Reflective automotive coating compositions
Assignee: BASF Corp
•
Filing: 1989-06-08
•
Granted: 1990-11-20
•
Expires: 2009-06-08
Abstract
Abstract Decorative, highly reflective, adherent coatings suitable for automotive finishes comprise a base coat layer and a top coat layer. The base coat layer comprises a film-forming agent, leafing aluminum flake and, optionally, one or more colored pigmenting agents. The top coat layer comprises a transparent film-forming agent and an acidic adhesion promoting agent effective to inhibit delamination of the coating system. Optionally an alkylamine/fatty ester stabilizing agent is added to the base coat composition to stabilize the composition against deleafing during storage.
Inventors
- 👤 Sol Panush
- 👤 James M. Gelmini
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:02
CPC Classifications
B; B32; B32B; B32B27/00; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/53; B05D7/536; B05D5/00; B05D5/06; B05D5/067; B05D5/068; C; C09; C09D; C09D5/00; C09D5/38; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31605; Y10T428/31678; Y10T428/31681; Y10T428/31688; Y10T428/31692
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
163 words
A multi-layer coating system for producing adherent, decorative, highly reflective coatings on substrates comprising (a) a cured base coat layer formed on a substrate from a base coat composition comprising effective amounts of (i) a first film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) leafing aluminum flake; (b) a cured transparent top coat layer deposited on said cured basecoat layer and formed from a top, coat composition comprising effective amounts of (i) a second film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) an acidic adhesion promoting agent in an amount effective to inhibit delamination of said coating system comprising at least one selected from the group consisting of phosphoric acid, alkylbenzenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms, and alkylnaphthylenesulfonic and dialkylnaphthylenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms.
Claim 2
Dependent Claim
163 words
A multi-layer coating system for producing adherent, decorative, highly reflective coatings on substrates comprising (a) a cured base coat layer formed on a substrate from a base coat composition comprising effective amounts of (i) a first film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) leafing aluminum flake; (b) a cured transparent top coat layer deposited on said cured basecoat layer and formed from a top, coat composition comprising effective amounts of (i) a second film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) an acidic adhesion promoting agent in an amount effective to inhibit delamination of said coating system comprising at least one selected from the group consisting of phosphoric acid, alkylbenzenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms, and alkylnaphthylenesulfonic and dialkylnaphthylenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms.
Claim 3
Dependent Claim
118 words
A multi-layer coating system as defined in claim 1 wherein said base coat composition comprises (a) a cross-linking agent; and (b) a copolymer which is the reaction product of (i) from about 0.2% to about 10% of at least one ethylenically unsaturated acid selected from the group consisting of acrylic acid and methacrylic acid; (ii) from about 1% to about 50% of esters of acrylic or methacrylic acid with saturated alcohols of from one to ten carbon atoms; (iii) up to about 35% of esters of acrylic or methacrylic acid with monohydroxylated saturated alcohols of from one to ten carbon atoms; (iv) up to about 25% styrene; (v) up to about 50% of a polyester polyol copolymerizable therewith.
Claim 4
Dependent Claim
34 words
A multi-layer coating system as defined in claim 1 wherein said acidic adhesion promoting agent comprising at least one selected from the group consisting of phosphoric acid, p-toluenesulfonic acid, dodecylbenzenesulfonic acid, and dinonylnaphthalenesulfonic acid.
Claim 5
Dependent Claim
40 words
A multi-layer coating system as defined in claim 3 wherein said acidic adhesion promoting agent is present in an amount of between about 0.05 volume percent and 1.0 volume percent, based on the total volume of said top coat composition.
Claim 6
Dependent Claim
18 words
A multi-layer coating system as defined in claim 4 wherein said acidic adhesion promoting agent is phosphoric acid.
Claim 7
Dependent Claim
33 words
A multi-layer coating system as defined in claim 5 wherein said phosphoric acid is present in an amount of about 0.25 volume percent, based on the total volume of said top coat composition.
Claim 8
Dependent Claim
32 words
A multi-layer coating system as defined by claim 1 wherein said base coat composition further comprises an alkylamine/fatty ester mixture in an amount effective to stabilize said base coat composition against deleafing.
Claim 9
Dependent Claim
44 words
A multi-layer coating system as defined by claim 7 wherein said alkylamine/fatty ester mixture is present in said base coat composition in an amount of between about 0.25 weight percent and 2.0 weight percent, based upon the total weight of said base coat composition.
Claim 10
Dependent Claim
18 words
A multi-layer coating system as defined by claim 1 further comprising a transparent inorganic or organic pigmenting agent.
Claim 11
Dependent Claim
49 words
A multi-layer coating system as defined by claim 9 wherein said transparent inorganic or inorganic pigmenting agent comprises, together with said leafing aluminum, from about 1% by weight to about 20% by weight of said base coat composition, based on the total non-volatile content of said base coat composition.
Claim 12
Dependent Claim
49 words
A multi-layer coating system as defined by claim 10 wherein said pigmenting agent is selected from the group consisting of transparent iron oxide, phthalocyanine green, phthalocyanine blue, anthrapyrimidine yellow, flavanthrone yellow, imidazole orange, quinacridrone red, carbazole dioxazine violet, indanthrene blue, azo browns, isoindolinones, and high molecular weight azo pigments.
Claim 13
Independent Claim
189 words
A method of coating substrates with decorative, adherent, highly reflective coatings comprising the steps of: (a) applying to said substrate a base coat coating comprising effective amounts of (i) a first film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) leafing aluminum flake; (b) curing said base coat coating to a hard, durable coating layer; (c) applying on top of the cured base coat coating at least one top coat coating comprising effective amounts of (i) a second film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) volatile organic solvents for said second film-forming material; and (iii) an acidic adhesion promoting agent in an amount effective to inhibit delamination of said coating system comprising at least one selected from the group consisting of phosphoric acid, alkylbenzenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms, and alkylnaphthylenesulfonic and dialkylnaphthylenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms; and (d) curing said top coat coating to a hard, durable coating layer.
Claim 14
Independent Claim
189 words
A method of coating substrates with decorative, adherent, highly reflective coatings comprising the steps of: (a) applying to said substrate a base coat coating comprising effective amounts of (i) a first film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) leafing aluminum flake; (b) curing said base coat coating to a hard, durable coating layer; (c) applying on top of the cured base coat coating at least one top coat coating comprising effective amounts of (i) a second film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) volatile organic solvents for said second film-forming material; and (iii) an acidic adhesion promoting agent in an amount effective to inhibit delamination of said coating system comprising at least one selected from the group consisting of phosphoric acid, alkylbenzenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms, and alkylnaphthylenesulfonic and dialkylnaphthylenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms; and (d) curing said top coat coating to a hard, durable coating layer.
Claim 15
Dependent Claim
12 words
A method as defined in claim 12 wherein said substrate is metal.
Claim 16
Dependent Claim
153 words
An article having a multi-layer, decorative, adherent, highly reflective coating comprising (a) a cured base coat layer formed from a base coat composition comprising effective amounts of (i) a first film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) leafing aluminum flake; and (b) at least one cured transparent top coat layer formed from a top coat composition comprising effective amounts of (i) a second film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) an acidic adhesion promoting agent in an amount effective to inhibit delamination of said coating system comprising at least one selected from the group consisting of phosphoric acid, alkylbenzenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms, and alkylnaphthylenesulfonic and dialkylnaphthylenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms.
Claim 17
Dependent Claim
153 words
An article having a multi-layer, decorative, adherent, highly reflective coating comprising (a) a cured base coat layer formed from a base coat composition comprising effective amounts of (i) a first film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) leafing aluminum flake; and (b) at least one cured transparent top coat layer formed from a top coat composition comprising effective amounts of (i) a second film-forming material selected from the group consisting of acrylic resins, alkyd resins, polyurethane resins, polyester resins and aminoplast resins; (ii) an acidic adhesion promoting agent in an amount effective to inhibit delamination of said coating system comprising at least one selected from the group consisting of phosphoric acid, alkylbenzenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms, and alkylnaphthylenesulfonic and dialkylnaphthylenesulfonic acids wherein the alkyl group contains from one to twelve carbon atoms.
References Cited (Backward Citations)
US3050412A
Cited
US3232903A
Cited
US3198759A
Cited
US3255135A
Cited
US3639149A
Cited
US4048136A
Cited
US4499143A
Cited
US4605687A
Cited
US4781949A
Cited
US4731290A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-19 | 1994-05-21 | 1994-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-19 | 1998-05-21 | 1998-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-19 | 2002-05-21 | 2002-11-20 | $7700.00 | Window Closed / Lapsed |