US4980210A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Laminates of polyolefin-based film and metal and processes for producing such laminates
Assignee: Crown Packaging UK Ltd
•
Filing: 1988-10-12
•
Granted: 1990-12-25
•
Expires: 2008-10-12
Abstract
Abstract In a laminated material comprising a polyolefin-based film bonded to a metal sheet (M), the polyolefin-based film is a multi-layer co-extruded film comprising an inner layer (B2) of a bonding resin which is an acid-modified polyolefin resin containing carboxyl or anhydride groups and an outer layer (B1) of a polyolefin or polyamide containing 0.15% to 0.5% by weight of a finely divided non-reactive low-opacity synthetic silica having an average particle size on the range 0.5 to 5 microns. Another thermoplastic film (A1,A2), such as a biaxially oriented polyester film, may be simultaneously laminated to the other surface of the metal sheet. The lamination process involves heating the laminated material to effect bonding and then quenching the laminated material rapidly and uniformly from above the melting point of the polyolefin to below its softening point. The laminated material may be used in the formation of can ends and can bodies, which can be double seamed together without fibrillation of the polyolefin-based coating.
Inventors
- 👤 Peter J. Heyes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:06
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B21; B21D; B21D51/00; B21D51/16; B21D51/38; B21D51/383; B21D51/44; B32B1/00; B32B15/085; B32B15/088; B32B15/18; B32B27/00; B32B27/06; B32B27/08; B32B27/18; B32B27/32; B32B27/34; B32B37/00; B32B37/08; B32B37/085; B32B37/14; B32B37/16; B32B37/20; B32B37/203; B32B37/206; B32B38/00; B32B38/0036; B32B7/00; B32B7/04; B32B7/12; B65; B65D; B65D1/00; B65D1/22; B65D1/26; B65D1/28; B32B2255/00; B32B2255/20; B32B2264/00; B32B2264/10; B32B2264/102; B32B2310/00; B32B2310/04; B32B2310/0409; B32B2311/00; B32B2311/30; B32B2367/00; B32B2377/00; B32B2439/00; B32B2439/40; B32B2439/66; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1355; Y10T428/1359; Y10T428/1372; Y10T428/25; Y10T428/259; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31855; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
84 words
A laminated material comprising a polyolefin based film bonded to one major surface of a metal sheet, characterised in that the polyolefin-based film is a multi-layer co-extruded film comprising an inner layer of a bonding resin which is an acid-modified polyolefin resin containing carboxyl or anhydride groups and an outer layer of a polyolefin or a polyamide containing 0.15% to 0.5% by weight of a finely divided non-reactive low-opacity synthetic silica having an average particle size in the range of 0.5 to 5 microns.
Claim 2
Dependent Claim
84 words
A laminated material comprising a polyolefin based film bonded to one major surface of a metal sheet, characterised in that the polyolefin-based film is a multi-layer co-extruded film comprising an inner layer of a bonding resin which is an acid-modified polyolefin resin containing carboxyl or anhydride groups and an outer layer of a polyolefin or a polyamide containing 0.15% to 0.5% by weight of a finely divided non-reactive low-opacity synthetic silica having an average particle size in the range of 0.5 to 5 microns.
Claim 3
Dependent Claim
38 words
A laminated material according to claim 1 characterised in that the bonding resin is chosen from a maleic anhydride modified polypropylene, maleic anhydride modified ethylene-propylene copolymer, maleic anhydride modified polyethylene, or a maleic anhydride modified ethylene vinyl acetate.
Claim 4
Dependent Claim
19 words
A laminated material according to claim 1 characterised in that the outer layer comprises a polypropylene or ethylene-propylene copolymer.
Claim 5
Dependent Claim
16 words
A laminated material according to claim 1, characterised in that the outer layer comprises nylon 6.
Claim 6
Dependent Claim
22 words
A laminated material according to claim 1 characterised in that the multi-layer co-extruded film further comprises an intermediate layer of a polyolefin.
Claim 7
Dependent Claim
16 words
A laminated material according to claim 5 characterised in that the outer layer comprises a polyolefin.
Claim 8
Dependent Claim
30 words
A laminated material according to claim 5 characterised in that the film further comprises a second bonding resin layer between the intermediate layer and the outer layer which comprises nylon.
Claim 9
Dependent Claim
40 words
A laminated material according to claim 1, characterised in that the multi-layer co-extruded film further comprises an intermediate layer of a nylon and a second bonding resin layer between the intermediate layer and the outer layer, which comprises a polyolefin.
Claim 10
Dependent Claim
24 words
A laminated material according to claim 1 characterised by having another thermoplastic polymer film bonded to the other major surface of the metal sheet.
Claim 11
Dependent Claim
29 words
A laminated material according to claim 1 characterised in that the metal sheet is of electrolytically chromium coated steel with a dual layer of chromium metal and chromium oxide.
Claim 12
Dependent Claim
18 words
A can end characterised in that it is formed from a laminated material as defined in claim 1.
Claim 13
Dependent Claim
19 words
A flanged can body characterised in that it is formed from a laminated material as defined in claim 1.
Claim 14
Dependent Claim
34 words
A can body having an end secured thereto by a double seam, characterised in that both the can body and the can end being formed from a laminated material as defined in claim 1.
Claim 15
Dependent Claim
134 words
A process for producing a laminated material comprising a polyolefin-based film bonded to one major surface of a metal sheet, characterised by the steps of: laminating to one major surface of a metal strip a multi-layer co-extruded polyolefin-based film comprising an inner layer of a bonding resin which is an acid-modified polyolefin resin containing carboxyl or anhydride groups and an outer layer of a polyolefin or polyamide containing 0.15% to 0.5% by weight of a finely divided non-reactive low-opacity synthetic silica having an average particle size in the range of 0.5 to 5 microns, subjecting the laminated material to a temperature sufficient to cause the polyolefin film to bond with the metal strip, and quenching the laminated material rapidly and uniformly from above the melting point of the polyolefin to below its softening point.
Claim 16
Dependent Claim
134 words
A process for producing a laminated material comprising a polyolefin-based film bonded to one major surface of a metal sheet, characterised by the steps of: laminating to one major surface of a metal strip a multi-layer co-extruded polyolefin-based film comprising an inner layer of a bonding resin which is an acid-modified polyolefin resin containing carboxyl or anhydride groups and an outer layer of a polyolefin or polyamide containing 0.15% to 0.5% by weight of a finely divided non-reactive low-opacity synthetic silica having an average particle size in the range of 0.5 to 5 microns, subjecting the laminated material to a temperature sufficient to cause the polyolefin film to bond with the metal strip, and quenching the laminated material rapidly and uniformly from above the melting point of the polyolefin to below its softening point.
Claim 17
Dependent Claim
37 words
A process according to claim 14 characterised in that the bonding resin is chosen from a maleic anhydride modified polypropylene, maleic anhydride modified ethylene-propylene copolymer, maleic anhydride modified polyethylene, or a maleic anhydride modified ethylene vinyl acetate.
Claim 18
Dependent Claim
18 words
A process according to claim 14 characterised in that the outer layer comprises a polypropylene or ethylene-propylene copolymer.
Claim 19
Dependent Claim
15 words
A process according to claim 14 characterised in that the outer layer comprises nylon 6.
Claim 20
Dependent Claim
25 words
A process according to claim 14 characterised in that another thermoplastic polymer film is laminated simultaneously to the other major surface of the metal strip.
Claim 21
Dependent Claim
26 words
A process according to claim 18 characterised in that the other polymer film is a composite polyolefin or polyolefin-polyamide film with an inner bonding resin layer.
Claim 22
Dependent Claim
89 words
A process according to claim 19 characterised in that the lamination is effected by first simultaneously laminating both of the films to the metal strip with the metal strip at a temperature T 1 which is sufficient to cause softening of the bonding resin layers of both films but is below the temperature at which the outer surface of the films would be damaged during lamination, and then re-heating the resultant laminate to a temperature T 2 which is above the melting point of the polyolefin-based film or films.
Claim 23
Dependent Claim
45 words
A process according to claim 20 characterised in that the temperature T 1 is in the range from 130° C. to 22° C. and the temperature T 2 is in the range from 220° C. to the degradation temperature of the polymer film or films.
Claim 24
Dependent Claim
28 words
A process according to claim 14, characterised in that the quenching is effected by flooding the polymer coated surface or surfaces of the laminated material with cold liquid.
Claim 25
Dependent Claim
17 words
A process according to claim 22 characterised in that the cold liquid is water at room temperature.
References Cited (Backward Citations)
US4451506A
Cited
EP0031701A2
Cited
EP0035392A1
Cited
US4358493A
Cited
EP0062385A2
Cited
US4695492A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-24 | 1994-06-25 | 1994-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-24 | 1998-06-25 | 1998-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-24 | 2002-06-25 | 2002-12-25 | $7700.00 | Window Closed / Lapsed |