US4957601A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming an array of apertures in an aluminum foil
Assignee: Spheral Solar Power Inc
•
Filing: 1989-05-08
•
Granted: 1990-09-18
•
Expires: 2009-05-08
Abstract
Abstract The disclosures relates to a method of forming an array of small apertures in an aluminum foil for receiving semiconductor spheres in said aperature. The apertures are formed by embossing the foil at the locations of the apertures to provide worked metal regions of reduced thickness at said locations. The foil is then etched in toto, etching taking place more rapidly at the worked metal region. Also, due to the reduced thickness of the foil at the embossed regions, such regions are etched away to provide apertures before the remainder of the foil undergoes material metal loss to provide the desired aperture array.
Inventors
- 👤 Jules D. Levine
- 👤 Millard J. Jensen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:43
CPC Classifications
H; H10; H10F; H10F19/00; C; C23; C23F; C23F1/00; C23F1/02; H02; H02S; H02S40/00; H02S40/30; H02S40/36; H10F71/00; H10F71/137; H10F77/00; H10F77/10; H10F77/14; H10F77/147; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
97 words
A method of forming an array of apertures through an aluminum foil for use in fabrication of solar cells, comprising the steps of: (a) providing a flexible aluminum foil having a thin oxide on the surface thereof, (b) embossing said foil at predetermined spaced unconnected locations to provide regions of reduced thickness in said foil at the locations of said embossments, and (c) etching without protective coating said aluminum foil along an entire unmasked surface of said foil to remove said regions of reduced thickness to provide apertures through said foil at said regions of reduced thickness.
Claim 2
Independent Claim
97 words
A method of forming an array of apertures through an aluminum foil for use in fabrication of solar cells, comprising the steps of: (a) providing a flexible aluminum foil having a thin oxide on the surface thereof, (b) embossing said foil at predetermined spaced unconnected locations to provide regions of reduced thickness in said foil at the locations of said embossments, and (c) etching without protective coating said aluminum foil along an entire unmasked surface of said foil to remove said regions of reduced thickness to provide apertures through said foil at said regions of reduced thickness.
Claim 3
Dependent Claim
16 words
A method as set forth in claim 1 wherein said foil has a native oxide thereon.
Claim 4
Dependent Claim
20 words
A method as set forth in claim 1 wherein said embossed locations are in the form of a periodic arrangement.
Claim 5
Dependent Claim
20 words
A method as set forth in claim 2 wherein said embossed locations are in the form of a periodic arrangement.
Claim 6
Dependent Claim
40 words
The method of claim 1 further including the step of inserting a member having a dimension greater than the diameter of a said aperture into said aperture to cause said member to penetrate said oxide and contact the aluminum thereunder.
Claim 7
Dependent Claim
12 words
The method of claim 5 wherein said member is a silicon sphere.
Claim 8
Independent Claim
70 words
A method of forming an array of apertures through an aluminum foil for use in fabrication of solar cells, comprising the steps of: (a) providing a flexible aluminum foil of about 2 mil thickness having a thin oxide on the surface thereof, (b) mechanically reducing the thickness of said foil at predetermined spaced discrete locations thereon, and (c) etching said foil without masking to create apertures through said discrete locations.
Claim 9
Independent Claim
70 words
A method of forming an array of apertures through an aluminum foil for use in fabrication of solar cells, comprising the steps of: (a) providing a flexible aluminum foil of about 2 mil thickness having a thin oxide on the surface thereof, (b) mechanically reducing the thickness of said foil at predetermined spaced discrete locations thereon, and (c) etching said foil without masking to create apertures through said discrete locations.
Claim 10
Dependent Claim
16 words
A method as set forth in claim 7 wherein said foil has a native oxide thereon.
Claim 11
Dependent Claim
20 words
A method as set forth in claim 7 wherein said discrete locations are in the form of a periodic arrangement.
Claim 12
Dependent Claim
20 words
A method as set forth in claim 8 wherein said discrete locations are in the form of a periodic arrangement.
Claim 13
Dependent Claim
26 words
A method as set forth in claim 7 further including the step of removing organic contaminants from the surface of said foil prior to step (c).
Claim 14
Dependent Claim
26 words
A method as set forth in claim 8 further including the step of removing organic contaminants from the surface of said foil prior to step (c).
Claim 15
Dependent Claim
40 words
The method of claim 7 further including the step of inserting a member having a dimension greater than the diameter of a said aperture into said aperture to cause said member to penetrate said oxide and contact the aluminum thereunder.
Claim 16
Dependent Claim
12 words
The method of claim 13 wherein said member is a silicon sphere.
References Cited (Backward Citations)
US2554256A
Cited
US3035990A
Cited
US3505180A
Cited
US3773576A
Cited
US3923566A
Cited
US3813310A
Cited
JPS5122902A
Cited
JPS5638473A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-17 | 1994-03-19 | 1994-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-17 | 1998-03-19 | 1998-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-17 | 2002-03-19 | 2002-09-18 | $7700.00 | Window Closed / Lapsed |