Method of haze-free polishing for semiconductor wafers
Assignee: Siltronic AG
•
Filing: 1988-09-28
•
Granted: 1990-11-06
•
Expires: 2008-09-28
Abstract
Abstract A polishing process in which haze-free semiconductor wafers can be obtained in a single-stage process in which an initial phase of the polishing operation is carried out in the usual manner in the alkaline region. This initial stage is followed by a final phase in which polishing is carried out, at a pH of 3 to 7, in the presence of additives in the polishing agent which reduce the amount of material removed by polishing. Consequently, it may be possible to dispense with polishing agent components which act mechanically. Both phases can be carried out on one and the same equipment without interrupting the polishing operation.
Inventors
- 👤 Helene Prigge
- 👤 Anton Schnegg
- 👤 Gerhard Brehm
- 👤 Herbert Jacob
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:55
CPC Classifications
H; H10; H10P; H10P52/00; H10P52/40; H10P52/402
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
199 words
In a process for the haze-free polishing of a semiconductor surface by means of a polishing cloth, the improvement comprising the steps of: performing a polishing operation in a one-stage process by applying a polishing agent having at least one member selected from the group consisting of a polishing sol, a polishing gel, an alkaline polishing agent containing solid components, and a combination thereof to the polishing cloth in an initial phase of the polishing operation to thereby obtain a removal in the range of from 10 to 60 μm from the said semiconductor surface; and applying to the polishing cloth in a final phase of said polishing operation a polishing solution which is adjusted to a pH range of 3 to 8 and which contains at least one member selected from the group consisting of (a) from 0.1 to 10% by volume of at least one polar compound containing hydrophilic and hydrophobic groups and also selected from the group consisting of alcohols, ketones, ethers, esters and amides, (b) an ingredient which contains less than 0.1% by volume of a surface-active substance, and (c) a combination of (a) and (b) to thereby produce a haze-free surface for said semiconductor.
Claim 2
Dependent Claim
199 words
In a process for the haze-free polishing of a semiconductor surface by means of a polishing cloth, the improvement comprising the steps of: performing a polishing operation in a one-stage process by applying a polishing agent having at least one member selected from the group consisting of a polishing sol, a polishing gel, an alkaline polishing agent containing solid components, and a combination thereof to the polishing cloth in an initial phase of the polishing operation to thereby obtain a removal in the range of from 10 to 60 μm from the said semiconductor surface; and applying to the polishing cloth in a final phase of said polishing operation a polishing solution which is adjusted to a pH range of 3 to 8 and which contains at least one member selected from the group consisting of (a) from 0.1 to 10% by volume of at least one polar compound containing hydrophilic and hydrophobic groups and also selected from the group consisting of alcohols, ketones, ethers, esters and amides, (b) an ingredient which contains less than 0.1% by volume of a surface-active substance, and (c) a combination of (a) and (b) to thereby produce a haze-free surface for said semiconductor.
Claim 3
Dependent Claim
42 words
The process as claimed in claim 1, wherein up to 10% by volume of at least one member selected from the group consisting of polishing sol, polishing gel, solid polishing components and a combination thereof are additionally added to the polishing solution.
Claim 4
Dependent Claim
27 words
The process as claimed in claim 1, wherein said polar compound is an organosilicon compound selected from the group consisting of silanols, trimethylsilanol, hexamethyldisilazane, hexamethyldisiloxane and dimethyldimethoxysilane.
Claim 5
Dependent Claim
36 words
The process as claimed in claim 1, wherein said polishing agent is adjusted to a pH of 11 to 13 and contains up to 20% by volume of said member is used in said initial phase.
Claim 6
Dependent Claim
70 words
The process as claimed in claim 1, wherein, between the initial and final phase of said polishing operation, an intermediate phase is performed in which a polishing agent adjusted to a pH of 9 to 11 and containing up to 10% by volume of at least one member selected from the group consisting of a polishing sol, a polishing gel, a solid polishing component and a combination thereof is used.
Claim 7
Dependent Claim
20 words
The process as claimed in claim 5, wherein said intermediate phase has a time duration of 2 to 10 minutes.
Claim 8
Dependent Claim
20 words
The process as claimed in claim 1, wherein the final phase has a time duration of 3 to 20 minutes.
Claim 9
Dependent Claim
20 words
The process as claimed in claim 1, wherein the time duration of the initial phase is 5 to 100 minutes.
References Cited (Backward Citations)
US3485608A
Cited
US3874129A
Cited
US3979239A
Cited
US4070797A
Cited
US4064660A
Cited
US4050954A
Cited
US4549374A
Cited
US4837923A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-05 | 1994-05-07 | 1994-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-05 | 1998-05-07 | 1998-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-05 | 2002-05-07 | 2002-11-06 | $7700.00 | Window Closed / Lapsed |