US4978427A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Water-soluble copolymers containing vinylamine units as wet strength and dry strength agent for paper
Assignee: BASF SE
•
Filing: 1989-09-05
•
Granted: 1990-12-18
•
Expires: 2009-09-05
Abstract
Abstract Water-soluble copolymers containing copolymerized vinylamine units are prepared by copolymerizing (a) from 95 to 10 mol % of N-vinylformamide and (b) from 5 to 90 mol % of an ethylenically unsaturated monomer from the group consisting of vinyl acetate, vinyl propionate, C 1 -C 4 -alkyl vinyl ethers, the esters, nitriles and amines of acrylic acid and methacrylic acid and N-vinylpyrrolidone, and then eliminating from 30 to 100 mol % of the formyl groups from the copolymer. Preferred copolymers are copolymers of N-vinyl-formamide and vinyl acetate, in which from 30 to 100 mol % of the monomer units are hydrolyzed. The copolymers are used in papermaking to increase the dry strength and wet strength of the paper.
Inventors
- 👤 Sigberg Pfohl
- 👤 Michael Kroener
- 👤 Heinrich Hartmann
- 👤 Walter Denzinger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:29
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/20; D21H17/33; D21H17/34; D21H17/41; D21H17/44; D21H17/45; C; C08; C08F; C08F226/00; C08F226/02; C08F8/00; C08F8/44; D21H17/36; D21H17/37; C08F2810/00; C08F2810/50; D21H21/00; D21H21/14; D21H21/18
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
148 words
A process for making paper which has high dry strength and wet strength, comprising adding a hydrolyzed copolymer to a paper stock, wherein said hydrolyzed copolymer is prepared by a process, comprising: (i) copolymerizing (a) N-vinylformamide in an amount of from 95 to 10 mole % with (b) an ethylenicaly unsaturated monomer selected from the group consisting of vinyl acetate, vinyl propionate, the C 1 -C 4 -alkyl vinyl ethers, N-vinylpyrrolidone and the esters, nitriles, and amides of acrylic acid and methacrylic acid in an amount of from 5 to 90 mole % to give a copolymer with formyl groups; and (ii) hydrolyzing from 30 to 100 mole % of said formyl groups of said copolymer to form a hydrolyzed copolymer with amino groups; wherein said hydrolyzed copolymer is added to said paper stock in an amount of from 0.1 to 5% by weight, based on dry fiber.
Claim 2
Dependent Claim
148 words
A process for making paper which has high dry strength and wet strength, comprising adding a hydrolyzed copolymer to a paper stock, wherein said hydrolyzed copolymer is prepared by a process, comprising: (i) copolymerizing (a) N-vinylformamide in an amount of from 95 to 10 mole % with (b) an ethylenicaly unsaturated monomer selected from the group consisting of vinyl acetate, vinyl propionate, the C 1 -C 4 -alkyl vinyl ethers, N-vinylpyrrolidone and the esters, nitriles, and amides of acrylic acid and methacrylic acid in an amount of from 5 to 90 mole % to give a copolymer with formyl groups; and (ii) hydrolyzing from 30 to 100 mole % of said formyl groups of said copolymer to form a hydrolyzed copolymer with amino groups; wherein said hydrolyzed copolymer is added to said paper stock in an amount of from 0.1 to 5% by weight, based on dry fiber.
Claim 3
Dependent Claim
34 words
The process of claim 1, wherein said hydrolyzed copolymer is prepared by copolymerizing from 60 to 40 mole % of said N-vinylformamide with from 40 to 60 mole % of said ethylenically unsaturated monomer.
Claim 4
Dependent Claim
25 words
The process of claim 1, wherein said hydrolyzed copolymer is prepared by hydrolyzing from 70 to 95% of said formyl groups to said amino groups.
Claim 5
Dependent Claim
28 words
The process of claim 1, wherein said ethylenically unsaturated monomer is selected from the group consisting of vinyl acetate and vinyl propionate and said copolymer has ester groups.
Claim 6
Dependent Claim
41 words
The process of claim 4, wherein said hydrolyzed copolymer is prepared by hydrolyzing from 70 to 95 mole % of said formyl groups to said amino groups and from 70 to 95 mole % of said ester groups to hydroxy groups.
Claim 7
Dependent Claim
24 words
The process of claim 1, further comprising the step of: draining said paper stock after adding said hydrolyzed copolymer to form a paper sheet.
Claim 8
Dependent Claim
22 words
The process of claim 1, wherein said adding step comprises mixing an aqueous solution of said hydrolyzed copolymer with said paper stock.
Claim 9
Dependent Claim
34 words
The process of claim 1, wherein said paper stock comprises an aqueous suspension of one or more fiber materials selected from the group consisting of ground wood, waste paper, sulfite pulp and sulfate pulp.
Claim 10
Dependent Claim
17 words
The process of claim 1, wherein said paper stock has a pH of from 4 to 9.
Claim 11
Dependent Claim
17 words
The process of claim 1, wherein said paper stock has a pH of from 6 to 8.
Claim 12
Dependent Claim
32 words
The process of claim 1, wherein said adding step comprises adding said hydrolyzed copolymer to said paper stock in an amount of from 0.25 to 1% by weight, based on dry fiber.
References Cited (Backward Citations)
US3597314A
Cited
US4421602A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-17 | 1994-06-18 | 1994-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-17 | 1998-06-18 | 1998-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-17 | 2002-06-18 | 2002-12-18 | $7700.00 | Window Closed / Lapsed |