Manufacture of a quartz glass vessel for the growth of single crystal semiconductor
Assignee: Shin Etsu Quartz Products Co Ltd
•
Filing: 1989-07-06
•
Granted: 1990-09-11
•
Expires: 2009-07-06
Abstract
Abstract A quartz glass crucible adapted for use in a process for pulling a single crystal semiconductor material having an opaque outer substrate of a quartz glass with a relatively high bubble content and an inner transparent glass layer which is substantially free from bubbles. The crucible is produced while the substrate is supported by a rotating mould by forming an atmosphere of high temperature gas and supplying a metered quantity of powders of quartz to the high temperature gas atmosphere to have the quartz powders molten at least partly and directed toward an inner surface of the substrate to be adhered thereon.
Inventors
- 👤 Akira Uchikawa
- 👤 Atsushi Iwasaki
- 👤 Toshio Fukuoka
- 👤 Mitsuo Matsumura
- 👤 Hiroshi Matsui
- 👤 Yasuhiko Sato
- 👤 Masaaki Aoyama
- 👤 Eiichi Shinomiya
- 👤 Akira Fujinoki
- 👤 Nobuyoshi Ogino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:24
CPC Classifications
C; C30; C30B; C30B35/00; C03; C03B; C03B19/00; C03B19/09; C03B19/095; C30B15/00; C30B15/10; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57; Y10; Y10S; Y10S117/00; Y10S117/90; Y10T; Y10T117/00; Y10T117/10; Y10T117/1024; Y10T117/1032; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1317; Y10T428/24; Y10T428/24942; Y10T428/249921; Y10T428/249953; Y10T428/249967; Y10T428/249969; Y10T428/249978; Y10T428/24998; Y10T428/249987; Y10T428/249988; Y10T428/24999; Y10T428/26; Y10T428/263; Y10T428/31; Y10T428/315
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
91 words
A quartz crucible including an opaque quartz glass outer layer containing bubbles of 20 to 250 μm in diameter in a density not smaller than 20,000 per cm 2 , and a transparent quartz glass inner layer of 0.3 mm to 3.0 mm in thickness which is integrally formed with said opaque layer and having a smooth inner surface, said transparent layer having no bubbles with a diameter greater than 50 μm, and having less than 10 each per cm 2 of bubbles with a diameter between 20 and 50 μm.
Claim 2
Dependent Claim
91 words
A quartz crucible including an opaque quartz glass outer layer containing bubbles of 20 to 250 μm in diameter in a density not smaller than 20,000 per cm 2 , and a transparent quartz glass inner layer of 0.3 mm to 3.0 mm in thickness which is integrally formed with said opaque layer and having a smooth inner surface, said transparent layer having no bubbles with a diameter greater than 50 μm, and having less than 10 each per cm 2 of bubbles with a diameter between 20 and 50 μm.
Claim 3
Dependent Claim
17 words
A quartz crucible in accordance with claim 1 in which said opaque glass layer contains crystalline components.
Claim 4
Dependent Claim
26 words
A quartz crucible in accordance with claim 2 in which said crystalline components are contained in the vicinity of outer surface of the opaque glass layer.
Claim 5
Dependent Claim
37 words
A quartz crucible in accordance with claim 1 in which said opaque glass layer has bubbles distributed in an area of 60% thickness from external surface with a concentration of 40,000 to 70,000 per cm 2 .
References Cited (Backward Citations)
US3776809A
Cited
US3927697A
Cited
US3609829A
Cited
US3772134A
Cited
US3925583A
Cited
US4528163A
Cited
US4416680A
Cited
US4437727A
Cited
US4676814A
Cited
US4632686A
Cited
US4713104A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-10 | 1994-03-12 | 1994-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-10 | 1998-03-12 | 1998-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-10 | 2002-03-12 | 2002-09-11 | $7700.00 | Window Closed / Lapsed |