Manganese activated zinc silicate phosphor

Claim 2

A manganese activated zinc silicate phosphor having cations consisting essentially of zinc, silicon, manganese, and tungsten prepared by a method comprising the following steps: Step 1--heating in a furnace a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1000° C. to about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from the acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 7--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 8--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 3

A fluorescent lamp comprising a light transmitting envelope having an inner wall, and inert ionizable gas and a charge of mercury therein said wall of said light transmitting envelope being coated with at least one layer of a phosphor prepared by a method comprising the following steps: Step 1--heating a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1000° C. to about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from the acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 7--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 8--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 4

A fluorescent lamp comprising a light transmitting envelope having an inner wall, and inert ionizable gas and a charge of mercury therein said wall of said light transmitting envelope being coated with at least one layer of a phosphor prepared by a method comprising the following steps: Step 1--heating a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1000° C. to about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from the acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 7--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 8--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 5

A fluorescent lamp in accordance with claim 2 wherein said one layer comprises a blend of phosphors, said blend of phosphors comprising at least one phosphor in accordance with claim 4.

Claim 6

A manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten prepared by a method comprising the following steps: Step 1--heating a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from said acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5; Step 7--adding NH 4 Cl to said phosphor powder from Step 6 to form a mixture of said NH 4 Cl and said phosphor powder; Step 8--heating said mixture of said NH 4 Cl and said phosphor powder from Step 7 in a furnace to a temperature of about 1000° C. in air; Step 9--cooling said phosphor powder from Step 8; Step 10--wet milling said phosphor powder from Step 9 in an acid solution; Step 11--separating said phosphor powder from Step 10 from said acid solution; Step 12--washing said phosphor powder from Step 11 with water; and Step 13--drying said phosphor powder from Step 12 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 14--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 15--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 7

A manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten prepared by a method comprising the following steps: Step 1--heating a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from said acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5; Step 7--adding NH 4 Cl to said phosphor powder from Step 6 to form a mixture of said NH 4 Cl and said phosphor powder; Step 8--heating said mixture of said NH 4 Cl and said phosphor powder from Step 7 in a furnace to a temperature of about 1000° C. in air; Step 9--cooling said phosphor powder from Step 8; Step 10--wet milling said phosphor powder from Step 9 in an acid solution; Step 11--separating said phosphor powder from Step 10 from said acid solution; Step 12--washing said phosphor powder from Step 11 with water; and Step 13--drying said phosphor powder from Step 12 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 14--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 15--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 8

A fluorescent lamp comprising a light transmitting envelope having an inner wall, and inert ionizable gas and a charge of mercury therein said wall of said light transmitting envelope being coated with at least one layer of a phosphor prepared by a method comprising the following steps: Step 1--heating a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from said acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5; Step 7--adding NH 4 Cl to said phosphor powder from Step 6 to form a mixture of said NH 4 Cl and said phosphor powder; Step 8--heating said mixture of said NH 4 Cl and said phosphor powder from Step 7 in a furnace to a temperature of about 1000° C. in air; Step 9--cooling said phosphor powder from Step 8; Step 10--wet milling said phosphor powder from Step 9 in an acid solution; Step 11--separating said phosphor powder from Step 10 from said acid solution; Step 12--washing said phosphor powder from Step 11 with water; and Step 13--drying said phosphor powder from Step 12 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 14--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 15--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 9

A fluorescent lamp comprising a light transmitting envelope having an inner wall, and inert ionizable gas and a charge of mercury therein said wall of said light transmitting envelope being coated with at least one layer of a phosphor prepared by a method comprising the following steps: Step 1--heating a manganese activated zinc silicate phosphor powder having cations consisting essentially of zinc, silicon, manganese, and tungsten and having a 350 nm reflectance less than 80%, and a 275 nm reflectance greater than 13.5% in a furnace to a temperature of about 1225° C. in air; Step 2--cooling said phosphor powder from Step 1; Step 3--wet milling said phosphor powder from Step 2 in an acid solution; Step 4--separating said phosphor powder from Step 3 from said acid solution; Step 5--washing said phosphor powder from Step 4 with water; Step 6--drying said phosphor powder from Step 5; Step 7--adding NH 4 Cl to said phosphor powder from Step 6 to form a mixture of said NH 4 Cl and said phosphor powder; Step 8--heating said mixture of said NH 4 Cl and said phosphor powder from Step 7 in a furnace to a temperature of about 1000° C. in air; Step 9--cooling said phosphor powder from Step 8; Step 10--wet milling said phosphor powder from Step 9 in an acid solution; Step 11--separating said phosphor powder from Step 10 from said acid solution; Step 12--washing said phosphor powder from Step 11 with water; and Step 13--drying said phosphor powder from Step 12 to form a manganese activated zinc silicate phosphor powder having individual particles, a 350 nm reflectance equal to or greater than 80%, a 275 nm reflectance equal to or less than 13.5%, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm; Step 14--coating said individual particles of said manganese activated zinc silicate phosphor powder with a continuous coating of alumina to form a manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles; Step 15--annealing said manganese activated zinc silicate phosphor powder having a continuous coating of alumina on said individual particles at a temperature of about 700° C. to about 850° C. for a period of about 15 min. to about 20 hours to form an annealed coated phosphor.

Claim 10

A fluorescent lamp comprising a light transmitting envelope having an inner wall, and inert ionizable gas and a charge of mercury therein said wall of said light transmitting envelope being coated with at least one layer of a blend of phosphors, said blend of phosphors comprising at least one phosphor in accordance with claim 3 wherein said one layer comprises a blend of phosphors, said blend of phosphors comprising at least one phosphor in accordance with claim 4.

Claim 11

A manganese activated zinc silicate phosphor having cations consisting essentially of zinc, silicon, manganese and tungsten and having an absolute reflectance less than or equal to 13.5 percent at 275 nm, an absolute reflectance equal to or greater than 80 percent at 350 nm, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm.

Claim 12

A manganese activated zinc silicate phosphor having cations consisting essentially of zinc, silicon, manganese and tungsten and having an absolute reflectance less than or equal to 13.5 percent at 275 nm, an absolute reflectance equal to or greater than 80 percent at 350 nm, and a surface area from about 0.3 m 2 /gm to about 0.4 m 2 /gm.

Claim 13

The phosphor according to claim 7 further comprising a continuous layer of alumina on each particle of said phosphor.

Claim 14

The phosphor according to claim 8 wherein said phosphor has been annealed at a temperature of about 700° C. to about 850° C. for a period of about 20 minutes to about 20 hours to form an annealed coated phosphor.