Sol gel method for forming thin luminescent films
Assignee: Furukawa Electric North America Inc
•
Filing: 1987-10-01
•
Granted: 1990-10-23
•
Expires: 2007-10-01
Abstract
Abstract A sol-gel procedure is described for making display devices with luminescent films. The procedure typically involves hydrolysis and polymerization of an organometallic compound together with selected luminescent ions, and coating of a substrate and then heat treatment to form a polycrystalline layer. The procedure is particularly useful for making cathode ray tubes, expecially those for high power operation because of the excellent luminescence characteristics obtained, good thermal contact from the luminescent layer to faceplate and low cost of the procedure. Also described are the devices obtained which exhibit a layer of complex oxide with network structure much like the corresponding bulk compound.
Inventors
- 👤 Vincent J. Fratello
- 👤 Eliezer M. Rabinovich
- 👤 Joseph Shmulovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:18
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/20; H01J9/22; H01J9/227; C; C09; C09K; C09K11/00; C09K11/08; C09K11/0805; C09K11/0822; C09K11/77; C09K11/7766; C09K11/77742; C09K11/77747; C09K11/7783; C09K11/77922; C09K11/77927; H01J29/00; H01J29/02; H01J29/10; H01J29/18; H01J29/20; H01J2209/00; H01J2209/01; H01J2209/012
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
189 words
A method for fabricting a device, comprising the steps of: forming a complex oxide capable of luminescing when impinged by energy, said complex oxide including at least first and second cations, said first cation being selected from the group consisting of silicon and aluminum, and said second cation being selected from the group consisting of rare earth elements with atomic number 57-71 and yttrium; and completing the fabrication of said device, said completing step including the step of incorporating a substrate coated with said complex oxide into said device, characterized in that said forming step includes the steps of (a) dissolving in an aqueous solution salts comprising at least one second cation element, said salts being selected from the group consisting of nitrate, chloride, bromide, iodide, and sulfate, (b) mixing said salts solution with a metal alkoxide containing said first cation to promote hydrolysis of said alkoxide with formation of a sol capable of gellation to provide a sol. . . (c) applying a coating of said sol to a substrate and (d) heat treating the coated substrated in a temperature range of about 800° C. to 1500° C.
Claim 2
Independent Claim
189 words
A method for fabricting a device, comprising the steps of: forming a complex oxide capable of luminescing when impinged by energy, said complex oxide including at least first and second cations, said first cation being selected from the group consisting of silicon and aluminum, and said second cation being selected from the group consisting of rare earth elements with atomic number 57-71 and yttrium; and completing the fabrication of said device, said completing step including the step of incorporating a substrate coated with said complex oxide into said device, characterized in that said forming step includes the steps of (a) dissolving in an aqueous solution salts comprising at least one second cation element, said salts being selected from the group consisting of nitrate, chloride, bromide, iodide, and sulfate, (b) mixing said salts solution with a metal alkoxide containing said first cation to promote hydrolysis of said alkoxide with formation of a sol capable of gellation to provide a sol. . . (c) applying a coating of said sol to a substrate and (d) heat treating the coated substrated in a temperature range of about 800° C. to 1500° C.
Claim 3
Dependent Claim
13 words
The method of claim 1 in which the metal alkoxide is silicon alkoxide.
Claim 4
Dependent Claim
12 words
The method of claim 1 in which the metal alkoxide is tetraethylorthosilicate.
Claim 5
Dependent Claim
16 words
The method of claim 1 in which the said at least one second cation is yttrium.
Claim 6
Dependent Claim
31 words
The method of claim 1 in which at least one of said at least one second cations is selected from the group consisting of rare earth elements with atomic numbers 57-71.
Claim 7
Dependent Claim
53 words
The method of claim 1 in which the metal alkoxide is tetraethylorthosilicate, one of the said at least one second cation is yttrium and another one of said at least one second cations is selected from the group of rare earth elements with atomic number 57-71, the latter is added to provide luminescence.
Claim 8
Dependent Claim
18 words
The method of claim 6 in which said at least one another of said second cations is terbium.
Claim 9
Dependent Claim
85 words
The method of claim 7 in which the forming step includes a. dissolving the tetraethylorthosilicate in ethyl alchol to form a tetraethylorthosilicate solution; b. dissolving yttrium nitrate and terbium nitrate in acidified water to form a yttrium-terbium solution; c. mixing the tetraethylorthosilicate solution and yttrium-terbium solution together to form a coating solution; d. coating a substrate with the coating solution; and e. heat treating the coated substrate to form a luminescent complex oxide layer in the temperature range from about 800° C. to 1500° C.
Claim 10
Dependent Claim
20 words
The method of claim 8 in which the heat treatment comprises heating the coated substrate to at least 900° C.
Claim 11
Dependent Claim
16 words
The method of claim 9 in which the coated substrate is heated to approximately 1300° C.
Claim 12
Dependent Claim
14 words
The method of claim 1 in which the device comprises a cathode ray tube.
Claim 13
Independent Claim
175 words
A method for fabricating a device incorporating a complex oxide capable of liminescing when impinged by energy, which comprises the steps of forming complex oxide including at least a first and second cations, and completing the fabrication of the device by steps including incorporation of a substrate coated with the complex oxide into the device, wherein said forming step includes combining in an aqueous solution water-soluble salts comprising at least one second cation element and a metal alkoxide containing said first cation so as to promote hydrolysis of said alkoxide with formation of a sol capable of gellation, said first cation being selected from the group consisting of silicon and aluminum, said at least one second cation being selected from the group consisting of rare earth elements with atomic number 57-71 and yttrium, and said salt being selected from the group consisting of nitrate, chloride, bromide, iodide and sulfate applying a coating of said sol to a substrate and heat treating the coated substrate in the temperature range of about 800° C. to 1500° C.
Claim 14
Independent Claim
175 words
A method for fabricating a device incorporating a complex oxide capable of liminescing when impinged by energy, which comprises the steps of forming complex oxide including at least a first and second cations, and completing the fabrication of the device by steps including incorporation of a substrate coated with the complex oxide into the device, wherein said forming step includes combining in an aqueous solution water-soluble salts comprising at least one second cation element and a metal alkoxide containing said first cation so as to promote hydrolysis of said alkoxide with formation of a sol capable of gellation, said first cation being selected from the group consisting of silicon and aluminum, said at least one second cation being selected from the group consisting of rare earth elements with atomic number 57-71 and yttrium, and said salt being selected from the group consisting of nitrate, chloride, bromide, iodide and sulfate applying a coating of said sol to a substrate and heat treating the coated substrate in the temperature range of about 800° C. to 1500° C.
Claim 15
Dependent Claim
30 words
The method of claim 12, in which said metal alkoxide is tetraethylorthosilicate, the said at least one second cation is yttrium and at least one of said rare earth elements.
Claim 16
Dependent Claim
26 words
The method of claim 13 in which said second cation salts are yttrium nitrate and a water-soluble salt of said at least one rare earth element.
Claim 17
Dependent Claim
24 words
The method of claim 14 in which said at least one rare earth element is terbium and said water soluble salt is terbium nitrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-22 | 1994-04-23 | 1994-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-22 | 1998-04-23 | 1998-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-22 | 2002-04-23 | 2002-10-23 | $7700.00 | Window Closed / Lapsed |