Low oxygen content fine spherical copper particles and process for producing same by fluid energy milling and high temperature processing
Assignee: Osram Sylvania Inc
•
Filing: 1989-01-03
•
Granted: 1990-07-31
•
Expires: 2009-01-03
Abstract
Abstract A powder material and a process for producing same are disclosed. The process comprises reducing the size of an electrolytically produced starting dendritic copper powder material by fluid energy milling to produce a finer powder, essentially all of which has a particle size of less than about 20 micrometers in diameter, entraining the finer powder in a carrier gas and passing it through a high temperature zone at a temperature above the melting point of the finer powder, the temperature being from about 5500 DEG C. to about 17,000 DEG C., to melt at least about 50% by weight of the finer powder to form essentially fine spherical particles of the melted portion, and rapidly and directly resolidifying the resulting high temperature treated material while the material is in flight, to form fine spherical particles having a particle size of less than about 20 micrometers in diameter. The particles are essentially free of elliptical shaped material and essentially free of elongated particles having rounded ends, and have an oxygen content of less than about 0.5% by weight, and a carbon content of no greater than the carbon content of the starting material.
Inventors
- 👤 Preston B. Kemp, Jr.
- 👤 Walter A. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:48
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/60; H10W70/62; H10W70/66; H10W70/666; B; B22; B22F; B22F9/00; B22F9/02; B22F9/04; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
193 words
A process for producing fine spherical copper powder particles, said process comprising: (a) reducing the size of a electrolytically produced starting dendritic copper powder material by fluid energy milling to produce a finer powder, essentially all of which has a particle size of less than about 20 micrometers in diameter; (b) entraining said finer powder in a carrier gas and passing said powder through a high temperature zone at a temperature above the melting point of said finer powder said temperature being from about 5500° C. to about 17,000° C., to melt at least about 50% by weight of said finer powder to form essentially fine spherical particles of said melted portion; and (c) rapidly and directly resolidifying the resulting high temperature treated material while said material is in flight, to form fine spherical particles having a particle size of less than about 20 micrometers in diameter, said particles being essentially free of elliptical shaped material and essentially free of elongated particles having rounded ends, said particles having an oxygen content of less than about 0.5% by weight, and a carbon content of no greater than the carbon content of said starting material.
Claim 2
Dependent Claim
193 words
A process for producing fine spherical copper powder particles, said process comprising: (a) reducing the size of a electrolytically produced starting dendritic copper powder material by fluid energy milling to produce a finer powder, essentially all of which has a particle size of less than about 20 micrometers in diameter; (b) entraining said finer powder in a carrier gas and passing said powder through a high temperature zone at a temperature above the melting point of said finer powder said temperature being from about 5500° C. to about 17,000° C., to melt at least about 50% by weight of said finer powder to form essentially fine spherical particles of said melted portion; and (c) rapidly and directly resolidifying the resulting high temperature treated material while said material is in flight, to form fine spherical particles having a particle size of less than about 20 micrometers in diameter, said particles being essentially free of elliptical shaped material and essentially free of elongated particles having rounded ends, said particles having an oxygen content of less than about 0.5% by weight, and a carbon content of no greater than the carbon content of said starting material.
Claim 3
Dependent Claim
27 words
A process of claim 1 wherein the size of said starting material is reduced by fluidized bed opposed jet milling said material to produce said finer powder.
Claim 4
Dependent Claim
20 words
A process of claim 2 wherein the size of said starting material is reduced by fluidized bed opposed jet milling.
Claim 5
Dependent Claim
26 words
A process of claim 1 wherein after said resolidification, said high temperature treated material is classified to obtain the desired particle size of said spherical particles.
Claim 6
Dependent Claim
13 words
A process of claim 1 wherein said high temperature zone is a plasma.
Claim 7
Dependent Claim
132 words
A powder material consisting essentially of spherical copper particles, said powder material being essentially free of elliptical shaped material and essentially free of elongated particles having rounded ends, said powder material having a particle size of less than about 20 micrometers in diameter, said powder material being made by jet milling a starting electrolytically produced material which is dendritic copper powder in the dry state with an inert gas by impacting the particles of said starting material against each other to fracture said particles of said starting material, followed by high temperature processing and direct solidification of the resulting high temperature treated material, said powder material having an oxygen content of less than about 0.5% by weight and a carbon content of no greater than the carbon content of said starting material.
Claim 8
Dependent Claim
132 words
A powder material consisting essentially of spherical copper particles, said powder material being essentially free of elliptical shaped material and essentially free of elongated particles having rounded ends, said powder material having a particle size of less than about 20 micrometers in diameter, said powder material being made by jet milling a starting electrolytically produced material which is dendritic copper powder in the dry state with an inert gas by impacting the particles of said starting material against each other to fracture said particles of said starting material, followed by high temperature processing and direct solidification of the resulting high temperature treated material, said powder material having an oxygen content of less than about 0.5% by weight and a carbon content of no greater than the carbon content of said starting material.
Claim 9
Dependent Claim
23 words
A powder material of claim 6 wherein the maximum particle size of said spherical particles is less than about 10 micrometers in diameter.
Claim 10
Dependent Claim
19 words
A powder material of claim 6 wherein said maximum particle size is greater than about 0.1 micrometer in diameter.
Claim 11
Dependent Claim
18 words
A powder material of claim 7 wherein the particle size is greater than about 0.1 micrometer in diameter.
References Cited (Backward Citations)
US4711611A
Cited
US4783214A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-30 | 1994-01-29 | 1994-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-30 | 1998-01-29 | 1998-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-30 | 2002-01-29 | 2002-07-31 | $7700.00 | Window Closed / Lapsed |