Phase separation processes
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1988-08-16
•
Granted: 1990-08-07
•
Expires: 2008-08-16
Abstract
Abstract A separation process has been found in which a polymer-solvent solution separates into phases of highly different composition which are in equilibrium over a broad temperature range. Upon addition of the phase separating agent, which is near or above its supercritical conditions, rapid disengagement into two phases occurs. The relative volume of solvent rich phase is substantially larger than the polymer rich phase. The process can be practiced at relatively low temperatures such as those employed in polymerization or post-polymerization processes. The separation is accomplished by adding or elevating the concentration of a phase separation agent to or above a minimum effective concentration, which causes the UCST and LCST lines to merge. Suitable phase separating agents are organic and inorganic compounds that are gases at 1 atm pressure and 25 DEG C. Due to the gaseous nature of the phase separating agent, it is easily removed from the solvent phase for reuse in the process.
Inventors
- 👤 Terry L. Guckes
- 👤 Mark A. McHugh
- 👤 Charles Cozewith
- 👤 Ronald L. Hazelton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:16
CPC Classifications
C; C08; C08F; C08F6/00; C08F6/06; C08F6/12; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/54
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
211 words
A process for separating a polymer from a solvent in which it is dissolved which comprises: (1) introducing a phase separation agent (PSA) into said solution to form a system, said agent being a gas at 25° C. and one atmosphere absolute, the concentration of said agent in the system being at least equal to a critical concentration for said agent; (2) conducting a separation in the system whereby a liquid, solvent rich phase is separated from a liquid, polymer rich phase, said separation being conducted at a concentration of PSA in the liquid phases, of at least a critical amount effective to impart to the system, phase relationships which are substantially temperature-independent with respect to a first region having two liquid phases, a second region having liquid-liquid-vapor phases and a third region having a homogenous liquid phase, over a temperature range below the Lower Critical Solution Temperature and down to the Upper Critical Solution Temperature points of the pure solvent-polymer combination; the separation being carried out at a preselected pressure at which the system separates into at least two distinct phases comprising a first liquid, solvent-rich phase and a second liquid, polymer-rich phase; (3) separating the polymer-rich phase from the system; and (4) recovering the polymer from the polymerrich phase.
Claim 2
Dependent Claim
211 words
A process for separating a polymer from a solvent in which it is dissolved which comprises: (1) introducing a phase separation agent (PSA) into said solution to form a system, said agent being a gas at 25° C. and one atmosphere absolute, the concentration of said agent in the system being at least equal to a critical concentration for said agent; (2) conducting a separation in the system whereby a liquid, solvent rich phase is separated from a liquid, polymer rich phase, said separation being conducted at a concentration of PSA in the liquid phases, of at least a critical amount effective to impart to the system, phase relationships which are substantially temperature-independent with respect to a first region having two liquid phases, a second region having liquid-liquid-vapor phases and a third region having a homogenous liquid phase, over a temperature range below the Lower Critical Solution Temperature and down to the Upper Critical Solution Temperature points of the pure solvent-polymer combination; the separation being carried out at a preselected pressure at which the system separates into at least two distinct phases comprising a first liquid, solvent-rich phase and a second liquid, polymer-rich phase; (3) separating the polymer-rich phase from the system; and (4) recovering the polymer from the polymerrich phase.
Claim 3
Dependent Claim
21 words
The process of claim 1 wherein the separation of step 3 is conducted in the liquid=phase phases of said first region.
Claim 4
Dependent Claim
21 words
The process of claim 1 where the separation of step 3 is conducted in the liquid-liquid-vapor phases of said second region.
Claim 5
Dependent Claim
21 words
A process according to claim 1 wherein said separation temperature in step 2 is from about 20° C. to 100° C.
Claim 6
Dependent Claim
11 words
A process according to claim 1 wherein the PSA comprises methane.
Claim 7
Dependent Claim
13 words
A process according to claim 1 wherein the polymer is a hydrocarbon polymer.
Claim 8
Dependent Claim
22 words
A process according to claim 4 wherein the separation of step 2 is achieved by additionally adjusting the pressure of said system.
Claim 9
Dependent Claim
19 words
A process according to claim 1 wherein the separation of step is simultaneous with the recovery of step 4.
Claim 10
Dependent Claim
23 words
The process of claim 1 wherein the separation of step 2 is conducted at a temperature of up to about the LCST point.
Claim 11
Dependent Claim
33 words
The process according to claim 1 wherein the PSA comprises methane and the separation of step 2 is conducted at a temperature in the range of from about 20° C. to 100° C.
Claim 12
Dependent Claim
18 words
A process according to claim 1 wherein the polymer is selected from ethylene-propylene and ethylenepropylene nonconjugated diene rubbers.
Claim 13
Dependent Claim
21 words
A process according to claim 11 wherein the separation of step 2 is conducted at a temperature above the UCST point.
Claim 14
Dependent Claim
35 words
A process according to claim 1 wherein the polymer is selected from the group consisting of EPM and EPDM rubbers and said separation temperature in step 2 is from about 20° C. to 100° C.
Claim 15
Dependent Claim
212 words
A process for separating a polymer from a solution comprising hexane in which it was polymerized and which contains unreacted monomer comprising: (1) introducing a phase separation agent (PSA) into said solution to form a system, said agent being a gas at 25° C. and one atmosphere absolute the concentration of said agent being at least equal to a critical concentration of said agent for said system; (2) conducting a separation in the system to separate a liquid, hexane-rich phase from a liquid, polymer-rich phase said separation being conducted at a concentration of PSA in the liquid phases, of at least a critical amount effective to impart to the system, phase relationships which are substantially temperature independent, with respect to a first region having two liquid phases, a second region having liquid-liquid-vapor phases and a third region having a homogeneous liquid phase; over a temperature range below the Lower Critical Solution Temperature and the Upper Critical Solution Temperature points of the pure solvent-polymer combination; the separation being carried out at a preselected pressure at which the system separates into at least two phases comprising a first liquid, solvent-rich phase and a second liquid, polymer-rich phase; (3) separating the polymer-rich phase from the system; and (4) recovering the polymer from the polymerrich phase.
Claim 16
Dependent Claim
212 words
A process for separating a polymer from a solution comprising hexane in which it was polymerized and which contains unreacted monomer comprising: (1) introducing a phase separation agent (PSA) into said solution to form a system, said agent being a gas at 25° C. and one atmosphere absolute the concentration of said agent being at least equal to a critical concentration of said agent for said system; (2) conducting a separation in the system to separate a liquid, hexane-rich phase from a liquid, polymer-rich phase said separation being conducted at a concentration of PSA in the liquid phases, of at least a critical amount effective to impart to the system, phase relationships which are substantially temperature independent, with respect to a first region having two liquid phases, a second region having liquid-liquid-vapor phases and a third region having a homogeneous liquid phase; over a temperature range below the Lower Critical Solution Temperature and the Upper Critical Solution Temperature points of the pure solvent-polymer combination; the separation being carried out at a preselected pressure at which the system separates into at least two phases comprising a first liquid, solvent-rich phase and a second liquid, polymer-rich phase; (3) separating the polymer-rich phase from the system; and (4) recovering the polymer from the polymerrich phase.
Claim 17
Dependent Claim
17 words
The process according to 14 wherein the separation of step 3 is conducted in the first region.
Claim 18
Dependent Claim
17 words
The process according to 14 wherein the separation of step 3 is conducted in the first region.
Claim 19
Dependent Claim
17 words
The process according to 14 wherein the separation of step 3 is conducted in the second region.
Claim 20
Dependent Claim
17 words
The process according to 14 wherein the separation of step 3 is conducted in the second region.
Claim 21
Dependent Claim
20 words
The process according to 14 wherein said separation temperature in step 2 is from about 20° C. to 100° C.
Claim 22
Dependent Claim
20 words
The process according to 14 wherein said separation temperature in step 2 is from about 20° C. to 100° C.
Claim 23
Dependent Claim
37 words
The process according to claim 14 wherein the phase separation agent is methane, the polymer is an EPM or EPDM and the methane is utilized at a concentration in the system of at least 11.5 wt. %.
Claim 24
Dependent Claim
20 words
The process of claim 14 wherein the polymer is selected from the group consisting of ethylene-propylene and ethylene-propylene-nonconjugated diene rubbers.
Claim 25
Dependent Claim
20 words
The process according to claim 1 wherein the polymer is selected from the group consisting of butyl and halobutyl rubbers.
Claim 26
Dependent Claim
27 words
The process according to claim 1 wherein the phase separation agent is CO 2 , CO, hydrogen, helium, neon, nitrogen, an oxide of nitrogen, or mixtures thereof.
Claim 27
Dependent Claim
34 words
The process according to claim 1 wherein the phase separation agent is CO 2 or nitrogen and the polymer is selected from the group consisting of EPM, EPDM, butyl rubber and halo butyl rubber.
Claim 28
Dependent Claim
34 words
The process according to claim 14 wherein the phase separation agent is CO 2 or nitrogen and the polymer is selected from the group consisting of EPM, EPDM, butyl rubber and halo butyl rubber.
References Cited (Backward Citations)
US3932371A
Cited
US3553156A
Cited
US3496135A
Cited
US3726843A
Cited
US4319021A
Cited
US4444922A
Cited
US4623712A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-06 | 1994-02-05 | 1994-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-06 | 1998-02-05 | 1998-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-06 | 2002-02-05 | 2002-08-07 | $7700.00 | Window Closed / Lapsed |