US4956030A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of fabricating simulated stone surfaces and improved simulated stone products
Assignee: Academy of Applied Science Inc
•
Filing: 1989-10-05
•
Granted: 1990-09-11
•
Expires: 2009-10-05
Abstract
Abstract A method of fabricating stone-simulated articles including facings for substrates, involving roller-flattening mixtures of preferably polyester resins, curing agent, polyester-dispersed pigments, fumed silica (and other) filler and aluminum trihydrate filler into flat stone-pattern-simulating surfaces or slabs, maintaining the same sufficiently cool (as by refrigeration) to prevent curing until it is desired to use the same, and then applying to, and rolling over a substrate to be covered or faced, or otherwise forming the same into the desired article, and permitting to cure under the action of said curing agent, with the resulting product containing the stone-simulated pattern throughout.
Inventors
- 👤 David Baskin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:24
CPC Classifications
B; B29; B29C; B29C43/00; B29C43/02; B29C43/021; B29C33/00; B29C33/0011; B29C33/0016; B29C70/00; B29C70/68; B29C70/78; B44; B44F; B44F9/00; B44F9/04; Y; Y10; Y10S; Y10S52/00; Y10S52/07; Y10T; Y10T156/00; Y10T156/11; Y10T156/1153; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24446
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
127 words
A method of fabricating an artificial stone-like facing as for attachment to a substrate, that comprises, preparing a mixture of a wet, soft and uncured synthetic resin binder, color pigment and filler particles and curing agent for the resin, for ultimate attachment to a permanent substrate; applying the mixture to a temporary substrate, presenting a wet surface of irregular and uneven particles; successively and continuously pressing together by rolling pressure successive adjacent portions of the irregular and uneven surface of the wet, soft and uncured resin mixture against the temporary substrate into a flat surface and maintaining the mixture in a cooled condition, as by refrigeration, to inhibit curing and keeping the same soft and uncured until removed from such cooling for application to a permanent substrate.
Claim 2
Independent Claim
127 words
A method of fabricating an artificial stone-like facing as for attachment to a substrate, that comprises, preparing a mixture of a wet, soft and uncured synthetic resin binder, color pigment and filler particles and curing agent for the resin, for ultimate attachment to a permanent substrate; applying the mixture to a temporary substrate, presenting a wet surface of irregular and uneven particles; successively and continuously pressing together by rolling pressure successive adjacent portions of the irregular and uneven surface of the wet, soft and uncured resin mixture against the temporary substrate into a flat surface and maintaining the mixture in a cooled condition, as by refrigeration, to inhibit curing and keeping the same soft and uncured until removed from such cooling for application to a permanent substrate.
Claim 3
Dependent Claim
40 words
A method as claimed in claim 1 and in which, upon removal from said cooling, the mixture is applied to the said permanent substrate, is rolled there against and thereafter permitted to cure by the action of said curing agent.
Claim 4
Dependent Claim
31 words
A method as claimed in claim 2 and in which said temporary substrate is separated from the mixture before curing and either before or after application to the said permanent substrate.
Claim 5
Dependent Claim
125 words
A method as claimed in claim 1 and in which the uncured synthetic resin binder is selected from the group consisting of polymerizable unsaturated polyester resins, with and without styrene monomers, epoxy resins, and urethane resins; said filler particles are selected from the group consisting of silica, powdered talc, powdered quartz, diatomaceous earth, gypsum, powdered glass, clay minerals, illite, powdered chalk, powdered marble, powdered limestone, aluminum silicate, aluminum stearate, calcium silicate, boracite, borax and alumina trihydrate; said color pigments are selected from the group consisting of inert inorganic powders and pastes, and polyester-dispersed pigments; and said curing agent is selected from the group consisting of polymerization catalysts including free radical catalysts based on peroxide-type compounds, methyl ethyl ketone peroxide, benezoyl peroxide and tertiary butyl hydroperoxide.
Claim 6
Dependent Claim
48 words
An artificial stone-like facing preparation for storing in uncured condition under refrigeration that comprises a mixture of a wet, soft and uncured synthetic resin binder, color pigment and filler particles and curing agent for the resin, all pressure-crushed into flat form against a temporary substrate prior to refrigeration.
Claim 7
Dependent Claim
48 words
An artificial stone-like facing preparation for storing in uncured condition under refrigeration that comprises a mixture of a wet, soft and uncured synthetic resin binder, color pigment and filler particles and curing agent for the resin, all pressure-crushed into flat form against a temporary substrate prior to refrigeration.
Claim 8
Dependent Claim
22 words
An artificial stone-like facing preparation as claimed in claim 5 comprising a mixture of polyester resin, polyester-dispersed pigment and aluminum trihydrate filler.
Claim 9
Dependent Claim
80 words
An artificial stone-like facing preparation as claimed in claim 5 and in which the uncured wet and soft synthetic resin is selected from the group consisting of polymerizable unsaturated polyester resins, with and without styrene monomers, epoxy resins and urethane resins; said color pigments being selected from the group consisting of inert inorganic powders and pastes and polyester-dispersed pigments; and said filler particles being selected from the group consisting of powdered silica, silicates, quartz earths and clays and aluminum trihydrate.
Claim 10
Independent Claim
134 words
A method of fabricating an artificial stone-like article, that comprises, preparing a mixture of agglomorated particles of wet, soft and uncured synthetic resin binder, color pigment and filler particles and curing agent for the resin; applying the mixture to a temporary substrate, presenting a wet surface of irregular and uneven particles; successively and continuously pressing together by rolling pressure successive adjacent portions of the irregular and uneven surface of the wet, soft and uncured agglomorated particulate, resin mixture against the temporary substrate into a flat surface with a resulting stone-simulated pattern throughout the same; and removing the wet, soft and uncured pressure-rolled flat stone-simulated material from the temporary substrate; forming the same into the desired shape for the article and permitting the curing in such shape under the action of the said curing agent.
Claim 11
Independent Claim
134 words
A method of fabricating an artificial stone-like article, that comprises, preparing a mixture of agglomorated particles of wet, soft and uncured synthetic resin binder, color pigment and filler particles and curing agent for the resin; applying the mixture to a temporary substrate, presenting a wet surface of irregular and uneven particles; successively and continuously pressing together by rolling pressure successive adjacent portions of the irregular and uneven surface of the wet, soft and uncured agglomorated particulate, resin mixture against the temporary substrate into a flat surface with a resulting stone-simulated pattern throughout the same; and removing the wet, soft and uncured pressure-rolled flat stone-simulated material from the temporary substrate; forming the same into the desired shape for the article and permitting the curing in such shape under the action of the said curing agent.
Claim 12
Dependent Claim
23 words
A method as claimed in claim 8 and in which the said flat mixture is cooled to maintain it uncured before said forming.
Claim 13
Dependent Claim
11 words
An artificial stone-like article fabricated by the method of claim 8.
Claim 14
Dependent Claim
46 words
An artificial stone-like article comprising a mixture of polyester resin, curing agent, polyester-dispersed pigment, preferably fumed silica filler and aluminum trihydrate filler, all pressure-rolled into a flat stone-pattern-simulated surface and then formed into the artificial stone-like article and cured in such form by said curing agent.
Claim 15
Dependent Claim
46 words
An artificial stone-like article comprising a mixture of polyester resin, curing agent, polyester-dispersed pigment, preferably fumed silica filler and aluminum trihydrate filler, all pressure-rolled into a flat stone-pattern-simulated surface and then formed into the artificial stone-like article and cured in such form by said curing agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-10 | 1994-03-12 | 1994-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-10 | 1998-03-12 | 1998-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-10 | 2002-03-12 | 2002-09-11 | $7700.00 | Window Closed / Lapsed |