Diamond insert
Assignee: Smith International Inc
•
Filing: 1989-12-18
•
Granted: 1990-11-27
•
Expires: 2009-12-18
Abstract
Abstract A diamond cutter consisting of a polycrystalline diamond layer sintered to a cylindrically shaped tungsten carbide substrate is brazed to a cylindrically shaped mounting surface formed at a cutting end of a tungsten carbide insert body. The cylindrically shaped mounting surface of the insert body is the same diameter as the tungsten carbide substrate hence no fillet of braze material can form adjacent the juncture between the substrate and the insert body at the cutting end of the insert thereby minimizing the damaging affect of a leaching process that forms microvoids or cracks in the insert body.
Inventors
- 👤 Madapusi K. Keshavan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:48
CPC Classifications
E; E21; E21B; E21B10/00; E21B10/46; E21B10/56; E21B10/567; E21B10/573; B; B23; B23K; B23K31/00; B23K31/02; B23K31/025; Y; Y10; Y10T; Y10T407/00; Y10T407/26
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
267 words
A diamond insert having a diamond cutter at a first cutting end of a tungsten carbide insert body, the diamond cutter consisting of a layer of diamond sintered to a tungsten carbide substrate body, the substrate body being brazed to the insert body to form said diamond insert, mating surfaces formed by the substrate and the insert body adjacent an intersection formed between said substrate and said insert comprising; a peripheral surface formed by said substrate body being perpendicular to a base of said substrate body and a cutting surface of said body, and said first cutting end of said insert body forming a peripheral surface perpendicular to a mounting surface formed by said insert body, said peripheral surface completely surrounds said first cutting end, said mounting surface being parallel to said base of said substrate body, said peripheral surface of said substrate body and said peripheral surface of said first cutting end of said insert body aligning with one another forming a continuous and flush surface between said cutting end of said insert body and said substrate body after said diamond cutter is brazed to said first cutting end of said insert, the braze material being confined to said peripheral surface within a perimeter of an intersection formed between said mounting surface and said substrate to minimize the effects of cracking of the insert body due to leaching of cobalt from the mated tungsten carbide surface thereby increasing the ability of the insert body to resist the effects of shear and bending forces imparted to the insert body when said diamond insert cutter is in operation.
Claim 2
Dependent Claim
267 words
A diamond insert having a diamond cutter at a first cutting end of a tungsten carbide insert body, the diamond cutter consisting of a layer of diamond sintered to a tungsten carbide substrate body, the substrate body being brazed to the insert body to form said diamond insert, mating surfaces formed by the substrate and the insert body adjacent an intersection formed between said substrate and said insert comprising; a peripheral surface formed by said substrate body being perpendicular to a base of said substrate body and a cutting surface of said body, and said first cutting end of said insert body forming a peripheral surface perpendicular to a mounting surface formed by said insert body, said peripheral surface completely surrounds said first cutting end, said mounting surface being parallel to said base of said substrate body, said peripheral surface of said substrate body and said peripheral surface of said first cutting end of said insert body aligning with one another forming a continuous and flush surface between said cutting end of said insert body and said substrate body after said diamond cutter is brazed to said first cutting end of said insert, the braze material being confined to said peripheral surface within a perimeter of an intersection formed between said mounting surface and said substrate to minimize the effects of cracking of the insert body due to leaching of cobalt from the mated tungsten carbide surface thereby increasing the ability of the insert body to resist the effects of shear and bending forces imparted to the insert body when said diamond insert cutter is in operation.
Claim 3
Dependent Claim
16 words
The invention as set forth in claim 1 wherein said substrate body is cylindrical in shape.
Claim 4
Dependent Claim
32 words
The invention as set forth in claim 2 wherein said first cutting end of said insert body is cylindrical in shape and is the same diameter as said cylindrically shaped substrate body.
Claim 5
Independent Claim
174 words
A method of brazing a polycrystalline diamond disc sintered to a cylindrically shaped tungsten carbide substrate body to a cutting end of a tungsten carbide insert body that minimizes the effects of leaching of cobalt from an adjacent tungsten carbide material comprising the steps of: shaping said first cutting end of said insert body adjacent to a mounting surface formed by said first cutting end, to conform to the cylindrical shape and diameter of the substrate body of said diamond cutter disc, said mounting surface serving as a brazing surface for a base of said substrate body of said diamond disc, and brazing said substrate body of said diamond disc to said mounting surface of said first cutting end of said body, since the diameter of the first cutting end is the same as the diameter of the substrate, no fillet is formed therebetween that extends beyond the perimeter of the diamond disc and the matching mounting surface thereby minimizing the effects of the leaching process that creates microvoids in adjacent tungsten carbide surfaces.
Claim 6
Independent Claim
174 words
A method of brazing a polycrystalline diamond disc sintered to a cylindrically shaped tungsten carbide substrate body to a cutting end of a tungsten carbide insert body that minimizes the effects of leaching of cobalt from an adjacent tungsten carbide material comprising the steps of: shaping said first cutting end of said insert body adjacent to a mounting surface formed by said first cutting end, to conform to the cylindrical shape and diameter of the substrate body of said diamond cutter disc, said mounting surface serving as a brazing surface for a base of said substrate body of said diamond disc, and brazing said substrate body of said diamond disc to said mounting surface of said first cutting end of said body, since the diameter of the first cutting end is the same as the diameter of the substrate, no fillet is formed therebetween that extends beyond the perimeter of the diamond disc and the matching mounting surface thereby minimizing the effects of the leaching process that creates microvoids in adjacent tungsten carbide surfaces.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-26 | 1994-05-28 | 1994-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-26 | 1998-05-28 | 1998-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-26 | 2002-05-28 | 2002-11-27 | $7700.00 | Window Closed / Lapsed |