Method of making a thermal window glazing with conductive polymer coating to block radiative heating
Assignee: Zipperling Kessler GmbH and Co
•
Filing: 1989-05-04
•
Granted: 1990-10-16
•
Expires: 2009-05-04
Abstract
Abstract A method is provided for minimizing radiative heat transfer and maximizing the transmission of visible light through a window having at least one pane. The method comprises the step of applying a transparent conductive polymer layer to a face of the pane, the polymer layer being reflective and absorptive in an infrared region of the electromagnetic spectrum and being transparent in the visible region of the spectrum, and having a transparancy ratio greater than 2.
Inventors
- 👤 Lawrence W. Shacklette
- 👤 Kwan-Yue Jen
- 👤 Helmut Eckhardt
- 👤 Ronald L. Elsenbaumer
- 👤 Ray H. Baughman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 14:57
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/28; C03C17/32; C09; C09K; C09K2323/00; C09K2323/03; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31645; Y10T428/31649
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
87 words
A method for minimizing radiative heat transfer and maximizing the transmission of visible light through a window, having at least one pane, comprising the step of: applying a transparent conductive polymer layer to said pane, said polymer layer being reflective and absorptive in an infrared region of the electromagnetic spectrum having a wavelength range extending from 780 to 2500 nm, being transparent in a visible region of the spectrum having a wavelength range extruding from 400 to 780 nm, and having a transparenccy ratio greater than 2.
Claim 2
Independent Claim
87 words
A method for minimizing radiative heat transfer and maximizing the transmission of visible light through a window, having at least one pane, comprising the step of: applying a transparent conductive polymer layer to said pane, said polymer layer being reflective and absorptive in an infrared region of the electromagnetic spectrum having a wavelength range extending from 780 to 2500 nm, being transparent in a visible region of the spectrum having a wavelength range extruding from 400 to 780 nm, and having a transparenccy ratio greater than 2.
Claim 3
Dependent Claim
29 words
A method as recited in claim 1, further comprising the step of coating said conductive polymer layer on a flexible plastic substrate which is then associated with said pane.
Claim 4
Dependent Claim
19 words
A method as recited in claim 2, further comprising the step of adhesively securing said substrate to said pane.
Claim 5
Dependent Claim
30 words
A method as recited in claim 2, wherein said window has a frame and said method further comprises the step of spacing said substrate from a face of said pane.
Claim 6
Dependent Claim
52 words
A method as recited in claim 4, wherein said window has a frame housing a plurality of panes, and said method further comprises the step of securing said substrate to said frame to space said polymer layer from a face of at least one of said panes, thereby forming a thermal break.
Claim 7
Dependent Claim
54 words
A method as recited in claim 4, wherein said window has a frame housing a plurality of panes, and said method further comprises the step of securing said substrate to said frame to space said coated plastic substrate from interior opposing faces of two of said panes, thereby forming a plurality of thermal breaks.
Claim 8
Dependent Claim
18 words
A method as recited in claim 6, comprising the step of adjusting said panes to be substantially parallel.
Claim 9
Dependent Claim
21 words
A method as recited in claim 5 or 6 comprising the step of sealing said window panes to isolate said space.
Claim 10
Dependent Claim
30 words
A method as recited in claim 8, wherein said sealing step includes the step of injecting an inert gas into said space to enhance the characteristics of said thermal break.
Claim 11
Dependent Claim
26 words
A method as recited in claim 9, wherein said inert gas is selected from the group consisting of argon, nitrogen, dry air, neon and mixtures thereof.
Claim 12
Dependent Claim
20 words
A method as recited in claim 1, wherein said transparent conductive polymer layer comprises a p-type (anion inserted) conjugated polymer.
Claim 13
Dependent Claim
33 words
A method as recited in claim 2, in which said p-type conjugated polymer is selected from the group consisting of polypyrrole, poly(furylene vinylene), poly(carbazole), poly(thienylene vinylene), polyacetylene, polyaniline, polyisothianaphthene and substituted versions thereof.
Claim 14
Dependent Claim
34 words
A method as recited in claim 12, in which poly(thienylene vinylene) is substituted in the 3 and/or 4 position by at least one member selected from methyl, ethyl, propyl, butyl, hexyl or octyl substituents.
Claim 15
Dependent Claim
39 words
A method as recited in claim 12, in which said poly(thienylene vinylene) is substituted in the 3 and/or 4 position by at least one member selected from the group cosisting of methoxy, ethoxy, propoxy, butoxy, hexoxy, or octyloxy substituents.
Claim 16
Dependent Claim
14 words
A method as recited in claim 11, in which said anion is a sulfonate.
Claim 17
Dependent Claim
18 words
A method as recited in claim 2, wherein the flexible plastic substrate is a polyester, polycarbonate or polyacrylate.
Claim 18
Dependent Claim
37 words
A method as recited in claim 8, wherein said sealing step further comprises the step of injecting a dopant gas, liquid or vapor into said space to adjust and maintain a doping level for said conductive polymer.
Claim 19
Dependent Claim
18 words
A method as recited in claim 2, wherein said flexible plastic substrate is a heat shrinkable polymer film.
Claim 20
Dependent Claim
25 words
A method as recited in claim 8, wherein said sealing step includes the step of injecting a dopant or dopant coinserting agent into said space.
Claim 21
Dependent Claim
20 words
A method as recited in claim 19, wherein said dopant coinserting agent is acetonitrile, benzonitrile, water or an organic alcohol.
Claim 22
Dependent Claim
32 words
A method as recited in claim 19, wherein the optical transparency of the conductive polymer film is varied via controlled variation in the gas pressure of the dopant or dopant coinserting agent.
Claim 23
Dependent Claim
32 words
The method of claim 1, wherein the conductive polymer layer is obtained with preferential chain alignment in one direction within the plane of the pane, so as to provide a polarizing effect.
Claim 24
Dependent Claim
27 words
The method of claim 22, wherein the polarizing direction of the conducting polymer layer is verticle, so as to minimize glare from reflected and scattered solar radiation.
Claim 25
Dependent Claim
29 words
The method of claim 1, wherein at least two layers of conductive polymers are directly or indirectly applied to the panes, or to a free standing plastic substrate film.
Claim 26
Dependent Claim
28 words
The method of claim 24, wherein at least two of said conducting polymer layers are partially chain oriented so that the directions of preferential alignment are mutually orthogonal.
Claim 27
Dependent Claim
44 words
The method of claim 1, wherein at least two different conducting polymers are used to form at least two layers of conducting polymers and wherein the transmission characteristics of the window are adjusted by selection of the relative thicknesses of the different polymer layers.
Claim 28
Dependent Claim
46 words
The method of claim 1, wherein the absorption characteristics of the window are optimized by varying the relative amounts of different conducting polymer components, including either conducting polymers of the same type but different average conjugation length, or conducting polymers of different polymeric or dopant compositions.
Claim 29
Dependent Claim
35 words
The method of claim 1, wherein the conducting polymer layer is combined with a second absorptive window coating material, including a metal, metal-oxide, or insulating dye coating, to optimize the absorption characteristics of the window.
Claim 30
Dependent Claim
25 words
The method of claim 1, wherein the thickness of the conducting polymer layer decreases progressively from the top to the bottom of the window pane.
Claim 31
Dependent Claim
33 words
The method of claim 1, wherein an additional window coating is employed, comprising a liquid crystal layer which is electrically switchable from a state of greater opacity to a state of lower opacity.
Claim 32
Dependent Claim
21 words
The method of claim 30, wherein at least one electrical contact to the liquid crystal layer comprises the conductive polymer layer.
Claim 33
Dependent Claim
67 words
The method of claim 1, wherein said window is a vehicle window and said conducting polymer provides a transparency for radiation in said visible region of the spectrum and a transparency for radiation in a far-infrared region of the electromagnetic spectrum having a wavelength extending from 2500 to 100,000 nm, the transparency for radiation said near-infrared region being less than that for radiation in said far-infrared region.
References Cited (Backward Citations)
US4157417A
Cited
US4268126A
Cited
US4456335A
Cited
US4226910A
Cited
US4321114A
Cited
US4442187A
Cited
US4848875A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |