Method for preparing granular porous chitosan

Claim 2

A process for preparing granular porous chitosan which comprises: a step of dispersing an acidic aqueous solution of chitosan in a hydrophobic dispersing medium; and, a step of evaporating water off while stirring the resulting dispersion.

Claim 3

A process according to claim 1, wherein said chitosan is obtained by deacetylation and has an acetylation degree of 50 to 100 mol %.

Claim 4

A process according to claim 1, wherein said chitosan has a molecular weight of 5,000 to 1,000,000, an intrinsic viscosity (30° C., 0.2M acetic acid+0.1M sodium acetate) of 0.25 to 20 dl/g-chitosan, a colloid equivalent of 1.0 to 6.2 meq/g-chitosan and a mean grain diameter of 9 to 300 mesh.

Claim 5

A process according to claim 1, wherein said acidic aqueous solution of chitosan contains a 0.5 to 5-fold amount of an acid based on chitosan.

Claim 6

A process according to claim 1, wherein a concentration of said chitosan in the acidic aqueous solution of chitosan is 0.1 to 20 wt %.

Claim 7

A process according to claim 1, wherein said hydrophobic dispersing medium is selected from a compound having a boiling point of not lower than 100° C. and a compound that is azeotropically distillable with water.

Claim 8

A process according to claim 6, wherein said hydrophobic dispersing medium is selected from decahydronaphthalene (decalin), toluene, tetrahydronaphthalene (tetralin), xylene, ethylbenzene, diethylbenzene, anisole, hexanol, octanol, dibutyl ether, petroleum benzine and ligroin.

Claim 9

A process according to claim 6, wherein an organic compound capable of being azeotropically distilled with water is selected from benzene, methanol, ethanol, acetone, cyclohexane, toluene, chloroform, 2-pentanone or 3-pentanone.

Claim 10

A process according to claim 1, wherein a ratio of said dispersion to the chitosan solution is in a range of 100:1 to 100:100.

Claim 11

A process according to claim 1, wherein said dispersion is heated to 50° to 100° C. to evaporate water off.

Claim 12

A process according to claim 1, wherein water is evaporated off by using a dispersing medium capable of being azeotropically distilled with water and heating to a temperature lower than the azeotropic point.

Claim 13

A process according to claim 11, wherein said dispersing medium capable of being azeotropically distilled with water is separated from water by reflux and re-used.

Claim 14

A process according to claim 11, wherein said dispersing medium capable of being azeotropically distilled with water is selected from benzene, cyclohexane, toluene and chloroform.

Claim 15

A process according to claim 1, wherein said stirring is performed at a rotation number of 300 to 5,000 r.p.m. at a peripheral speed of 1 to 20 m/sec.

Claim 16

A process according to claim 1, wherein at least 80 wt % of water is evaporated off from the acidic aqueous solution.

Claim 17

A process according to claim 1, wherein a surface active agent is added to the dispersion.

Claim 18

A process for preparing granular porous chitosan, comprising: preparing an acidic aqueous solution of chitosan, said chitosan having a molecular weight of 5,000 to 1,000,000 and concentration of said chitosan in the acidic aqueous solution of chitosan being 0.1 to 20 wt %, dispersing the acidic aqueous solution of chitosan in a hydrophobic dispersing medium, said hydrophobic dispersing medium being selected from a compound having a boiling point of not lower than 100° C. and a compound azeotropically distillable with water, and evaporating water from the dispersion while stirring the hydrophobic dispersing medium containing the acidic aqueous solution of chitosan.

Claim 19

A process for preparing granular porous chitosan, comprising: preparing an acidic aqueous solution of chitosan, said chitosan having a molecular weight of 5,000 to 1,000,000 and concentration of said chitosan in the acidic aqueous solution of chitosan being 0.1 to 20 wt %, dispersing the acidic aqueous solution of chitosan in a hydrophobic dispersing medium, said hydrophobic dispersing medium being selected from a compound having a boiling point of not lower than 100° C. and a compound azeotropically distillable with water, and evaporating water from the dispersion while stirring the hydrophobic dispersing medium containing the acidic aqueous solution of chitosan.