Polymeric solid electrolytes and production process thereof
Assignee: Eneos Corp
•
Filing: 1989-12-04
•
Granted: 1990-11-13
•
Expires: 2009-12-04
Abstract
Abstract Polymeric solid electrolytes are formed by the present invention, namely, by incorporating a low molecular weight polyethylene glycol, a high molecular weight polyethylene oxide and an alkali metal or ammonium salt in a specific cinnamate ester compound, followed by a polymerization and crosslinking. The polymeric solid electrolytes have high ionic conductivity, high strength as a film, and good adhesion with electrodes. Therefore, they can be applied widely as ionics materials, e.g., for the total solidification of lithium batteries and plastic batteries and high capacity condensers and as electrolytes for electrochromic displays.
Inventors
- 👤 Nobuyuki Kuroda
- 👤 Hiroshi Kobayashi
- 👤 Kazuo Matsuura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:13
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/022; H01G9/025; C; C08; C08L; C08L71/00; C08L71/02; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/122; H01M; H01M6/00; H01M6/14; H01M6/18; H01M6/181
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
95 words
A polymeric solid electrolyte comprising: (i) crosslinked molecules of a radiation-cured substance of a cinnamate ester compound represented by the following formula (I): ##STR4## wherein R represents a hydrogen atom or an alkyl group having 1-5 carbon atoms and n stands for an integer of 3-40; and (ii) (a) a low molecular weight polyethylene glycol methyl-etherified at both terminals thereof; (b) a high molecular weight polyethylene oxide; and (c) an alkali metal or ammonium salt, said polyethylene glycol (a), polyethylene oxide (b) and salt (c) being contained in said crosslinked molecules of said radiation-cured substance.
Claim 2
Dependent Claim
95 words
A polymeric solid electrolyte comprising: (i) crosslinked molecules of a radiation-cured substance of a cinnamate ester compound represented by the following formula (I): ##STR4## wherein R represents a hydrogen atom or an alkyl group having 1-5 carbon atoms and n stands for an integer of 3-40; and (ii) (a) a low molecular weight polyethylene glycol methyl-etherified at both terminals thereof; (b) a high molecular weight polyethylene oxide; and (c) an alkali metal or ammonium salt, said polyethylene glycol (a), polyethylene oxide (b) and salt (c) being contained in said crosslinked molecules of said radiation-cured substance.
Claim 3
Dependent Claim
26 words
The polymeric solid electrolyte of claim 1, wherein each ester moiety in the cinnamate ester compound represented by the formula (I) contains 5-30 oxyalkylene units (n=5-30).
Claim 4
Dependent Claim
26 words
The polymeric solid electrolyte of claim 2, wherein the oxyalkylene units are oxyethylene units or oxypropylene units or a mixture of both oxyethylene and oxypropylene units.
Claim 5
Dependent Claim
22 words
The polymeric solid electrolyte of claim 1, wherein the molecular weight of the polyethylene glycol (a) is in a range of 100-3,000.
Claim 6
Dependent Claim
22 words
The polymeric solid electrolyte of claim 4, wherein the molecular weight of the polyethylene glycol (a) is in a range of 200-2,000.
Claim 7
Dependent Claim
20 words
The polymeric solid electrolyte of claim 1, wherein the molecular weight of the polyethylene oxide (b) is at least 100,000.
Claim 8
Dependent Claim
22 words
The polymeric solid electrolyte of claim 6, wherein the molecular weight of the polyethylene oxide (b) is in a range of 100,000-3,000,000.
Claim 9
Dependent Claim
22 words
The polymeric solid electrolyte of claim 7, wherein the molecular weight of the polyethylene oxide (b) is in a range of 200,000-2,000,000.
Claim 10
Dependent Claim
69 words
The polymeric solid electrolyte of claim 1, wherein the alkali metal salt (c) is selected from the group consisting of alkali metal perchlorates such as lithium perchlorate, sodium perchlorate and potassium perchlorate, alkali metal tetrafluoroborates such as lithium tetrafluoroborate, sodium tetrafluoroborate and potassium tetrafluoroborate, alkali metal hexafluorophosphates such as lithium hexafluorophosphate and potassium hexafluorophosphate, alkali metal trifluoroacetates such as lithium trifluoroacetate, and alkali metal trifluoromethanesulfonates such as lithium trifluoromethanesulfonate.
Claim 11
Dependent Claim
55 words
The polymeric solid electrolyte of claim 1, wherein the ammonium salt (c) is selected from the group consisting of quaternary ammonium salts of perchlorates such as tetraisopropyl ammonium perchlorate and tetra-n-butyl ammonium perchlorate, quaternary ammonium tetrafluoroborates and hexafluorophosphates such as tetra-n-butyl ammonium tetrafluoroborate and tetra-n-butyl ammonium hexafluorophosphate, and quaternary ammonium trifluoromethanesulfonatessuch as tetra-n-butyl ammonium trifluoromethanesulfonate.
Claim 12
Dependent Claim
27 words
The polymeric solid electrolyte of claim 1, further comprising a copolymer of methoxypolyethylene glycol monomethacrylate and methyl methacrylate or a copolymer of methoxypolyethylene glycol monomethacrylate and acrylonitrile.
Claim 13
Dependent Claim
95 words
A process for the production of a polymeric solid electrolyte, which comprises: (i) reacting a trifunctional polyethylene glycol with cinnamic chloride to obtain a compound represented by the following formula (I): ##STR5## wherein R represents a hydrogen atom or an alkyl group having 1-5 carbon atoms and n stands for an integer of 3-40; and (ii) causing the compound to undergo a crosslinking reaction in the presence of: (a) a low molecular weight polyethylene glycol methyl-etherified at both terminals thereof; (b) a high molecular weight polyethylene oxide; and (c) an alkali metal or ammonium salt.
Claim 14
Dependent Claim
95 words
A process for the production of a polymeric solid electrolyte, which comprises: (i) reacting a trifunctional polyethylene glycol with cinnamic chloride to obtain a compound represented by the following formula (I): ##STR5## wherein R represents a hydrogen atom or an alkyl group having 1-5 carbon atoms and n stands for an integer of 3-40; and (ii) causing the compound to undergo a crosslinking reaction in the presence of: (a) a low molecular weight polyethylene glycol methyl-etherified at both terminals thereof; (b) a high molecular weight polyethylene oxide; and (c) an alkali metal or ammonium salt.
Claim 15
Dependent Claim
16 words
The process of claim 12, wherein the crosslinking reaction is catalyzed by exposure to a radiation.
Claim 16
Dependent Claim
25 words
The process of claim 12, wherein the weight ratio of the polyethylene glycol (a) to the polyethylene oxide (b) is in a range of 1:0.1-1:10.
Claim 17
Dependent Claim
39 words
The process of claim 12, wherein the compound of the formula (I) is used in a proportion of 10-200 parts by weight per 100 parts by weight of the sum of the polyethylene glycol (a) and polyethylene oxide (b).
Claim 18
Dependent Claim
36 words
The process of claim 15, wherein the compound (I) is used in a proportion of 20-100 parts by weight per 100 parts by weight of the sum of the polyethylene glycol (a) and polyethylene oxide (b).
Claim 19
Dependent Claim
42 words
The process of claim 12, wherein the alkali metal or ammonium salt (c) is used in a proportion of 1-30 parts by weight per 100 parts by weight of the sum of the polyethylene glycol (a), polyethylene oxide (b) and compound (I).
Claim 20
Dependent Claim
42 words
The process of claim 17, wherein the alkali metal or ammonium salt (c) is used in a proportion of 3-20 parts by weight per 100 parts by weight of the sum of the polyethylene glycol (a), polyethylene oxide (b) and compound (I).
Claim 21
Dependent Claim
34 words
The process of claim 12, wherein the crosslinking reaction is carried out in the presence of a copolymer of methoxypolyethylene glycol monomethacrylate and methyl methacrylate or a copolymer of methoxypolyethylene glycol monomethacrylate and acrylonitrile.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-12 | 1994-05-14 | 1994-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-12 | 1998-05-14 | 1998-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-12 | 2002-05-14 | 2002-11-13 | $7700.00 | Window Closed / Lapsed |