Dimethylacrylamide-copolymer hydrogels with high oxygen permeability
Assignee: Novartis Corp
•
Filing: 1989-05-23
•
Granted: 1990-09-04
•
Expires: 2009-05-23
Abstract
Abstract This invention describes polymers which are obtained by copolymerization of 15-85 wt % N,N-dimethylacrylamide with about 15-85% of a fluorinated monomer such as perfluoroalkyl-alkylene acrylate or methacrylate with from 3 to 25 fluorine atoms and optionally, 0-50 wt % other acrylates or methacrylates and 0-20 wt %, but not more than 5 mol % of a polyvinyl functional crosslinking agent. These polymers are machinable in the dry state and form clear hydrogels with about 25-75 wt % water content and which possess oxygen-permeabilities 3-7 times higher than conventional hydrogels of similar water content. In the absence of crosslinking, the novel polymers are plasticized by water, forming clear hydroplastics with 30-70 wt % water content. The crosslinked polymers are especially useful for fabricating contact lenses for extended wear by either cutting and polishing a xerogel button, or by spin casting or direct molding in bulk or in solution.
Inventors
- 👤 Karl F. Mueller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 00:35
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/52; C08F220/54; A; A61; A61L; A61L26/00; A61L26/0009; A61L26/0014; A61L26/0061; A61L26/008; A61L27/00; A61L27/14; A61L27/16; A61L27/50; A61L27/52; C08F220/10; C08F220/22; G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/043
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
182 words
A copolymer, having the characteristics of high clarity, high hydrophilicity, and high oxygen permeability and which is, in the water swollen hydrated state, soft and flexible, which copolymer comprises the polymerization product of, with weight percent based on the total weight of monomers (a), (b), (c) and (d), of (a) 24.9 to 70 percent by weight of N,N-dimethylacrylamide, (b) 65 to 19.9 percent by weight of a vinyl monomer selected from the group consisting of the acrylate or methacrylate esters of formula B1 ##STR5## wherein R 1 is hydrogen or methyl, n is an integer from 1-4, m is an integer from 0-11, X is hydrogen or fluorine, with the proviso that, when m is 0, X is fluorine; and hexafluoroisopropyl methacrylate, (c) 10 to 40 percent by weight of a C 2 -C 4 -hydroxyalkyl acrylate or methacrylate, a C 2 -C 4 -alkoxy-alkyl acrylate or methacrylate or an oligosiloxanyl-silylalkyl acrylate or methacrylate containing 2 to 10 silicon atoms, or mixture thereof, and (d) 0.1 to 3 percent by weight of a crosslinking agent having at least two copolymerizable vinyl groups.
Claim 2
Dependent Claim
182 words
A copolymer, having the characteristics of high clarity, high hydrophilicity, and high oxygen permeability and which is, in the water swollen hydrated state, soft and flexible, which copolymer comprises the polymerization product of, with weight percent based on the total weight of monomers (a), (b), (c) and (d), of (a) 24.9 to 70 percent by weight of N,N-dimethylacrylamide, (b) 65 to 19.9 percent by weight of a vinyl monomer selected from the group consisting of the acrylate or methacrylate esters of formula B1 ##STR5## wherein R 1 is hydrogen or methyl, n is an integer from 1-4, m is an integer from 0-11, X is hydrogen or fluorine, with the proviso that, when m is 0, X is fluorine; and hexafluoroisopropyl methacrylate, (c) 10 to 40 percent by weight of a C 2 -C 4 -hydroxyalkyl acrylate or methacrylate, a C 2 -C 4 -alkoxy-alkyl acrylate or methacrylate or an oligosiloxanyl-silylalkyl acrylate or methacrylate containing 2 to 10 silicon atoms, or mixture thereof, and (d) 0.1 to 3 percent by weight of a crosslinking agent having at least two copolymerizable vinyl groups.
Claim 3
Dependent Claim
51 words
A copolymer according to claim 1 wherein based on the total weight of copolymer, component (a) is 34.99 to 55 percent by weight, component (b) is 14.9 to 55 percent by weight, component (c) is 10 to 40 percent by weight, and component (d) is 0.1 to 2 percent by weight.
Claim 4
Dependent Claim
27 words
A copolymer according to claim 1 wherein component (b) is hexafluoroisopropyl methacrylate, undecafluorocyclohexyl-methyl methacrylate or a fluorinated acrylate or methacrylate of formula B1 where X is fluorine.
Claim 5
Dependent Claim
40 words
A copolymer according to claim 1 wherein component (b) is a fluorinated methacrylate of formula B1where X is fluorine, n is 1 or 2, and m is 1 to 7, and component (c) is 10 to 40 percent by weight.
Claim 6
Dependent Claim
14 words
A copolymer according to claim 4 wherein in component (b) R 1 is methyl.
Claim 7
Dependent Claim
22 words
A copolymer according to claim 4 wherein component (c) is methoxy-ethyl acrylate, ethoxy-ethyl methacrylate, methoxy-ethyl methacrylate, 2-hydroxyethyl methacrylate or a mixture thereof.
Claim 8
Dependent Claim
21 words
A copolymer according to claim 4 wherein component (c) is methoxyethyl methacrylate or a mixture of methoxyethyl methacrylate and 2-hydroxyethyl methacrylate.
Claim 9
Dependent Claim
26 words
A copolymer according to claim 1 wherein component (c) is 5 to 30 percent by weight of an oligosiloxanyl-silylalkyl methacrylate having 3 to 7 silicon atoms.
Claim 10
Dependent Claim
12 words
A copolymer according to claim 8 wherein component (c) is tris(trimethylsiloxanyl-silyl)propyl methacrylate.
Claim 11
Dependent Claim
47 words
A copolymer according to claim 1 wherein component (c) is 0.1 to 10 percent by weight of an ethylenically unsaturated carboxylic acid, an ethylenically unsaturated sulfonic acid, a tertiary di-C 1 -C 2 -alkylaminoalkyl acrylate or methacrylate or a hydroxy-C 2 -C 4 -alkyl acrylate or methacrylate.
Claim 12
Dependent Claim
17 words
A copolymer according to claim 1 wherein component (c) is methoxy-ethyl methacrylate, methoxy-ethyl acrylate or ethoxy-ethyl methacrylate.
Claim 13
Dependent Claim
23 words
A copolymer according to claim 1, wherein component (d) is a poly(vinyl alcohol-co-ethylene) reacted with 0.1-10 mol % of a vinyl unsaturated isocyanate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-03 | 1994-03-05 | 1994-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-03 | 1998-03-05 | 1998-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-03 | 2002-03-05 | 2002-09-04 | $7700.00 | Window Closed / Lapsed |