US4958770A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for making uniform porosity flexible irrigation pipe
Assignee: Plastic Specialties and Technologies Inc
•
Filing: 1989-05-03
•
Granted: 1990-09-25
•
Expires: 2009-05-03
Abstract
Abstract This invention relates to the manufacture of flexible porous irrigation pipe having an essentially uniform porosity throughout its length which is produced by extruding an essentially moisture-free non-homogeneous, mixture of pre-vulcanized elastomeric particles such as reclaimed crumb rubber from vehicle tire treads in major amount and a thermoplastic polymer binder such as low-density polyethylene in minor amount. The mixture is intimately mixed and extruded from an unvented extruder through an annular extruder die at a precisely-controlled temperature and then through a lengthy cooling liquid bath, the rate of pull-off through the extruder die and liquid bath being maintained constant. The leak rate of the fluid delivered from the porous pipe is substantially uniform over a lengthy prescribed dimension exhibiting a delivery variation of less than about 5 percent per unit of length.
Inventors
- 👤 William S. Mitchell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 00:49
CPC Classifications
B; B29; B29D; B29D23/00; B29D23/001; A; A01; A01G; A01G25/00; A01G25/06; B29B; B29B17/00; B29B17/0026; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/507; B29C48/00; B29C48/001; B29C48/0012; B29C48/03; B29C48/09; B29C48/10; B29C48/25; B29C48/285; B29C48/29; B29K; B29K2021/00; B29K2023/00; B29K2023/04; B29K2023/06; B29K2105/00; B29K2105/04; B29K2105/26; B29K2995/00; B29K2995/0037; B29K2995/0068; B29L; B29L2023/00; B29L2023/005; B29L2023/22; B29L2030/00; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
149 words
The process for forming lengthy flexible porous irrigation pipe having a porosity which is essentially uniform throughout its length comprising the steps of extruding from an unvented extruder through an annular extruder die an intimate mixture of (a) pre-vulcanized elastomeric particles consisting of ground crumb rubber from vehicle tire treads in major amount and (b) low-density polyethylene particles in granular form as a binder in minor amount, both said elastomeric particles and polyethylene particles being essentially moisture-free, forming a continuous length of extruded pipe from said moisture-free intimate mixture, passing the newly-formed extruded pipe through a lengthy water bath to slowly cool the pipe into final form, and controlling the rate of delivery of said newly-formed pipe from said extruder die and through said water bath at essentially the same rate, said pipe exhibiting a porosity of less than about 5 percent variation in fluid delivery throughout its length.
Claim 2
Dependent Claim
149 words
The process for forming lengthy flexible porous irrigation pipe having a porosity which is essentially uniform throughout its length comprising the steps of extruding from an unvented extruder through an annular extruder die an intimate mixture of (a) pre-vulcanized elastomeric particles consisting of ground crumb rubber from vehicle tire treads in major amount and (b) low-density polyethylene particles in granular form as a binder in minor amount, both said elastomeric particles and polyethylene particles being essentially moisture-free, forming a continuous length of extruded pipe from said moisture-free intimate mixture, passing the newly-formed extruded pipe through a lengthy water bath to slowly cool the pipe into final form, and controlling the rate of delivery of said newly-formed pipe from said extruder die and through said water bath at essentially the same rate, said pipe exhibiting a porosity of less than about 5 percent variation in fluid delivery throughout its length.
Claim 3
Dependent Claim
30 words
The process in accordance with claim 1 including the step of extruding the said mixture from said annular extruder die at a temperature ranging from about 270° to 290° F.
Claim 4
Dependent Claim
31 words
The process in accordance with claim 1 wherein the said mixture of elastomeric particles and low-density polyethylene particles have a moisture content of less than about 0.15 percent by weight water.
Claim 5
Dependent Claim
46 words
The process in accordance with claim 1 wherein the said mixture comprises from about 64 to 68 percent by weight elastomeric particles and from about 32 to 36 percent by weight low-density polyethylene particles, both being intimately mixed and heated within said extruder prior to extrusion.
Claim 6
Dependent Claim
32 words
The process in accordance with claim 1 wherein the said pre-vulcanized elastomeric particles are ground to a fineness of about 40 mesh and are dried prior to their introduction into said extruder.
Claim 7
Dependent Claim
33 words
The process in accordance with claim 1 wherein the said low-density polyethylene particles in granular form have a fineness of about 40 mexh and are dried prior to their introduction into said extruder.
Claim 8
Dependent Claim
38 words
The process in accordance with claim 1 wherein the said newly-formed pipe is pulled in tension from said extruder die and through said water bath at substantially a constant rate by a tension puller to control pipe porosity.
Claim 9
Dependent Claim
33 words
The process in accordance with claim 1 wherein the said porous pipe is formed having an internal diameter ranging from about 0.375 to 1.0 inch with a wall thickness of about 0.11 inch.
Claim 10
Dependent Claim
30 words
The process in accordance with claim 1 wherein the said water bath has a length of not less than about 70 feet and a constant flow of cooling water therethrough.
Claim 11
Dependent Claim
25 words
The process in accordance with claim 1 wherein the temperature of the extruder die is maintained substantially constant as the length of pipe is extruded.
Claim 12
Dependent Claim
31 words
The process in accordance with claim 1 wherein the speed of pull-off of pipe from the extruder die and through said water bath is maintained precisely constant to obtain uniform porosity.
Claim 13
Dependent Claim
50 words
As an article of manufacture, the lengthy flexible porous irrigation pipe having a porosity of less than about 5 percent fluid delivery variation throughout its length made in accordance with the process of claim 1, said pipe being formed from an essentially moisture-free mixture of elastomeric particles and polyethylene particles.
Claim 14
Dependent Claim
59 words
As a product-by-process made in accordance with the process of claim 1, a lengthy flexible porous irrigation pipe having an internal diameter ranging from about 0.753 to 1.0 inch and a porosity of less than about 5 percent fluid delivery variation throughout its length said pipe being formed from an essentially moisture-free mixture of elastomeric particles and polyethylene particles.
Claim 15
Dependent Claim
70 words
As a product-by-process made in accordance with the process of claim 1, a lengthy flexible porous irrigation pipe comprised of a moisture-free nonhomogeneous mixture of from about 64 to 68 percent by weight elastomeric particles and from about 32 to 36 percent by weight low-density polyethylene particles and having essentially uniform porosity, said pipe having a porosity of less than about 5 percent variation in fluid delivery throughout its length.
References Cited (Backward Citations)
US2612655A
Cited
US2666947A
Cited
US3060512A
Cited
US3717695A
Cited
US4110420A
Cited
US4117073A
Cited
US4143105A
Cited
US4209476A
Cited
US4577998A
Cited
US4616055A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-24 | 1994-03-26 | 1994-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-24 | 1998-03-26 | 1998-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-24 | 2002-03-26 | 2002-09-25 | $7700.00 | Window Closed / Lapsed |