable lactone having the structure ##STR19## wherein, n is an integer chosen from 1, 3, 4 and 5; R 1 is a group selected from hydrogen, C 1 -C 20 alkyl, cycloalkyl, alkoxy and phenyl, and the number of R 1 groups which are H is at least (n+2); and, (B) a primary or secondary (meth)acryloyl alcohol wherein the ethylenic unsaturation is adjacent a carbonyl group said alcohol represented by the structure ##STR20## wherein R 2 is H or CH 3 ; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; in the presence of an effective amount of (C) an oxonium salt cationic initiator while maintaining a temperature in the range from about 10° C. to about 80° C.; so as to produce a macromer having the structure R--(M).sub.m --OH (LM) wherein R represents the residue of said alcohol having a (meth)acryloyl group, M represents the polyester repeating unit of at least one said lactone which is ring-opened, and, m represents an integer in the range from 2 to about 500; said macromer being formed essentially free of di(meth)acrylic species.
Claim 25
Dependent Claim
228 words
A polylactone macromer having a (meth)acrylol group at one end and a hydroxyl group at the other, formed by polymerizing (A) a cationically ring-openable lactone having the structure ##STR19## wherein, n is an integer chosen from 1, 3, 4 and 5; R 1 is a group selected from hydrogen, C 1 -C 20 alkyl, cycloalkyl, alkoxy and phenyl, and the number of R 1 groups which are H is at least (n+2); and, (B) a primary or secondary (meth)acryloyl alcohol wherein the ethylenic unsaturation is adjacent a carbonyl group said alcohol represented by the structure ##STR20## wherein R 2 is H or CH 3 ; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; in the presence of an effective amount of (C) an oxonium salt cationic initiator while maintaining a temperature in the range from about 10° C. to about 80° C.; so as to produce a macromer having the structure R--(M).sub.m --OH (LM) wherein R represents the residue of said alcohol having a (meth)acryloyl group, M represents the polyester repeating unit of at least one said lactone which is ring-opened, and, m represents an integer in the range from 2 to about 500; said macromer being formed essentially free of di(meth)acrylic species.
Claim 26
Dependent Claim
209 words
A random comb-shaped copolymer of a polylactone macromer having a (meth)acrylol group at one end and a hydroxyl group at the other, said comb-shaped copolymer having the structure ##STR21## wherein M o represents the olefinically unsaturated monomer; R 2 is H or CH 3 ; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; PolyLact represents a polymer chain of from 2 to about 300 ring-opened lactone units of at least one lactone; n' represents an integer in the range from 1 to about 10 4 , preferably 1-10 3 and refers to the number of pendant OH-terminated polyester chains; and, n" represents an integer in the range from 1 to about 10 5 ; said comb copolymer formed by polymerizing (a) a macromer having the structure ##STR22## said macromer having substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not above about 5.0; and, (b) an olefinically unsaturated monomer, in the presence of a sufficient amount for the purpose, of (c) a free radical polymerization initiator, while maintaining a temperature in the range from about 10° C. to about 80° C.
Claim 27
Dependent Claim
209 words
A random comb-shaped copolymer of a polylactone macromer having a (meth)acrylol group at one end and a hydroxyl group at the other, said comb-shaped copolymer having the structure ##STR21## wherein M o represents the olefinically unsaturated monomer; R 2 is H or CH 3 ; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; PolyLact represents a polymer chain of from 2 to about 300 ring-opened lactone units of at least one lactone; n' represents an integer in the range from 1 to about 10 4 , preferably 1-10 3 and refers to the number of pendant OH-terminated polyester chains; and, n" represents an integer in the range from 1 to about 10 5 ; said comb copolymer formed by polymerizing (a) a macromer having the structure ##STR22## said macromer having substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not above about 5.0; and, (b) an olefinically unsaturated monomer, in the presence of a sufficient amount for the purpose, of (c) a free radical polymerization initiator, while maintaining a temperature in the range from about 10° C. to about 80° C.
Claim 28
Dependent Claim
235 words
A comb-shaped block copolymer of polylactone-b-polyether said block copolymer having a (meth)acrylol group at one end and a hydroxyl group at the other, said comb-shaped block copolymer having the structure ##STR23## wherein M o represents the olefinically unsaturated monomer; R 2 is H or CH 3 ; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; PolyLact represents a polymer chain of from 2 to about 300 ring-opened lactone units of at least one lactone; n' represents an integer in the range from 1 to about 10 4 , preferably 1-10 3 and refers to the number of pendant OH-terminated polyester chains; and, n" represents an integer in the range from 1 to about 10 5 ; said comb-shaped block copolymer formed by polymerizing (a) a macromer block copolymer having the structure ##STR24## and, PolyEt represents a polymer chain of from 2 to about 300 alkylene oxide units forming a polyether; said macromer of block copolymer having substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not above about 5.0; with (b) an olefinically unsaturated monomer, in the presence of a sufficient amount for the purpose of (c) a free radical polymerization initiator, while maintaining a temperature in the range from about 10° C. to about 80° C.
Claim 29
Dependent Claim
235 words
A comb-shaped block copolymer of polylactone-b-polyether said block copolymer having a (meth)acrylol group at one end and a hydroxyl group at the other, said comb-shaped block copolymer having the structure ##STR23## wherein M o represents the olefinically unsaturated monomer; R 2 is H or CH 3 ; R 3 is selected from the group consisting of branched or linear alkylene, haloalkylene, alkoxyl, haloalkoxyl, each C 1 -C 20 , aralkylene, haloaralkylene, aralkoxyl, and haloaralkoxyl, each C 7 -C 20 ; PolyLact represents a polymer chain of from 2 to about 300 ring-opened lactone units of at least one lactone; n' represents an integer in the range from 1 to about 10 4 , preferably 1-10 3 and refers to the number of pendant OH-terminated polyester chains; and, n" represents an integer in the range from 1 to about 10 5 ; said comb-shaped block copolymer formed by polymerizing (a) a macromer block copolymer having the structure ##STR24## and, PolyEt represents a polymer chain of from 2 to about 300 alkylene oxide units forming a polyether; said macromer of block copolymer having substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not above about 5.0; with (b) an olefinically unsaturated monomer, in the presence of a sufficient amount for the purpose of (c) a free radical polymerization initiator, while maintaining a temperature in the range from about 10° C. to about 80° C.
Claim 30
Dependent Claim
159 words
The comb-shaped copolymer of claim 25 wherein said olefinically unsaturated monomer is selected from the group consisting of (i) C 2 -C 12 vinyl monomers such as readily available vinyl chloride, vinyl acetate, acrylonitrile, ethylene, propylene, 4-vinyl pyridine, vinyl pyrrolidone, vinyl benzoic acid, ethyl vinyl ether, salts of vinyl sulfonate, vinyl toluene, vinylidene chloride, N-vinyl carbazole, and the like; (ii) C 8 -C 16 styryl monomers such as styrene, 4-chlorostyrene, alpha-methyl styrene, and the like; (iii) alpha,beta-ethylenically unsaturated carboxylic acids having from 3 to 8 carbon atoms, and derivatives thereof selected from the group consisting of esters of C 1 -C 20 alcohols such as ethyl acrylate, ethyl methacrylate, glycidyl acrylate, butyl acrylate; acrylamide and amides of C 1 -C 20 amines such as N,N-dimethylacrylamide; and, metal salts such as sodium acrylate; (iv) C 4 -C 8 diene monomers such as butadiene and isoprene; and, (v) C 5 -C 10 allylically unsaturated monomers such as allyl acetate, and diallylphthalate.
Claim 31
Dependent Claim
21 words
The comb-shaped copolymer of claim 26 wherein said lactone is selected from the group consisting of epsilon-caprolactone, beta-propiolactone, beta-butyrolactone, and delta-valerolactone.
References Cited (Backward Citations)
US2945012A
Cited
US4188472A
Cited
US4281172A
Cited
US4368320A
Cited
GB2101121A
Cited
US4504635A
Cited
US4683287A
Cited
US4632975A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-07 | 1994-07-09 | 1995-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-07 | 1998-07-09 | 1999-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-07 | 2002-07-09 | 2003-01-08 | $7700.00 | Window Closed / Lapsed |