Method for electrically joining superconductors to themselves, to normal conductors, and to semi-conductors
Assignee: TRUSTEES OF BOSTON UNIVERSITY BOSTON MA 02215 A CORP OF
•
Filing: 1989-06-30
•
Granted: 1990-10-30
•
Expires: 2009-06-30
Abstract
Abstract A unique class of bonding alloys and methods for their use are provided which enable the user to electrically join superconductive materials to themselves, to normal conductive materials, or to semi-conductors. The bonding alloys have enhanced wetting properties and a melting point less than 100° C. in all instances. The bonding alloys are unusual and advantageous in that they create an intimate, direct, mechanical and electrical contact between the superconductive material and any other electrical conductor while minimizing mechanical and chemical stresses and avoiding alterations to the superconductive material itself.
Inventors
- 👤 George O. Zimmerman
- 👤 Alvaro Kaplan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:46
CPC Classifications
B; B23; B23K; B23K1/00; B23K1/19; B23K35/00; B23K35/22; B23K35/24; B23K35/26; H; H01; H01R; H01R4/00; H01R4/58; H01R4/68; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0744; H10N60/80
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
171 words
A method for electrically joining superconductive materials to themselves, to conductive materials, or to semi-conductive materials, said method comprising the steps of: obtaining a bonding alloy comprising from about 50 to 90 atomic percent indium, and an additive comprised of from about 0 to about 40 atomic percent mercury, from 0 to about 40 atomic percent gallium, and from 0 to about 55 atomic percent bismuth; preparing a surface of each material to be joined as a clean surface; heating said alloy such that at least a non-oxidized, semi-liquid state is formed; introducing said heated alloy to each non-oxidized surface such that each of said surfaces becomes substantially wetted by said heated alloy; applying additional heated alloy to each of said wetted surfaces concurrently to form a continuous alloy juncture between said materials; and allowing said alloy juncture to solidify such that a joined electrical interface resistance of not more than 10 -3 ohms per square centimeter is provided by said solidified alloy at temperatures not greater than about 20° C.
Claim 2
Independent Claim
171 words
A method for electrically joining superconductive materials to themselves, to conductive materials, or to semi-conductive materials, said method comprising the steps of: obtaining a bonding alloy comprising from about 50 to 90 atomic percent indium, and an additive comprised of from about 0 to about 40 atomic percent mercury, from 0 to about 40 atomic percent gallium, and from 0 to about 55 atomic percent bismuth; preparing a surface of each material to be joined as a clean surface; heating said alloy such that at least a non-oxidized, semi-liquid state is formed; introducing said heated alloy to each non-oxidized surface such that each of said surfaces becomes substantially wetted by said heated alloy; applying additional heated alloy to each of said wetted surfaces concurrently to form a continuous alloy juncture between said materials; and allowing said alloy juncture to solidify such that a joined electrical interface resistance of not more than 10 -3 ohms per square centimeter is provided by said solidified alloy at temperatures not greater than about 20° C.
Claim 3
Independent Claim
195 words
A method for electrically joining superconductive materials to themselves, to conductive materials, or to semi-conductive materials, said method comprising the steps of: obtaining a bonding alloy comprising from about 50 to 90 atomic percent indium, and an additive comprised of from about 0 to about 40 atomic percent mercury, from 0 to about 40 atomic percent gallium, from 0 to about 55 atomic percent bismuth, from 0 to about 30 atomic percent cadmium, from 0 to about 15 atomic percent tin, and from 0 to about 10 atomic percent lead; preparing a surface of each material to be joined as a clean surface; heating said alloy such that at least a non-oxidized, semi-liquid state is formed; introducing said alloy amalgam to each non-oxidized surface such that each of said surfaces becomes substantially wetted by said heated alloy; applying additional heated alloy to each of said wetted surfaces concurrently to form a continuous alloy juncture between said materials; and allowing said alloy juncture to solidify such that a joined electrical interface resistance of not more than 10 -3 ohms per square centimeter is provided by said solidified alloy at temperatures not greater than about 20° C.
Claim 4
Independent Claim
195 words
A method for electrically joining superconductive materials to themselves, to conductive materials, or to semi-conductive materials, said method comprising the steps of: obtaining a bonding alloy comprising from about 50 to 90 atomic percent indium, and an additive comprised of from about 0 to about 40 atomic percent mercury, from 0 to about 40 atomic percent gallium, from 0 to about 55 atomic percent bismuth, from 0 to about 30 atomic percent cadmium, from 0 to about 15 atomic percent tin, and from 0 to about 10 atomic percent lead; preparing a surface of each material to be joined as a clean surface; heating said alloy such that at least a non-oxidized, semi-liquid state is formed; introducing said alloy amalgam to each non-oxidized surface such that each of said surfaces becomes substantially wetted by said heated alloy; applying additional heated alloy to each of said wetted surfaces concurrently to form a continuous alloy juncture between said materials; and allowing said alloy juncture to solidify such that a joined electrical interface resistance of not more than 10 -3 ohms per square centimeter is provided by said solidified alloy at temperatures not greater than about 20° C.
Claim 5
Dependent Claim
19 words
The method as recited in claim 1 wherein said bonding alloy is comprised essentially of only indium and mercury.
Claim 6
Dependent Claim
19 words
The method as recited in claim 1 wherein said bonding alloy is comprised essentially of only indium and gallium.
Claim 7
Dependent Claim
19 words
The method as recited in claim 1 wherein said bonding alloy is comprised essentially of only indium and bismuth.
Claim 8
Dependent Claim
24 words
The method as recited in claim 1 wherein said bonding alloy is comprised of indium and an additive comprising at least two other metals.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-29 | 1994-04-30 | 1994-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-29 | 1998-04-30 | 1998-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-29 | 2002-04-30 | 2002-10-30 | $7700.00 | Window Closed / Lapsed |