Ceramic foam for filters for cleaning exhaust gases of diesel engines
Assignee: SWISS ALUMINIUM Ltd A CORP OF SWITZERLAND
•
Filing: 1988-12-06
•
Granted: 1990-10-23
•
Expires: 2008-12-06
Abstract
Abstract In certain operating conditions of diesel engines, diesel soot filters which are made of known ceramic foam and filter efficiently per se have zero or only a very low degree of particle filtration, in particular at hight exhaust temperatures and exhaust velocities, that is, above all when the diesel engines are running under full load. Ceramic foam filters for cleaning exhaust gases of diesel engines in which the surface is roughened and wherein the peak-to-peak interval is approximately 1 to 100 μm, preferably 1 to 10 μm, do not have this disadvantage. A ceramic foam of this kind is manufactured by roughening the surface by deposition of inorganic materials and, if required, subsequent decomposition by temperature treatment.
Inventors
- 👤 Olaf Frei
- 👤 Max Frish
- 👤 Viktor Bodmer
- 👤 Tiberiu Mizrah
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:38
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B01; B01D; B01D39/00; B01D39/14; B01D39/20; B01D39/2068; B01D39/2093; C04B38/00; C04B38/0051; C04B41/45; C04B41/50; C04B41/5025; C04B41/5031; C04B41/80; C04B41/81; C04B41/85; C04B41/87; F; F01; F01N; F01N3/00; F01N3/02; F01N3/021; F01N3/022; F01N3/0222; F01N2330/00; F01N2330/06; F02; F02B; F02B3/00; F02B3/06; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
120 words
Method for the manufacture of a ceramic foam for filters for cleaning exhaust gases of diesel engines which comprises: providing a ceramic foam filter body having a plurality of pores; roughening at least one surface of said body without blocking said pores so as to improve a filter action and enhance the capture of diesel soot particles; and said roughening step including depositing particles formed from an inorganic material on said at least one surface and thereby forming a roughening layer having a thickness in the range of from about 10 μm to about 200 μm and a particle peak-to-peak interval of approximately 1 μm to about 100 μm so as to insure said capture of said diesel soot particles.
Claim 2
Dependent Claim
120 words
Method for the manufacture of a ceramic foam for filters for cleaning exhaust gases of diesel engines which comprises: providing a ceramic foam filter body having a plurality of pores; roughening at least one surface of said body without blocking said pores so as to improve a filter action and enhance the capture of diesel soot particles; and said roughening step including depositing particles formed from an inorganic material on said at least one surface and thereby forming a roughening layer having a thickness in the range of from about 10 μm to about 200 μm and a particle peak-to-peak interval of approximately 1 μm to about 100 μm so as to insure said capture of said diesel soot particles.
Claim 3
Dependent Claim
16 words
Method according to claim 1 further comprising applying a temperature treatment to decompose said deposited particles.
Claim 4
Dependent Claim
17 words
Method according to claim 1 wherein said roughening step comprises a CVD deposition of said inorganic materials.
Claim 5
Dependent Claim
19 words
Method according to claim 1 characterized in that said roughening step comprises depositing said particles from a supersaturated solution.
Claim 6
Dependent Claim
19 words
Method according to claim 4 characterized in that said roughening step further comprises depositing a hydroxide or a salt.
Claim 7
Dependent Claim
24 words
Method according to claim 4 characterized in that said depositing step comprises depositing aluminum hydroxide particles from a caustic soda solution supersaturated with aluminum.
Claim 8
Dependent Claim
76 words
Method according to claim 6 wherein said caustic soda solution contains from 100 g Na 2 O/liter solution to about 170 g Na 2 O/liter as NaOH and from about 100 g Al 2 O 3 /liter solution to about 230 g Al 2 O 3 /liter in the form of Al(OH) 3 in a molar ratio in the range of from 1.20 to 1.45 moles Na 2 O to moles Al 2 O 3 .
Claim 9
Dependent Claim
43 words
Method according to claim 6 further characterized by converting said aluminum hydroxide to aluminum oxide by calcining at a temperature from about 600° C. to about 1000° C. for a time in the range of from about 1 hour to about 5 hours.
Claim 10
Dependent Claim
26 words
Method according to claim 8 wherein said calcining step is performed at a temperature in the range of from about 700° C. to about 800° C.
Claim 11
Dependent Claim
16 words
Method according to claim 4 further comprising etching said ceramic foam prior to said depositing step.
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein said roughening step comprises roughening an exterior surface of said filter body.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-22 | 1994-04-23 | 1994-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-22 | 1998-04-23 | 1998-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-22 | 2002-04-23 | 2002-10-23 | $7700.00 | Window Closed / Lapsed |