Method of producing waveguide
Assignee: Machida Endoscope Co Ltd
•
Filing: 1989-07-20
•
Granted: 1990-08-14
•
Expires: 2009-07-20
Abstract
Abstract In the production of a waveguide, a pipe of a glass which is soluble in an acid or an alkali is used in order to obtain a smooth inner peripheral surface of a reflecting layer of the waveguide. After the reflecting layer is formed on the outer periphery of the pipe, the glass pipe is dipped in an etchant to be dissolved and removed. A reinforcement layer can be applied to the waveguide, and the reinforcement layer is made of a resin in order to keep the flexibility of the waveguide. In this case, the reinforcement layer of a resin is formed on the outer periphery of the reflecting layer on the pipe, and thereafter the pipe is dipped in the etchant and is removed. The waveguide of a circular cross-section can be flatted. In this case, the reinforcement layer made of a thermoplastic resin is heated to be softened, and then a compressive force is applied to the waveguide radially thereof to flatten the waveguide.
Inventors
- 👤 Yuichi Komachi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 01:27
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/032; C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03B37/01861; C03B37/075; C03B37/0756; C03B2203/00; C03B2203/02; C03B2203/04; C03B2203/10; C03B2203/12; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1062; Y10T156/1064; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49016; Y10T29/4981
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
77 words
A method of producing a waveguide comprising the steps of: (a) forming a reflecting layer on an entire outer periphery of a core of glass which is soluble; and (b) subsequently dipping said core with said reflecting layer in an etchant to dissolve and remove said pipe, thereby providing the waveguide formed by said reflecting layer, said waveguide having a central bore which is disposed radially inwardly of said reflecting layer and serves as a waveguide path.
Claim 2
Independent Claim
77 words
A method of producing a waveguide comprising the steps of: (a) forming a reflecting layer on an entire outer periphery of a core of glass which is soluble; and (b) subsequently dipping said core with said reflecting layer in an etchant to dissolve and remove said pipe, thereby providing the waveguide formed by said reflecting layer, said waveguide having a central bore which is disposed radially inwardly of said reflecting layer and serves as a waveguide path.
Claim 3
Dependent Claim
26 words
A method according to claim 1, further comprising the step of forming a reinforcement layer of a resin on the outer periphery of said reflecting layer.
Claim 4
Dependent Claim
19 words
A method according to claim 1, wherein the core takes the form of a pipe of a circular cross-section.
Claim 5
Independent Claim
129 words
A method of producing a waveguide comprising the steps of: (a) forming a reflecting layer on an outer periphery of a core which is soluble; (b) inserting the core with the reflecting layer thereon into a tube of a heat-shrinkable resin; (c) subsequently forming a reinforcement layer of the resin on the outer periphery of the reflecting layer by heat-shrinking the tube radially into intimate contact with the reflecting layer; and (d) thereafter dipping the core with the reinforcement layer and the reflecting layer formed thereon in an etchant to dissolve and remove the core, thereby providing the waveguide formed by the reinforcement layer and the reflecting layer, the waveguide having a central bore which is disposed radially inwardly of the dielectric layer and serves as a waveguide path.
Claim 6
Independent Claim
129 words
A method of producing a waveguide comprising the steps of: (a) forming a reflecting layer on an outer periphery of a core which is soluble; (b) inserting the core with the reflecting layer thereon into a tube of a heat-shrinkable resin; (c) subsequently forming a reinforcement layer of the resin on the outer periphery of the reflecting layer by heat-shrinking the tube radially into intimate contact with the reflecting layer; and (d) thereafter dipping the core with the reinforcement layer and the reflecting layer formed thereon in an etchant to dissolve and remove the core, thereby providing the waveguide formed by the reinforcement layer and the reflecting layer, the waveguide having a central bore which is disposed radially inwardly of the dielectric layer and serves as a waveguide path.
Claim 7
Dependent Claim
49 words
A method according to claim 4, in which a first layer of metal is formed on the entire outer periphery of said pipe, a second layer of metal being formed on an entire outer periphery of said first layer, and said reflecting layer comprising said first and second layers.
Claim 8
Dependent Claim
23 words
A method according to claim 5, in which said first layer is formed by vacuum deposition, said second layer being formed by plating.
Claim 9
Independent Claim
148 words
A method of producing a generally flat-type waveguide comprising the steps of: (a) forming a reflecting layer on an outer periphery of a core of a circular cross-section which is soluble; (b) forming a reinforcement layer of a thermoplastic resin on an outer periphery of said reflecting layer; (c) subsequently dipping said pipe with said reflecting layer and said reinforcement layer in an etchant to dissolve and remove said core, thereby providing a waveguide of a circular cross-section formed by said reflecting layer and said reinforcement layer, said waveguide having a central bore which is disposed radially inwardly of said reflecting layer and serves as a waveguide path; and (d) subsequently heating said reinforcement layer to soften it, and applying a compressive force to said waveguide of a circular cross-section radially of said waveguide to flatten said reflecting layer and said reinforcement layer, thereby providing the flat-type waveguide.
Claim 10
Independent Claim
148 words
A method of producing a generally flat-type waveguide comprising the steps of: (a) forming a reflecting layer on an outer periphery of a core of a circular cross-section which is soluble; (b) forming a reinforcement layer of a thermoplastic resin on an outer periphery of said reflecting layer; (c) subsequently dipping said pipe with said reflecting layer and said reinforcement layer in an etchant to dissolve and remove said core, thereby providing a waveguide of a circular cross-section formed by said reflecting layer and said reinforcement layer, said waveguide having a central bore which is disposed radially inwardly of said reflecting layer and serves as a waveguide path; and (d) subsequently heating said reinforcement layer to soften it, and applying a compressive force to said waveguide of a circular cross-section radially of said waveguide to flatten said reflecting layer and said reinforcement layer, thereby providing the flat-type waveguide.
Claim 11
Dependent Claim
32 words
A method according to claim 7, in which opposite ends of said central bore of said waveguide of a circular cross-section are closed when the compressive force is applied to said waveguide.
Claim 12
Independent Claim
113 words
A method of producing a waveguide comprising the steps of: (a) forming a dielectric layer on an outer periphery of a core of glass which is soluble; (b) subsequently forming a reflecting layer on an outer periphery of the dielectric layer; and (c) thereafter dipping the core with the dielectric layer and the reflecting layer formed thereon in an etchant to dissolve and remove the core, thereby providing the waveguide formed by the dielectric layer and reflecting layer, the waveguide having a central bore which is disposed radially inwardly of the dielectric layer and serves as a waveguide path, the dielectric layer and the reflecting layer cooperating to enhance the efficiency of reflection.
Claim 13
Independent Claim
113 words
A method of producing a waveguide comprising the steps of: (a) forming a dielectric layer on an outer periphery of a core of glass which is soluble; (b) subsequently forming a reflecting layer on an outer periphery of the dielectric layer; and (c) thereafter dipping the core with the dielectric layer and the reflecting layer formed thereon in an etchant to dissolve and remove the core, thereby providing the waveguide formed by the dielectric layer and reflecting layer, the waveguide having a central bore which is disposed radially inwardly of the dielectric layer and serves as a waveguide path, the dielectric layer and the reflecting layer cooperating to enhance the efficiency of reflection.
Claim 14
Dependent Claim
27 words
A method according to claim 9, further comprising a step (d) of forming a reinforcement layer of a resin on the outer periphery of the reflecting layer.
Claim 15
Independent Claim
154 words
A method of producing a waveguide comprising the steps of: (a) forming a reflecting layer on an outer periphery of a core which is soluble; (b) applying an adhesive to at least one of an outer peripheral surface of the reflecting layer and an inner peripheral surface of a tube of a heat-shrinkable resin; (c) inserting the core with the reflecting layer thereon into the tube; (d) subsequently forming a reinforcement layer of the resin on the outer periphery of the reflecting layer by heat-shrinking the tube radially into intimate contact with the reflecting layer; and (e) thereafter dipping the core with the reinforcement layer and the reflecting layer formed thereon in an etchant to dissolve and remove the core, thereby providing the waveguide formed by the reinforcement layer and the reflecting layer, the waveguide having a central bore which is disposed radially inwardly of the dielectric layer and serves as a waveguide path.
Claim 16
Independent Claim
154 words
A method of producing a waveguide comprising the steps of: (a) forming a reflecting layer on an outer periphery of a core which is soluble; (b) applying an adhesive to at least one of an outer peripheral surface of the reflecting layer and an inner peripheral surface of a tube of a heat-shrinkable resin; (c) inserting the core with the reflecting layer thereon into the tube; (d) subsequently forming a reinforcement layer of the resin on the outer periphery of the reflecting layer by heat-shrinking the tube radially into intimate contact with the reflecting layer; and (e) thereafter dipping the core with the reinforcement layer and the reflecting layer formed thereon in an etchant to dissolve and remove the core, thereby providing the waveguide formed by the reinforcement layer and the reflecting layer, the waveguide having a central bore which is disposed radially inwardly of the dielectric layer and serves as a waveguide path.
References Cited (Backward Citations)
US3290762A
Cited
US3566516A
Cited
US3810302A
Cited
US4115916A
Cited
JPS5713412A
Cited
JPS60140202A
Cited
JPS6179303A
Cited
JPS61141204A
Cited
JPS61188506A
Cited
JPS61233705A
Cited
JPS61238104A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-13 | 1994-02-12 | 1994-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-13 | 1998-02-12 | 1998-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-13 | 2002-02-12 | 2002-08-14 | $7700.00 | Window Closed / Lapsed |