US4963650A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for separating low molecular weight compounds from polycaproamide melt with superheated steam
Assignee: ALLUNIONS-WISSENSCHAFTS- und
•
Filing: 1989-10-06
•
Granted: 1990-10-16
•
Expires: 2009-10-06
Abstract
Abstract A process for separating low molecular weight compounds from a crude polycaproamide melt comprises heat treating the melt in vacuo with superheated steam, in an extruder having a plurality of degassing zones, under precise conditions of temperature, pressure and configuration, such that the occurrence of side reactions and dehydration of the melt are substantially eliminated, the molecular weight of the polymer during the heat treatment in vacuo, during transport and subsequent processing remains substantially unchanged, a residual content of low molecular weight compounds of ≦1.8% is achieved, and the operating flexibility of the process is increased.
Inventors
- 👤 Elvina Z. Bokareva
- 👤 Jelena V. Schinkorenko
- 👤 Viktor V. Terenko
- 👤 Larisa A. Nosova
- 👤 Garri I. Faidel
- 👤 Sijar N. Nurmuchomedov
- 👤 Anatolij V. Beljakov
- 👤 Ivan M. Vlasov
- 👤 Anton Fuerst
- 👤 Heinz Herrmann
- 👤 Eckart Pantzer
- 👤 Bernhard Stoehrer
- 👤 Eberhard Uhland
- 👤 Hans Werner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:31
CPC Classifications
C; C08; C08G; C08G69/00; C08G69/02; C08G69/08; C08G69/14; C08G69/16; C08G69/26; C08G69/28; C08G69/46
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
207 words
A process for separating low molecular weight compounds from a crude polycaproamide melt, comprising the step of heat treating a crude polycaproamide melt, containing low molecular weight monomers and oligomers of caproamide and by-products thereof, said heat treatment being effected in vacuo, in an extruder having a plurality of degassing zones, wherein superheated steam is introduced into the polymer melt upstream of each degassing zone in a total amount of 30-150%, relative to the amount of low molecular weight compounds, the low molecular weight compounds and the superheated steam are withdrawn in 2 or more zones, a residual pressure of 2-50 mbar is maintained in all but the final zone and a residual pressure of 5 to 350 mbar is maintained in the final zone, and the melt temperature is either held constant between 240°-280° C or is steadily reduced over the length of the extruder from 280° C to 240° C, whereby the occurrence of side reactions and dehydration of the melt are substantially eliminated, the molecular weight of the polymer during the heat treatment in vacuo, during transport and subsequent processing remains substantially unchanged, a residual content of low molecular weight compounds of ≦1.8% is achieved, and the operating flexibility of the process is increased.
Claim 2
Dependent Claim
207 words
A process for separating low molecular weight compounds from a crude polycaproamide melt, comprising the step of heat treating a crude polycaproamide melt, containing low molecular weight monomers and oligomers of caproamide and by-products thereof, said heat treatment being effected in vacuo, in an extruder having a plurality of degassing zones, wherein superheated steam is introduced into the polymer melt upstream of each degassing zone in a total amount of 30-150%, relative to the amount of low molecular weight compounds, the low molecular weight compounds and the superheated steam are withdrawn in 2 or more zones, a residual pressure of 2-50 mbar is maintained in all but the final zone and a residual pressure of 5 to 350 mbar is maintained in the final zone, and the melt temperature is either held constant between 240°-280° C or is steadily reduced over the length of the extruder from 280° C to 240° C, whereby the occurrence of side reactions and dehydration of the melt are substantially eliminated, the molecular weight of the polymer during the heat treatment in vacuo, during transport and subsequent processing remains substantially unchanged, a residual content of low molecular weight compounds of ≦1.8% is achieved, and the operating flexibility of the process is increased.
Claim 3
Dependent Claim
30 words
The process of claim 1, wherein the amount of superheated steam introduced upstream of each successive degassing zone is 100-150% of the amount of steam introduced into the preceding zone.
Claim 4
Dependent Claim
52 words
The process of claim 1, wherein after removal of the low molecular weight compounds from the polycaproamide melt up to a residual content of ≦1.8% in the final zone, 0.1-5%, relative to the polymer, of superheated steam is introduced without degassing or with subsequent degassing at a residual pressure of 5-350 mbar.
References Cited (Backward Citations)
US3361721A
Cited
US4891420A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |