US4948548A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming reducing formation of impressions from the forming tool
Assignee: Roehm GmbH Darmstadt
•
Filing: 1989-03-02
•
Granted: 1990-08-14
•
Expires: 2009-03-02
Abstract
Abstract In forming operations on plastic sheets, plates, strips, or tubes (particularly, having highly glossy surfaces) by molding or forming tools, the surface qualities, particularly the gloss, remains undamaged if; (a) the tool is maintained at a temperature in the thermoelastic state region of the plastic until disengagement of the plastic from the tool; and (b) the formed plastic is cooled at its rear side to below the softening temperature, and is disengaged from the forming tool while said tool is hot.
Inventors
- 👤 Friedrich Hanstein
- 👤 Karl-Heinz Fehring
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:41
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/42; B29C49/64; B29C51/00; B29C51/26; B29C51/42; B29C51/426; B29C35/00; B29C35/16; B29K; B29K2033/00; B29K2995/00; B29K2995/0018; B29K2995/0022
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
139 words
A method of forming a plastic article having a first surface and a second surface opposing said first surface, by means of a heated forming tool, comprising the steps of: heating said plastic article to a thermoelastic state in a thermoelastic region of said plastic; contacting said first surface of said plastic article with said forming tool and forming said plastic article, said tool having a thermal conductivity at least an order of magnitude higher than the thermal conductivity of said plastic article and having a temperature which is in the thermoelastic region of the plastic; cooling said opposing surface of said formed plastic article below a softening temperature of the plastic until said opposing surface is shape-retentive; and then disengaging said first surface from the forming tool while the temperature of said tool is in said thermoelastic region.
Claim 2
Independent Claim
139 words
A method of forming a plastic article having a first surface and a second surface opposing said first surface, by means of a heated forming tool, comprising the steps of: heating said plastic article to a thermoelastic state in a thermoelastic region of said plastic; contacting said first surface of said plastic article with said forming tool and forming said plastic article, said tool having a thermal conductivity at least an order of magnitude higher than the thermal conductivity of said plastic article and having a temperature which is in the thermoelastic region of the plastic; cooling said opposing surface of said formed plastic article below a softening temperature of the plastic until said opposing surface is shape-retentive; and then disengaging said first surface from the forming tool while the temperature of said tool is in said thermoelastic region.
Claim 3
Dependent Claim
15 words
The method of claim 1, wherein said forming tool is comprised of a metal material,
Claim 4
Dependent Claim
23 words
The method of claim 2, wherein said metal material is aluminum, copper, steel or a press-formed material having substantial amounts of metal filler.
Claim 5
Dependent Claim
30 words
The method of claim 1, wherein said plastic article is in the thermoelastic state and is contacted by said forming tool by applying excess gas pressure, to said plastic article.
Claim 6
Dependent Claim
14 words
The method of claim 1, wherein said plastic article has a high gloss surface.
Claim 7
Dependent Claim
36 words
The method of claim 1, wherein said plastic article is comprised of a plastic selected from the group consisting of acrylic plastics, extruded acrylic glass substitutes, cellulose ester plastics, polyvinyl chlorides, polystyrenes, polyolefins, and mixtures thereof.
Claim 8
Dependent Claim
16 words
The method of claim 6, wherein said plastic article is comprised of an acrylic glass substitute.
Claim 9
Dependent Claim
12 words
The method of claim 1, wherein said contacting step includes vacuum molding.
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein said plastic article is comprised of an acrylic glass substitute and said opposing surface is cooled to about 80°-100° C. after forming with said tool.
Claim 11
Dependent Claim
33 words
The method of claim 1, wherein said plastic article is comprised of an extruded acrylic glass substitute and is cooled on the opposing surface to about 70°-90° C. after forming with said tool.
Claim 12
Dependent Claim
49 words
The method of claim 1, wherein said cooling step establishes a temperature gradient between said first surface and said opposing surface, wherein said first surface has a temperature in the thermoelastic region of said plastic and said opposing surface has a temperature below the softening temperature of the plastic.
Claim 13
Dependent Claim
29 words
The method of claim 11, wherein said first surface has a temperature in the thermoelastic region of said plastic to a depth of a few microns beneath said surface.
References Cited (Backward Citations)
US4584157A
Cited
US4704081A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-13 | 1994-02-12 | 1994-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-13 | 1998-02-12 | 1998-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-13 | 2002-02-12 | 2002-08-14 | $7700.00 | Window Closed / Lapsed |