US4960640A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Composite refractory material
Assignee: 3M Co
•
Filing: 1988-02-19
•
Granted: 1990-10-02
•
Expires: 2008-02-19
Abstract
Abstract A fibrous substrate having a first coefficient of thermal expansion and having porous characteristics is formed from discrete elements, such as carbon fibers, having anisotropic properties. A matrix formed from a refractory material encases the discrete elements and has a second coefficient of thermal expansion different from the first coefficient. The matrix has minimal chemical or mechanical bonding to the discrete elements to provide for a displacement of the matrix relative to the substrate with mechanical shock or changes in temperature. The matrix includes a first element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and also includes a second element bound to the first element. The matrix is preferably formed by providing a mixture of a first gas containing the refractory element and a second gas containing the second element and by introducing the gases into a chamber containing the substrate. The gases are introduced into the chamber at an elevated temperature and with a pressure pulsating at a particular rate between first and second pressure limits to obtain the deposition of the refractory material on the discrete elements. The gases are periodically exhausted from the chamber and fresh gases are introduced into the chamber. The matrix may consist of first and second layers respectively having hafnium (e.g. hafnium carbide) and zirconium (e.g. zirconium carbide) as the refractory materials. These layers define pores with the substrate and further define an external surface. A layer of rhenium may cover the matrix in the pores and in the external surface.
Inventors
- 👤 Edward L. Paquette
- 👤 Marc G. Simpson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:46
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B41/45; C04B41/50; C04B41/51; C04B41/515; C23; C23C; C23C16/00; C23C16/06; C23C16/08; C23C16/14; C23C16/22; C23C16/30; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2918; Y10T428/292; Y10T428/2933; Y10T428/2938; Y10T428/294; Y10T428/2942; Y10T428/2944
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
105 words
In combination, a substrate formed from a plurality of discrete elements having a porous relationship, and a matrix disposed on the substrate with a minimal chemical and mechanical bonding to the substrate and having a different coefficient of thermal expansion than that of the substrate to provide for changes in position of the matrix relative to the substrate with changes in temperature and with the imposition of mechanical shocks on the substrate, the matrix being formed from an element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and from another element chemically bonded to the refractory element.
Claim 2
Dependent Claim
105 words
In combination, a substrate formed from a plurality of discrete elements having a porous relationship, and a matrix disposed on the substrate with a minimal chemical and mechanical bonding to the substrate and having a different coefficient of thermal expansion than that of the substrate to provide for changes in position of the matrix relative to the substrate with changes in temperature and with the imposition of mechanical shocks on the substrate, the matrix being formed from an element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and from another element chemically bonded to the refractory element.
Claim 3
Dependent Claim
45 words
In a combination as set forth in claim 1, the matrix being formed from a first layer disposed on the substrate and including hafnium as the refractory element and from a second layer disposed on the first layer and including zirconium as the refractory element.
Claim 4
Dependent Claim
33 words
In a combination as set forth in claim 2, the first layer having a thickness of less than one (1) micron and the second layer having a thickness greater than one (1) micron.
Claim 5
Dependent Claim
39 words
In a combination as set forth in claim 2, the substrate being formed from carbon fibers, the first layer of the matrix being formed from hafnium carbide, and the second layer of the matrix being formed from zirconium carbide.
Claim 6
Dependent Claim
17 words
In a combination as set forth in claim 4, a layer of rhenium disposed on the matrix.
Claim 7
Dependent Claim
117 words
In combination, a fibrous substrate having a first coefficient of thermal expansion and defining porous characteristics and formed from discrete elements having anisotropic properties, a matrix formed from a refractory material and having a second coefficient of thermal expansion different from the first coefficient of thermal expansion, the matrix accommodating the substrate, as a result of mechanical shocks and changes in temperature, to relieve stresses between the matrix and the substrate in accordance with the differences in their coefficients of thermal expansion, the refractory material including a first element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and further including a second element chemically bound to the first element.
Claim 8
Dependent Claim
117 words
In combination, a fibrous substrate having a first coefficient of thermal expansion and defining porous characteristics and formed from discrete elements having anisotropic properties, a matrix formed from a refractory material and having a second coefficient of thermal expansion different from the first coefficient of thermal expansion, the matrix accommodating the substrate, as a result of mechanical shocks and changes in temperature, to relieve stresses between the matrix and the substrate in accordance with the differences in their coefficients of thermal expansion, the refractory material including a first element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and further including a second element chemically bound to the first element.
Claim 9
Dependent Claim
23 words
In a combination as set forth in claim 6, a layer of rhenium disposed on the matrix to resist corrosion from hydrogen gases.
Claim 10
Dependent Claim
45 words
In a combination as set forth in claim 7, the matrix being formed from at least two (2) layers, one of the layers including hafnium as the refractory element in the layer and the other layer including zirconium as the refractory element in the layer.
Claim 11
Dependent Claim
48 words
In a combination as set forth in claim 8, the layer in the matrix including hafnium as the refractory element having a thickness less than one (1) micron and the layer of the matrix including zirconium as the refractory element having a thickness greater than one (1) micron.
Claim 12
Dependent Claim
18 words
In a combination as set forth in claim 6, the matrix encasing the discrete elements in the substrate.
Claim 13
Independent Claim
153 words
A method of forming a refractory composite material including the following steps: forming a porous substrate from a plurality of discrete elements having a coefficient of thermal expansion and having anisotropic properties, providing a mixture of a first gas containing a refractory element selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and a second gas containing an element having properties of reacting with the refractory element to form a refractory material having a second coefficient of thermal expansion different from the first coefficient of thermal expansion, disposing the porous substrate in a furnace, and introducing into the furnace the mixture at an elevated temperature and with a pressure pulsating at a particular rate between first and second limits of pressure to obtain a deposition of the refractory material on the discrete elements in the substrate with a minimal chemical or mechanical bonding to the discrete elements in the substrate.
Claim 14
Independent Claim
153 words
A method of forming a refractory composite material including the following steps: forming a porous substrate from a plurality of discrete elements having a coefficient of thermal expansion and having anisotropic properties, providing a mixture of a first gas containing a refractory element selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and a second gas containing an element having properties of reacting with the refractory element to form a refractory material having a second coefficient of thermal expansion different from the first coefficient of thermal expansion, disposing the porous substrate in a furnace, and introducing into the furnace the mixture at an elevated temperature and with a pressure pulsating at a particular rate between first and second limits of pressure to obtain a deposition of the refractory material on the discrete elements in the substrate with a minimal chemical or mechanical bonding to the discrete elements in the substrate.
Claim 15
Dependent Claim
55 words
A method as set forth in claim 11 wherein a first layer of hafnium chloride is formed on the substrate by the pulsations in pressure on a mixture of gases and a second layer of zirconium chloride is formed on the layer of hafnium chloride by the pulsations in pressure on a mixture of gases.
Claim 16
Dependent Claim
31 words
A method as set forth in claim 12 wherein a layer of rhenium is formed on the layer of zirconium chloride by the pulsations in pressure on a mixture of gases.
Claim 17
Dependent Claim
25 words
A method as set forth in claim 12 wherein the refractory material is deposited on the substrate to encase the discrete elements in the substrate.
Claim 18
Dependent Claim
27 words
A method as set forth in claim 12 wherein the refractory material is deposited on the substrate to cover the interstices between adjacent fibers in the substrate.
Claim 19
Independent Claim
151 words
A method of forming a refractory composite material, including the following steps: forming a porous substrate from a plurality of discrete elements having a first coefficient of thermal expansion and having anisotropic properties, providing a mixture of a first gas containing a refractory element selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and a second gas containing an element having properties of reacting with the refractory element to form a refractory material having a second coefficient of thermal expansion different from the first coefficient of thermal expansion, disposing the porous substrate in a furnace, and introducing into the furnace the mixture at an elevated temperature and with a pressure pulsating at a particular rate between first and second limits of pressure to obtain a deposition of the refractory material on the discrete elements in the substrate with a minimal chemical or mechanical bonding to the discrete elements.
Claim 20
Independent Claim
151 words
A method of forming a refractory composite material, including the following steps: forming a porous substrate from a plurality of discrete elements having a first coefficient of thermal expansion and having anisotropic properties, providing a mixture of a first gas containing a refractory element selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and a second gas containing an element having properties of reacting with the refractory element to form a refractory material having a second coefficient of thermal expansion different from the first coefficient of thermal expansion, disposing the porous substrate in a furnace, and introducing into the furnace the mixture at an elevated temperature and with a pressure pulsating at a particular rate between first and second limits of pressure to obtain a deposition of the refractory material on the discrete elements in the substrate with a minimal chemical or mechanical bonding to the discrete elements.
Claim 21
Dependent Claim
88 words
A method as set forth in claim 16, including: initially introducing into the furnace the mixture with hafnium as the refractory element and with the pulsating pressure to obtain a deposition of the refractory material on the discrete elements in the substrate with a minimal chemical and mechanical bonding to the discrete elements in the substrate, and subsequently introducing into the chamber the mixture with zirconium as the refractory element and with the pulsating pressure to obtain a deposition of the refractory material on the hafnium refractory material.
Claim 22
Dependent Claim
52 words
A method as set forth in claim 16 wherein the hafnium refractory material is deposited on the discrete elements of the substrate with a thickness of less than one (1) micron and wherein the zirconium refractory material is deposited on the hafnium refractory material with a thickness greater than one (1) micron.
Claim 23
Dependent Claim
19 words
A method as set forth in claim 15 wherein rhenium is deposited in the chamber on the refractory material.
Claim 24
Dependent Claim
36 words
A method as set forth in claim 16 wherein the discrete elements in the substrate include carbon fibers and wherein the hafnium refractory material constitutes hafnium carbide and wherein the zirconium refractory material constitutes zirconium carbide.
Claim 25
Dependent Claim
48 words
A method as set forth in claim 17 wherein the discrete elements in the substrate include carbon fibers and wherein the hafnium refractory material constitutes hafnium carbide and wherein the zirconium refractory material constitutes zirconium carbide and wherein rhenium is deposited in the furnace on the zirconium carbide.
Claim 26
Dependent Claim
146 words
In combination, a fibrous substrate having a first coefficient of thermal expansion and having porous characteristics and formed from discrete elements having anisotropic properties, a matrix formed from a refractory material encasing the discrete elements and having a second coefficient of thermal expansion different from the first coefficient of thermal expansion and having a minimal chemical and mechanical bonding to the discrete elements to provide for a displacement of the matrix relative to the substrate with mechanical shock or changes in temperature, the refractory material including a first element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and further including a second element chemically bound to the first element, the matrix defining pores with the substrate and further defining an external surface, and a layer of rhenium covering the matrix in the pores and on the external surface.
Claim 27
Dependent Claim
146 words
In combination, a fibrous substrate having a first coefficient of thermal expansion and having porous characteristics and formed from discrete elements having anisotropic properties, a matrix formed from a refractory material encasing the discrete elements and having a second coefficient of thermal expansion different from the first coefficient of thermal expansion and having a minimal chemical and mechanical bonding to the discrete elements to provide for a displacement of the matrix relative to the substrate with mechanical shock or changes in temperature, the refractory material including a first element having refractory properties and selected from the group consisting of hafnium, zirconium, tantalum, tungsten and molybdenum and further including a second element chemically bound to the first element, the matrix defining pores with the substrate and further defining an external surface, and a layer of rhenium covering the matrix in the pores and on the external surface.
Claim 28
Dependent Claim
23 words
A combination as set forth in claim 22, the refractory material being selected from the group consisting of hafnium carbide and zirconium carbide.
Claim 29
Dependent Claim
26 words
In a combination as set forth in claim 22, the matrix being formed from a layer of hafnium carbide and then a layer of zirconium carbide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-01 | 1994-04-02 | 1994-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-01 | 1998-04-02 | 1998-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-01 | 2002-04-02 | 2002-10-02 | $7700.00 | Window Closed / Lapsed |