US4970783A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making split remateable connecting rod portions
Assignee: Ford Global Technologies LLC
•
Filing: 1989-12-14
•
Granted: 1990-11-20
•
Expires: 2009-12-14
Abstract
Abstract A method of cracking bearing assembles including the steps of (a) forming a ductile metal (steel, aluminum or titanium) connecting rod in one piece (e.g., by hot forging) having an annular wall defining a crankshaft opening with preformed surface crevices for guiding the initiation of a cracking plane that extends across the crank opening; (b) charging (i.e., for about 40 seconds) the region of such wall along at least one portion of the cracking plane with hydrogen by means of an electrolytic cell or by means of reacting the metal rod with a strong acid (e.g., concentrated sulfuric) to cause hydrogen to dissolve in the metal to facilitate hydrogen stress cracking thereat, with or without the imposition of static mechanical tensile loading at such crevices (i.e., for about 40 seconds) of a magnitude insufficient to cause yielding of the metal; and (c) prolonging, increasing, or imposing the static mechanical loading (i.e., for another 40 seconds) at the crevices to effect fracture across the entire cracking plane and thereby separate the connecting rod into a cap and body with rough, fractured mating surfaces.
Inventors
- 👤 Moses A. Olaniran
- 👤 Charles A. Stickels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:28
CPC Classifications
B; B23; B23D; B23D31/00; B23D31/002; B23D31/003; F; F16; F16C; F16C9/00; F16C9/04; F16C9/045; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49229; Y10T29/49231; Y10T29/49233; Y10T29/49288; Y10T29/49789; Y10T29/4979; Y10T29/49792; Y10T29/49796; Y10T74/00; Y10T74/21; Y10T74/2142; Y10T74/2162
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
160 words
A method of making a connecting rod for attachment to a bearing journal by separation of the connecting rod, comprising: (a) forming a ductile metal connecting rod in one piece having an annular wall defining a crank opening with preformed surface crevices for guiding the initiation of a cracking plane that extends across said crank opening; (b) exposing at least a region of said wall adjacent to and including at least one crevice to a source of hydrogen to effect dissolution of said hydrogen into the metal of the rod near or at the root of such crevice and promote cracking thereat With or without the imposition at said crevice of static mechanical loading creating a mechanical stress insufficient to cause yielding; and (c) prolonging, increasing, or imposing said static mechanical loading at said crevices to effect complete fracture across the entire cracking plane and thereby separate the connecting rod into a cap and body with rough, fractured mating surfaces.
Claim 2
Independent Claim
160 words
A method of making a connecting rod for attachment to a bearing journal by separation of the connecting rod, comprising: (a) forming a ductile metal connecting rod in one piece having an annular wall defining a crank opening with preformed surface crevices for guiding the initiation of a cracking plane that extends across said crank opening; (b) exposing at least a region of said wall adjacent to and including at least one crevice to a source of hydrogen to effect dissolution of said hydrogen into the metal of the rod near or at the root of such crevice and promote cracking thereat With or without the imposition at said crevice of static mechanical loading creating a mechanical stress insufficient to cause yielding; and (c) prolonging, increasing, or imposing said static mechanical loading at said crevices to effect complete fracture across the entire cracking plane and thereby separate the connecting rod into a cap and body with rough, fractured mating surfaces.
Claim 3
Dependent Claim
47 words
The method as in claim 1, in which said method further comprises a step (d): remating the cap and body after insertion of said bearing journal by a compression coupling drawing the cap and body together to effect substantially an exact remating of the fractured mating surfaces.
Claim 4
Dependent Claim
29 words
The method as in claim 1, in which said ductile metal connecting rod is formed of steel by hot forging at a temperature in the range of 1800°-2400° F.
Claim 5
Dependent Claim
30 words
The method as in claim 1, in which said connecting rod is constituted of a ductile metal selected from the group consisting of ductile (nodular) iron, aluminum, steel, and titanium.
Claim 6
Dependent Claim
15 words
The method as in claim 4, in which said ductile metal is SAE 1151 steel.
Claim 7
Dependent Claim
22 words
The method as in claim 1, in which said preformed crevices are forged thereinto at the time the connecting rod is forged.
Claim 8
Dependent Claim
40 words
The method as in claim 1, in which said preformed crevices are machined into the connecting rod subsequent to forging of the connecting rod, said crevices being constituted as sharp-angled notches having an included angle in the range of 30°-120°.
Claim 9
Dependent Claim
39 words
The method as in claim 1, in which said exposing step is carried out by depositing concentrated acid within the crevice while simultaneously subjecting the crevice to low tensile mechanical loading insufficient to cause plastic yielding of the metal.
Claim 10
Dependent Claim
46 words
The method as in claim 1, in which said exposing step is carried out by immersing said region in an aqueous acid solution wherein the connecting rod is a cathode and a steel wall within said bath is constituted as the anode for an electrolytic system.
Claim 11
Dependent Claim
23 words
The method as in claim 9, in which said aqueous acid solution is maintained at a temperature in the range of 50°-100° F.
Claim 12
Dependent Claim
20 words
The method as in claim 1, in which said region is constituted as the lateral margin along a cracking plane.
Claim 13
Dependent Claim
20 words
The method as in claim 11, in which said region is defined by masking the remainder of said connecting rod.
Claim 14
Dependent Claim
14 words
The method as in claim 1, in which said region is only the crevice.
Claim 15
Dependent Claim
39 words
The method as in claim 1, in which static tensile mechanical loading is applied by an expandable fixture inserted within the large crankshaft opening of said connecting rod to apply a force normal to a surface of the crevices.
Claim 16
Dependent Claim
39 words
The method as in claim 1, which further comprises the step of reversing hydrogen dissolution by a baking step comprising heating the connecting rod to a temperature in the range of 300°-400° F. for a period of 1-4 hours.
Claim 17
Independent Claim
113 words
A method of making split remateable connecting rod portions from a unitary ductile rod having an annular wall defining a crank opening with preformed surface crevices along a cracking plane, comprising: (a) charging hydrogen into a region of said wall along at least one part of said cracking plane including at least one crevice, with or without the concurrent application of static mechanical tensile loading at said included crevice insufficient to cause metal yielding; and (b) imposing, prolonging or increasing static mechanical tensile loading at said included crevice to effect fracture across the entire cracking plane and thereby separate the unitary connecting rod into a cap and body with rough fractured mating surfaces.
Claim 18
Independent Claim
113 words
A method of making split remateable connecting rod portions from a unitary ductile rod having an annular wall defining a crank opening with preformed surface crevices along a cracking plane, comprising: (a) charging hydrogen into a region of said wall along at least one part of said cracking plane including at least one crevice, with or without the concurrent application of static mechanical tensile loading at said included crevice insufficient to cause metal yielding; and (b) imposing, prolonging or increasing static mechanical tensile loading at said included crevice to effect fracture across the entire cracking plane and thereby separate the unitary connecting rod into a cap and body with rough fractured mating surfaces.
Claim 19
Dependent Claim
25 words
The method as in claim 16, in which said charging is carried out by creation of an electrolytic cell for dissolving hydrogen into said region.
Claim 20
Dependent Claim
44 words
The method as in claim 16, in which said charging is carried out by adding concentrated acid to the metal only at said region and concurrent imposition of static mechanical stress to induce an electrolytic cell without the imposition of an outside current source.
Claim 21
Dependent Claim
27 words
The method as in claim 18, in which charging is carried out for about 20-60 seconds and said step (b) is carried out for about 30-60 seconds.
Claim 22
Dependent Claim
42 words
The method as in claim 16, in which static mechanical loading is a static energy force that will effect a tensile stress in a metal at the root of the crevice of about 10-30% below the plastic yielding stress for said metal.
References Cited (Backward Citations)
USRE26261E
Cited
US2553935A
Cited
US3751080A
Cited
US3994054A
Cited
US4198879A
Cited
US4304593A
Cited
US4569109A
Cited
US4802269A
Cited
US4768694A
Cited
US4860419A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-19 | 1994-05-21 | 1994-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-19 | 1998-05-21 | 1998-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-19 | 2002-05-21 | 2002-11-20 | $7700.00 | Window Closed / Lapsed |