US4980251A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of synthesizing a lithium manganese oxide
Assignee: CSIR ADMINISTRATION BUILDING SCIENTIA PRETORIA TRANSVAAL PROVINCE REPUBLIC OF S AFRICA
•
Filing: 1989-07-12
•
Granted: 1990-12-25
•
Expires: 2009-07-12
Abstract
Abstract A method of synthesizing a lithium manganese oxide in accordance with the formula Li1-xMn2O4 in which 0</=x<1 and having a spinel-type crystal structure includes forming a mixture in finely divided solid form of at least one lithium salt such as Li2CO3 which decomposes when heated in air to form an oxide of lithium, and at least one manganese salt such as MnCO3 which decomposes when heated in air to form an oxide of manganese. The mixture is heated in an oxidizing atmosphere to a temperature in the range 200 DEG -600 DEG C. to decompose the salts and to obtain the Li1-xMn2O4 having a spinel-type crystal structure.
Inventors
- 👤 Michael M. Thackeray
- 👤 Annemare De Kock
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:03
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/13; H01M4/139; H01M4/1391; C; C01; C01G; C01G45/00; C01G45/12; C01G45/1221; C01G45/1242; H01M4/131; H01M4/36; H01M4/48; H01M4/485; H01M4/50; H01M4/505; C01P; C01P2002/00; C01P2002/30; C01P2002/32; C01P2002/70; C01P2002/72; C01P2006/00; C01P2006/12; C01P2006/40; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
84 words
A method of synthesizing a lithium manganese oxide having a spinel-type crystal structure, the method comprising forming a mixture in finely divided solid form of at least one lithium salt and at least one manganese salt, and heating the mixture in air in an oxidizing atmosphere at a temperature in the range 200°-600° C. to cause said salts to react with each other to obtain said lithium manganese oxide having a spinel-type crystal structure, by simultaneous decomposition and cubic close packed oxygen lattice construction.
Claim 2
Independent Claim
84 words
A method of synthesizing a lithium manganese oxide having a spinel-type crystal structure, the method comprising forming a mixture in finely divided solid form of at least one lithium salt and at least one manganese salt, and heating the mixture in air in an oxidizing atmosphere at a temperature in the range 200°-600° C. to cause said salts to react with each other to obtain said lithium manganese oxide having a spinel-type crystal structure, by simultaneous decomposition and cubic close packed oxygen lattice construction.
Claim 3
Dependent Claim
53 words
A method as claimed in claim 1, in which the salt of lithium is a member of the group consisting of LiCO 3 , LiNO 3 and mixtures thereof and the salt of manganese is a member of the group consisting of Mn(NO 3 ) 2 , MnCO 3 O, and mixtures thereof.
Claim 4
Dependent Claim
25 words
A method as claimed in claim 1, in which forming the mixture is so that the molar ratio of Li:Mn is from 1:1.7 to 1:2.5.
Claim 5
Dependent Claim
29 words
A method as claimed in claim 1, in which forming the mixture is by milling such that the average particle size in the mixture is at most 250 microns.
Claim 6
Dependent Claim
47 words
A method as claimed in claim 1, in which forming the mixture is by making a slurry in a solvent selected from the group consisting of water, ethanol and mixtures thereof and thereafter drying the mixture until the solvent content thereof is at most 10% by mass.
Claim 7
Dependent Claim
39 words
A method as claimed in claim 1, in which the heating of the mixture is in air to a temperature of 300°-400° C., the mixture being held at the maximum temperature for a period of at least 2 hours.
Claim 8
Dependent Claim
51 words
A method as claimed in claim 1, which includes the step, prior to the heating, of compacting the mixture by pressing it at a pressur of 5-10 MPa to form a unitary artifact, so that, after the heating, the lithium manganese oxide is in the form of a self-supporting unitary artifact.
Claim 9
Dependent Claim
15 words
Lithium manganese oxide having a spinel crystal structure, synthesized by the method of claim 1.
Claim 10
Dependent Claim
38 words
An electrochemical cell having a cathode comprising a lithium manganese oxide as claimed in claim 8, an anode which comprises lithium metal or a lithium-containing alloy, and an electrolyte whereby the anode is electrochemically coupled to the cathode.
Claim 11
Dependent Claim
75 words
A cell as claimed in claim 9, in which the lithium manganese 15 oxide of the cathode is present in the cathode in admixture with a binder and with an electronically conductive current collector in a compacted artifact, the electrolyte being a room-temperature electrolyte comprising a member of the group consisting of LiClO 4 , LiAsF 6 and LiBF 4 dissolved in an organic solvent selected from the group consisting of propylene carbonate and dimethoxyethane.
Claim 12
Dependent Claim
28 words
A method as claimed in claim 1, in which the lithium manganese oxide is in accordance with the formula Li 1-x Mn 2 O 4 in which 0x<1.
Claim 13
Dependent Claim
43 words
A method as claimed in claim 11, in which the Li 1-x Mn 2 O 4 has a (Mn 2 )O 4 (Mn 2 )O 4 n- ) 1 framework structure in which the quantity of Mn cations varies from the stoichiometric value.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-24 | 1994-06-25 | 1994-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-24 | 1998-06-25 | 1998-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-24 | 2002-06-25 | 2002-12-25 | $7700.00 | Window Closed / Lapsed |