Tire having decorative applique on sidewall and method for preparing same
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1988-10-11
•
Granted: 1990-11-06
•
Expires: 2008-10-11
Abstract
Abstract Tires having white sidewalls are very popular in the United States and Canada. Tires having white lettering thereon are also very popular. This invention discloses a process for preparing such tires having decorative appliques thereon. By practicing the process of this invention, tires having better uniformity can be built at lower costs than when standard tire building techniques are utilized. This invention specifically relates to a method of preparing a pneumatic rubber tire having a decorative design on the sidewall thereof which comprises (a) applying the decorative design to the sidewall of an uncured tire and (b) curing the tire; wherein the decorative design is comprised of from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and from about 25 weight percent to about 75 weight perecent of at least one polydiene rubber which is cocurable with said sydiotactic 1,2-polybutadiene, at least one pigment or colorant, sulfur, and zinc oxide.
Inventors
- 👤 Robert J. Gartland
- 👤 Anthony F. Finelli
- 👤 Anthony J. Bell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 18:22
CPC Classifications
B; B60; B60C; B60C13/00; B60C13/04; B29; B29D; B29D30/00; B29D30/06; B29D30/72; B29D2030/726; Y; Y10; Y10S; Y10S152/00; Y10S152/12
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
129 words
A pneumatic tire having a decorative applique on the sidewall thereof, comprising an outer circumferential tread, a supporting carcass therefor, two-spaced beads and two rubber sidewalls connecting said beads; wherein at least one of said sidewalls has a decorative applique thereon; wherein the decorative applique has a thickness which is within the range of about 10 mils to about 100 mils; and wherein said decorative applique is comprised of from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and from about 25 weight percent to about 75 weight percent of at least one polydiene rubber which is cocured with said syndiotactic 1,2-polybutadiene, and at least one pigment or colorant.
Claim 2
Dependent Claim
129 words
A pneumatic tire having a decorative applique on the sidewall thereof, comprising an outer circumferential tread, a supporting carcass therefor, two-spaced beads and two rubber sidewalls connecting said beads; wherein at least one of said sidewalls has a decorative applique thereon; wherein the decorative applique has a thickness which is within the range of about 10 mils to about 100 mils; and wherein said decorative applique is comprised of from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and from about 25 weight percent to about 75 weight percent of at least one polydiene rubber which is cocured with said syndiotactic 1,2-polybutadiene, and at least one pigment or colorant.
Claim 3
Independent Claim
118 words
A method of preparing a pneumatic rubber tire having a decorative applique on the sidewall thereof which comprises (a) applying the decorative applique having a thickness which ranges from about 10 mils to about 100 mils to the sidewall of an uncured tire and (b) curing the tire; wherein the decorative applique is comprised of from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and from about 25 weight percent to about 75 weight percent of at least one polydiene rubber which is cocurable with said syndiotactic 1,2-polybutadiene, sulfur, zinc oxide and at least one pigment or colorant.
Claim 4
Independent Claim
118 words
A method of preparing a pneumatic rubber tire having a decorative applique on the sidewall thereof which comprises (a) applying the decorative applique having a thickness which ranges from about 10 mils to about 100 mils to the sidewall of an uncured tire and (b) curing the tire; wherein the decorative applique is comprised of from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and from about 25 weight percent to about 75 weight percent of at least one polydiene rubber which is cocurable with said syndiotactic 1,2-polybutadiene, sulfur, zinc oxide and at least one pigment or colorant.
Claim 5
Dependent Claim
131 words
A pneumatic tire having a decorative applique on at least one sidewall thereof, the improvement which comprises utilizing as the material for the decorative applique a blend of syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and at least one rubber which is cocurable with the syndiotactic 1,2-polybutadiene; wherein the blend contains from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene and from about 25 weight percent to about 75 weight percent of the rubber based upon the total amount of polymers in the blend, wherein the blend further comprises at least one pigment or colorant, and wherein the decorative applique has a thickness which is within the range of about 10 mils to about 100 mils.
Claim 6
Dependent Claim
131 words
A pneumatic tire having a decorative applique on at least one sidewall thereof, the improvement which comprises utilizing as the material for the decorative applique a blend of syndiotactic 1,2-polybutadiene having a melting point which is within the range of about 100° C. to about 160° C. and at least one rubber which is cocurable with the syndiotactic 1,2-polybutadiene; wherein the blend contains from about 25 weight percent to about 75 weight percent syndiotactic 1,2-polybutadiene and from about 25 weight percent to about 75 weight percent of the rubber based upon the total amount of polymers in the blend, wherein the blend further comprises at least one pigment or colorant, and wherein the decorative applique has a thickness which is within the range of about 10 mils to about 100 mils.
Claim 7
Dependent Claim
13 words
A pneumatic tire as specified in claim 3 wherein the rubber is cis-1,4-polybutadiene.
Claim 8
Dependent Claim
14 words
A pneumatic tire as specified in claim 3 wherein the rubber is styrene-butadiene rubber.
Claim 9
Dependent Claim
17 words
A pneumatic tire as specified in claim 3 wherein the rubber is natural rubber or synthetic polyisoprene.
Claim 10
Dependent Claim
24 words
A pneumatic tire as specified in claim 3 wherein the rubber is a blend of a halobutyl rubber, natural rubber, and an EPDM rubber.
Claim 11
Dependent Claim
16 words
A pneumatic tire as specified in claim 7 wherein the halobutyl rubber is a chlorobutyl rubber.
Claim 12
Dependent Claim
45 words
A pneumatic tire as specified in claim 8 wherein the rubber is comprised of from about 30 to about 80 weight percent chlorobutyl rubber, from about 15 to about 55 weight percent natural rubber, and from about 2 to about 10 weight percent EPDM rubber.
Claim 13
Dependent Claim
26 words
A pneumatic tire as specified in claim 9 wherein the blend is comprised of from about 33 weight percent to about 67 weight percent syndiotactic 1,2-polybutadiene.
Claim 14
Dependent Claim
50 words
A pneumatic tire as specified in claim 10 wherein the rubber is comprised of from about 55 weight percent to about 65 weight percent chlorobutyl rubber, from about 25 weight percent to about 45 weight percent natural rubber, and from about 3 weight to about 7 weight percent EPDM rubber.
Claim 15
Dependent Claim
26 words
A pneumatic tire as specified in claim 11 wherein said blend is comprised of from about 45 weight percent to about 55 weight percent syndiotactic 1,2-polybutadiene.
Claim 16
Dependent Claim
28 words
A pneumatic tire as specified in claim 12 wherein the melting point of the syndiotactic 1,2-polybutadiene is within the range of about 100° C. to about 160° C.
Claim 17
Dependent Claim
28 words
A pneumatic tire as specified in claim 12 wherein the melting point of the syndiotactic 1,2-polybutadiene is within the range of about 120° C. to about 160° C.
Claim 18
Dependent Claim
16 words
A pneumatic tire as specified in claim 12 wherein the pigment or colorant is titanium dioxide.
Claim 19
Dependent Claim
31 words
A pneumatic tire as specified in claim 12 wherein the colorant is selected from the group consisting of diarylid yellow 17, pththalocy blue 15, diarylid orange 13, and perm red 28.
Claim 20
Dependent Claim
23 words
A method as specified in claim 2 wherein the decorative applique is positioned in a mold prior to putting the uncured tire therein.
Claim 21
Dependent Claim
19 words
A method as specified in claim 17 wherein the decorative applique is cocured with the sidewall of the tire.
Claim 22
Dependent Claim
28 words
A pneumatic tire as specified in claim 12 wherein the melting point of the syndiotactic 1,2-polybutadiene is within the range of about 150° C. to about 150° C.
References Cited (Backward Citations)
US2979099A
Cited
US4220564A
Cited
JPS54132907A
Cited
JPS55152605A
Cited
JPS5834834A
Cited
US4684431A
Cited
US4790365A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-05 | 1994-05-07 | 1994-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-05 | 1998-05-07 | 1998-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-05 | 2002-05-07 | 2002-11-06 | $7700.00 | Window Closed / Lapsed |