Resin-fortified emulsion polymers and methods of preparing the same
Assignee: SC Johnson Commercial Markets Inc
•
Filing: 1989-01-11
•
Granted: 1990-09-04
•
Expires: 2009-01-11
Abstract
Abstract The stability and physical properties of high molecular weight emulsion polymers are improved by the addition of a low molecular weight support resin during the emulsion polymerization process. The resin is soluble or dispersible in water or alkali and has a number average molecular weight between 500 and 20,000.
Inventors
- 👤 Sheng-Liang Tsaur
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:24
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/12; C08F2/16; C08F2/22
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
202 words
A resin-fortified polymer emulsion having Newtonian-like flow characteristics, the resin-fortified polymer emulsion being made by a method which comprises the following steps: (a) emulsion-polymerizing a monomer charge comprising at least one emulsion-polymerizable monomer in the presence of a polymeric stabilizer and an initiator under emulsion-polymerization reaction conditions effective for initiating emulsion polymerization of an emulsion-polymerization mixture, the polymeric stabilizer being present in an amount that is effective for preventing coagulation of emulsion polymer particles which are forming in the emulsion-polymerization mixture; and thereafter (b) adding to the emulsion-polymerization mixture, while emulsion polymerization of the emulsion-polymerizable monomer is occurring, an effective amount of at least one support resin for controllably affecting the physical characteristics of the emulsion polymer product, said resin being selected from the group consisting of water soluble resins, water dispersible resins, alkali soluble resins, alkali dispersible resins and mixtures thereof, said resin having been produced either by a solution-polymerization method or by a bulk-polymerization method, wherein the resin is produced from at least one ethylenically-unsaturated monomer selected from the group consisting of olefins, mono vinylidene aromatics, alpha beta ethylenically-unsaturated carboxylic acids and esters thereof, ethylenically-unsaturated dicarboxylic anhydrides, and mixtures thereof, thereby producing the resin-fortified polymer emulsion having Newtonian-like flow characteristics.
Claim 2
Dependent Claim
202 words
A resin-fortified polymer emulsion having Newtonian-like flow characteristics, the resin-fortified polymer emulsion being made by a method which comprises the following steps: (a) emulsion-polymerizing a monomer charge comprising at least one emulsion-polymerizable monomer in the presence of a polymeric stabilizer and an initiator under emulsion-polymerization reaction conditions effective for initiating emulsion polymerization of an emulsion-polymerization mixture, the polymeric stabilizer being present in an amount that is effective for preventing coagulation of emulsion polymer particles which are forming in the emulsion-polymerization mixture; and thereafter (b) adding to the emulsion-polymerization mixture, while emulsion polymerization of the emulsion-polymerizable monomer is occurring, an effective amount of at least one support resin for controllably affecting the physical characteristics of the emulsion polymer product, said resin being selected from the group consisting of water soluble resins, water dispersible resins, alkali soluble resins, alkali dispersible resins and mixtures thereof, said resin having been produced either by a solution-polymerization method or by a bulk-polymerization method, wherein the resin is produced from at least one ethylenically-unsaturated monomer selected from the group consisting of olefins, mono vinylidene aromatics, alpha beta ethylenically-unsaturated carboxylic acids and esters thereof, ethylenically-unsaturated dicarboxylic anhydrides, and mixtures thereof, thereby producing the resin-fortified polymer emulsion having Newtonian-like flow characteristics.
Claim 3
Dependent Claim
11 words
A coating composition comprising the resin-fortified polymer emulsion of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-03 | 1994-03-05 | 1994-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-03 | 1998-03-05 | 1998-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-03 | 2002-03-05 | 2002-09-04 | $7700.00 | Window Closed / Lapsed |