US4963644A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for crystallization of polyethylene naphthalate
Assignee: M&G USA Corp
•
Filing: 1989-09-18
•
Granted: 1990-10-16
•
Expires: 2009-09-18
Abstract
Abstract High molecular weight polyester resins are sometimes produced from low molecular weight polyester prepolymers having the same composition by solid state polymerization. Polyester prepolymers are generally converted from the amorphous state to the crystalline state prior to solid state polymerization in order to raise their sticking temperature. This is done to keep the polyester prepolymer from sticking together as a solid mass in the solid state polymerization reactor. Such polyester prepolymers are traditionally crystallized by simply heating them to an elevated temperature at which crystallization occurs. However, polyethylene naphthalate prepolymer cannot be crystallized by utilizing this simply traditional approach. This inventions discloses a process for crystallizing amorphous polyethylene naphthalate prepolymer which comprises: (1) heating the amorphous polyethylene naphthalate prepolymer to a temperature which is within the range of about 80° C. to about 140° C. in the presence of a stream of an inert gas or under a vacuum to devolatilize the amorphous polyethylene naphthalate prepolymer; and (2) subsequently heating the devolatilized polyethylene naphthalate prepolymer to a temperature which is within the range of about 150° C. to about 260° C. while providing agitation to produce the crystallized polyethylene naphthalate prepolymer.
Inventors
- 👤 Ben Duh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:27
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/16; C08G63/18; C08G63/181; C08G63/88; C08G63/78; C08G63/80
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
97 words
A process for crystallizing amorphous polyethylene naphthalate prepolymer which comprises: (1) heating the amorphous polyethylene naphthalate prepolymer to a temperature which is within the range of about 80° C. to about 140° C. in the presence of a stream of an inert gas or under a vacuum for a period of time which is sufficient to devolatilize the amorphous polyethylene naphthalate prepolymer; and (2) subsequently heating the devolatilized polyethylene naphthalate prepolymer to a temperature which is within the range of about 150° C. to about 260° C. while providing agitation to produce the crystallized polyethylene naphthalate prepolymer.
Claim 2
Dependent Claim
97 words
A process for crystallizing amorphous polyethylene naphthalate prepolymer which comprises: (1) heating the amorphous polyethylene naphthalate prepolymer to a temperature which is within the range of about 80° C. to about 140° C. in the presence of a stream of an inert gas or under a vacuum for a period of time which is sufficient to devolatilize the amorphous polyethylene naphthalate prepolymer; and (2) subsequently heating the devolatilized polyethylene naphthalate prepolymer to a temperature which is within the range of about 150° C. to about 260° C. while providing agitation to produce the crystallized polyethylene naphthalate prepolymer.
Claim 3
Dependent Claim
120 words
A process for solid state polymerizing polyethylene naphthalate prepolymer into high molecular weight polyethylene naphthalate resin comprising: (1) devolatilizing the polyethylene naphthalate prepolymer at a temperature which is within the range of about 80° C. to about 140° C. in the presence of a stream of an inert gas or under a vacuum; (2) crystallizing the devolatilized polyethylene naphthalate prepolymer by heating it to a temperature which is within the range of about 150° C. to about 260° C. while providing agitation: and (3) subsequently heating the crystallized polyethylene naphthalate prepolymer to a temperature from about 50° C. to about 1° C. below its sticking temperature for a period of time sufficient to produce the high molecular polyethylene naphthalate resin.
Claim 4
Dependent Claim
120 words
A process for solid state polymerizing polyethylene naphthalate prepolymer into high molecular weight polyethylene naphthalate resin comprising: (1) devolatilizing the polyethylene naphthalate prepolymer at a temperature which is within the range of about 80° C. to about 140° C. in the presence of a stream of an inert gas or under a vacuum; (2) crystallizing the devolatilized polyethylene naphthalate prepolymer by heating it to a temperature which is within the range of about 150° C. to about 260° C. while providing agitation: and (3) subsequently heating the crystallized polyethylene naphthalate prepolymer to a temperature from about 50° C. to about 1° C. below its sticking temperature for a period of time sufficient to produce the high molecular polyethylene naphthalate resin.
Claim 5
Dependent Claim
26 words
A process as specified in claim 1 wherein said amorphous polyethylene naphthalate prepolymer is prepared by the melt polymerization of ethylene glycol and 2,6-naphthalene dicarboxylic acid.
Claim 6
Dependent Claim
25 words
A process as specified in claim 2 wherein the polyethylene naphthalate prepolymer is prepared by the melt polymerization of ethylene glycol and 2,6-naphthalene dicarboxylic acid.
Claim 7
Dependent Claim
18 words
A process as specified in claim 1 wherein the amorphous polyethylene naphthalate prepolymer is a polyethylene naphthalate homopolymer.
Claim 8
Dependent Claim
17 words
A process as specified in claim 2 wherein the polyethylene naphthalate prepolymer is a polyethylene naphthalate homopolymer.
Claim 9
Dependent Claim
52 words
A process as specified in claim 1 wherein the amorphous polyethylene naphthalate prepolymer is heated to a temperature within the range of about 115° C. to about 137° C. and wherein the devolatilized polyethylene naphthalate prepolymer is heated at a temperature within the range of about 180° C. to about 220° C.
Claim 10
Dependent Claim
50 words
A process as specified in claim 2 wherein the devolatilization is conducted at a temperature which is within the range of about 115° C. to about 137° C. and wherein the crystallization is conducted at a temperature which is within the range of about 180° C. to about 220° C.
Claim 11
Dependent Claim
54 words
A process as specified in claim 1 wherein the amorphous polyethylene naphthalate prepolymer is heated to a temperature which is within the range of about 120° C. to about 135° C. and wherein the crystallization step is conducted at a temperature which is within the range of about 190° C. to about 200° C.
Claim 12
Dependent Claim
51 words
A process as specified in claim 2 wherein the devolatilization is conducted at a temperature which is within the range of about 120° C. to about 135° C. and wherein the crystallization step is conducted at a temperature which is within the range of about 190° C. to about 200° C.
Claim 13
Dependent Claim
22 words
A process as specified in claim 1 wherein the amorphous polyethylene naphthalate prepolymer is heated in the presence of an inert gas.
Claim 14
Dependent Claim
13 words
A process as specified in claim 11 wherein the inert gas is air.
Claim 15
Dependent Claim
23 words
A process as specified in claim 1 wherein the devolatilization is conducted by heating the amorphous polyethylene naphthalate prepolymer in a fluidized bed.
Claim 16
Dependent Claim
55 words
A process as specified in claim 2 wherein the solid state polymerization is conducted in a cylindrical polymerization reactor; wherein the polyethylene naphthalate polymer moves from the top to the bottom of the reactor by reason of the force of gravity in a partially dammed state; and wherein nitrogen gas flows countercurrently through the reactor.
Claim 17
Dependent Claim
36 words
A process as specified in claim 8 wherein the crystallized polyethylene naphthalate prepolymer is solid state polymerized in step (3) at a temperature which is within the range of about 210° C. to about 265° C.
Claim 18
Dependent Claim
36 words
A process as specified in claim 8 wherein the crystallized polyethylene naphthalate prepolymer is solid state polymerized in step (3) at a temperature which is within the range of about 230° C. to about 265° C.
Claim 19
Dependent Claim
36 words
A process as specified in claim 8 wherein the crystallized polyethylene naphthalate prepolymer is solid state polymerized in step (3) at a temperature which is within the range of about 240° C. to about 260° C.
Claim 20
Dependent Claim
31 words
A process as specified in claim 1 wherein the time required in step (1) to devolatilize the amorphous polyethylene naphthalate prepolymer is within the range of 15 minutes to 10 hours.
Claim 21
Dependent Claim
33 words
A process as specified in claim 18 wherein the time required in step (2) to crystallize the devolatilized polyethylene naphthalate prepolymer is within the range of about 1 minute to about 4 hours.
References Cited (Backward Citations)
US4327205A
Cited
US4374975A
Cited
US4755587A
Cited
US4876326A
Cited
US4792573A
Cited
US4849497A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |