Non-woven fibrous product
Assignee: Guardian Industries Corp
•
Filing: 1989-12-22
•
Granted: 1990-08-07
•
Expires: 2009-12-22
Abstract
Abstract A non-woven matrix of sized bushing glass and synthetic fibers provides a rigid but resilient product having good strength and insulating characteristics. The product finds particular application in large area panels such as vehicle headliners. The matrix consists of glass fibers, first, solid or hollow homogeneous synthetic fibers such as polyester, nylon or Kevlar and second, bi-component synthetic fibers which have been intimately combined with a thermosetting resin into a homogeneous mixture. The bi-component synthetic fibers include an outer low melting temperature sheath and a higher melting temperature core. This mixture is dispersed to form a blanket. The blanket may be heated and pressed to cure and form it into a final product in one step on two steps. In the one step process, the curing temperature is sufficiently high to melt the sheath of the bi-component fibers and activate and cure the thermosetting resin. In the two step process, first the sheath of the bi-component fibers is melted to form initial bonds. Subsequently, the thermosetting resin is heated and cured. The product may be utilized in a planar configuration or be formed into complexly curved and shaped configurations. The product may also include a skin, film or fabric on one or both faces thereof.
Inventors
- 👤 Vaughn C. Chenoweth
- 👤 Roger C. Goodsell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:04
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/40; D04H1/58; D04H1/60; D04H1/42; D04H1/4209; D04H1/4218; D04H1/4326; D04H1/4334; D04H1/4342; D04H1/435; D04H1/4382; D04H1/43825; D04H1/43828; D04H1/43835; D04H1/4391; D04H1/43914; D04H1/43838; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24074; Y10T428/24091; Y10T442/00; Y10T442/10; Y10T442/184; Y10T442/197; Y10T442/60; Y10T442/637; Y10T442/641
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
61 words
A non-woven fibrous product comprising, in combination, a blended matrix of bushing glass fibers and synthetic fibers, said synthetic fibers including homogeneous fibers selected from the group consisting of polyester, nylon, Nomex or Kevlar and bi-component fibers having a core of higher melting temperature polymer and a sheath of lower melting temperature polymer, and a thermosetting resin dispersed in said matrix.
Claim 2
Dependent Claim
61 words
A non-woven fibrous product comprising, in combination, a blended matrix of bushing glass fibers and synthetic fibers, said synthetic fibers including homogeneous fibers selected from the group consisting of polyester, nylon, Nomex or Kevlar and bi-component fibers having a core of higher melting temperature polymer and a sheath of lower melting temperature polymer, and a thermosetting resin dispersed in said matrix.
Claim 3
Dependent Claim
18 words
The non-woven fibrous product of claim 1 wherein said bushing glass fibers include a coating of plastic size.
Claim 4
Dependent Claim
27 words
The non-woven fibrous product of claim 1 further including a scrim on one surface of said product and a fabric on the other surface of said product.
Claim 5
Dependent Claim
36 words
The non-woven fibrous product of claim 1 wherein said bushing glass fibers have a diameter of between approximately 4 and 20 microns and said synthetic fibers have a diameter of between approximately 10 and 50 microns.
Claim 6
Dependent Claim
38 words
The non-woven fibrous product of claim 1 wherein said bushing glass fibers have a length of between approximately one quarter and four inches and said synthetic fibers have a length of between approximately one quarter and four inches.
Claim 7
Dependent Claim
64 words
The non-woven fibrous product of claim 1 wherein said bushing glass fibers constitute between 35 and 50 weight percent of said product, said synthetic homogeneous fibers constitute between 30 and 45 weight percent of said product, said synthetic, bi-component fibers constitute between 2 and 6 weight percent of said product, and said thermosetting resin constitutes between 10 and 23 weight percent of said product.
Claim 8
Dependent Claim
57 words
The non-woven fibrous product of claim 1 wherein said bushing glass fibers constitute about 42 weight percent of said product, said synthetic homogeneous fibers constitute about 38 weight percent of said product, said synthetic, bi-component fibers constitute between about 4 weight percent of said product, and said thermosetting resin constitutes about 16 weight percent of said product.
Claim 9
Dependent Claim
43 words
The non-woven fibrous product of claim 1 further including a scrim secured to at least one face of said product, said scrim having a thickness of from 2 to 10 mils and a fabric layer secured to the other face of said product.
Claim 10
Dependent Claim
23 words
The non-woven fibrous product of claim 1 wherein said higher melting temperature is at least 100° F. higher than said lower melting temperature.
Claim 11
Dependent Claim
62 words
A non-woven fibrous product comprising, in combination, a homogeneously blended matrix of bushing glass fibers and synthetic fibers, said synthetic fibers including homogeneous fibers selected from the group consisting of polyester, nylon, Nomex or Kevlar and bi-component fibers having a core of higher melting temperature polymer and a sheath of lower melting temperature polymer, and a thermosetting resin dispersed in said matrix.
Claim 12
Dependent Claim
62 words
A non-woven fibrous product comprising, in combination, a homogeneously blended matrix of bushing glass fibers and synthetic fibers, said synthetic fibers including homogeneous fibers selected from the group consisting of polyester, nylon, Nomex or Kevlar and bi-component fibers having a core of higher melting temperature polymer and a sheath of lower melting temperature polymer, and a thermosetting resin dispersed in said matrix.
Claim 13
Dependent Claim
23 words
The non-woven fibrous product of claim 10 wherein said bushing glass fibers are E glass fibers chopped to lengths less than 4 inches.
Claim 14
Dependent Claim
36 words
The non-woven fibrous product of claim 10 wherein said bushing glass fibers have a diameter of between approximately 4 and 20 microns and said synthetic fibers have a diameter of between approximately 10 and 50 microns.
Claim 15
Dependent Claim
38 words
The non-woven fibrous product of claim 10 wherein said bushing glass fibers have a length of between approximately one quarter and four inches and said synthetic fibers have a length of between approximately one quarter and four inches.
Claim 16
Dependent Claim
64 words
The non-woven fibrous product of claim 10 wherein said bushing glass fibers constitute between 35 and 50 weight percent of said product, said synthetic homogeneous fibers constitute between 30 and 45 weight percent of said product, said synthetic, bi-component fibers constitute between 2 and 6 weight percent of said product, and said thermosetting resin constitutes between 10 and 23 weight percent of said product.
Claim 17
Dependent Claim
57 words
The non-woven fibrous product of claim 10 wherein said bushing glass fibers constitute about 42 weight percent of said product, said synthetic homogeneous fibers constitute about 38 weight percent of said product, said synthetic, bi-component fibers constitute between about 4 weight percent of said product, and said thermosetting resin constitutes about 16 weight percent of said product.
Claim 18
Dependent Claim
32 words
The non-woven fibrous product of claim 1 wherein said sheath of said bi-component fibers has melted and formed bonds with adjacent said fibers and said thermosetting resin is in its uncured state.
Claim 19
Dependent Claim
41 words
The non-woven fibrous product of claim 10 further including a scrim secured to one face of said product, said scrim having a thickness of from 2 to 10 mils and a fabric layer secured to the other face of said product.
Claim 20
Dependent Claim
18 words
The non-woven fibrous product of claim 1 wherein said homogeneous synthetic fibers define at least one axial passageway.
Claim 21
Dependent Claim
23 words
The non-woven fibrous product of claim 10 wherein said higher melting temperature is at least 100° F. higher than said lower melting temperature.
Claim 22
Dependent Claim
65 words
A non-woven fibrous product comprising, in combination, a homogeneously blended matrix of sized bushing glass fibers and synthetic fibers, said synthetic fibers including homogeneous fibers selected from the group consisting of polyester, nylon, Nomex or Kevlar fibers and bi-component polyester fibers having a core of higher melting temperature polyester and a sheath of lower melting temperature polyester, and a thermosetting resin disposed in said matrix.
Claim 23
Dependent Claim
65 words
A non-woven fibrous product comprising, in combination, a homogeneously blended matrix of sized bushing glass fibers and synthetic fibers, said synthetic fibers including homogeneous fibers selected from the group consisting of polyester, nylon, Nomex or Kevlar fibers and bi-component polyester fibers having a core of higher melting temperature polyester and a sheath of lower melting temperature polyester, and a thermosetting resin disposed in said matrix.
References Cited (Backward Citations)
US2483405A
Cited
US2695855A
Cited
US2689199A
Cited
US4612238A
Cited
US4508777A
Cited
US4568581A
Cited
US4681802A
Cited
US4680223A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-06 | 1994-02-05 | 1994-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-06 | 1998-02-05 | 1998-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-06 | 2002-02-05 | 2002-08-07 | $7700.00 | Window Closed / Lapsed |