Method for the preparation of a silicone-based pressure-sensitive adhesive
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1989-01-17
•
Granted: 1990-07-24
•
Expires: 2009-01-17
Abstract
Abstract The invention proposes use of ammonia water in place of a conventional caustic alkali or amine compound as a catalyst in the siloxane rearrangement reaction for the preparation of a silicone-based pressure-sensitive adhesive between a poly(diorganosiloxane) having a linear molecular structure and another organopolysiloxane composed mainly of the monofunctional organosiloxane units and tetrafunctional siloxane units. The ammonia water after completion of the reaction can be easily and completely removed by distillation so that the resultant adhesive product is free from any alkaline residue of the catalyst to be imparted with greatly improved stability against viscosity changes and excellent electrical properties along with high reproducibility of the product quality.
Inventors
- 👤 Shiro Gomyo
- 👤 Takahide Kobori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:55
CPC Classifications
C; C09; C09J; C09J183/00; C09J183/10; C08; C08G; C08G77/00; C08G77/04; C08G77/06; C08G77/08; C08G77/10; C08G77/42; C08G77/44
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
181 words
A method for the preparation of a silicone-based pressure-sensitive adhesive which comprises the steps of: (a) adding ammonia water to a mixture of a first organopolysiloxane having a substantially linear molecular structure represented by the average unit formula R 1 m SiO.sub.(4-m)/2, in which R 1 is a substituted or unsubstituted monovalent hydrocarbon group and m is a positive number in the range from 1.8 to 2.1, at least 90% by moles of the organosiloxane units being diorganosiloxane units of the formula R 1 2 SiO, and a second organopolysiloxane composed mainly of monofunctional siloxane units of the formula R 2 3 SiO 0 .5, in which R 2 is a substituted or unsubstituted monovalent hydrocarbon group, and tetrafunctional siloxane units of the formula SiO 2 , the molar ratio of the monofunctional siloxane units to the tetrafunctional siloxane units being in the range from 0.4 to 2.0, to form a reaction mixture; (b) agitating the reaction mixture to effect the siloxane rearrangement reaction between the first and the second organopolysiloxanes; and (c) removing the ammonia water from the reaction mixture.
Claim 2
Independent Claim
181 words
A method for the preparation of a silicone-based pressure-sensitive adhesive which comprises the steps of: (a) adding ammonia water to a mixture of a first organopolysiloxane having a substantially linear molecular structure represented by the average unit formula R 1 m SiO.sub.(4-m)/2, in which R 1 is a substituted or unsubstituted monovalent hydrocarbon group and m is a positive number in the range from 1.8 to 2.1, at least 90% by moles of the organosiloxane units being diorganosiloxane units of the formula R 1 2 SiO, and a second organopolysiloxane composed mainly of monofunctional siloxane units of the formula R 2 3 SiO 0 .5, in which R 2 is a substituted or unsubstituted monovalent hydrocarbon group, and tetrafunctional siloxane units of the formula SiO 2 , the molar ratio of the monofunctional siloxane units to the tetrafunctional siloxane units being in the range from 0.4 to 2.0, to form a reaction mixture; (b) agitating the reaction mixture to effect the siloxane rearrangement reaction between the first and the second organopolysiloxanes; and (c) removing the ammonia water from the reaction mixture.
Claim 3
Dependent Claim
34 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 1 wherein the group denoted by R 1 is selected from the group consisting of methyl, phenyl and vinyl groups.
Claim 4
Dependent Claim
30 words
The method for the preparation of a silicone-based pressure sensitive adhesive as claimed in claim 1 wherein the group denoted by R 2 is a methyl group or phenyl group.
Claim 5
Dependent Claim
32 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed ;n claim 1 wherein the first organopolysiloxane has an average degree of polymerization in the range from 100 to 10,000.
Claim 6
Dependent Claim
35 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 1 wherein the weight ratio of the first organopolysiloxane to the second organopolysiloxane is in the range from 0.3 to 3.0.
Claim 7
Dependent Claim
63 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 1 wherein the amount of the ammonia water is in the range from 0.2 to 2.0% by weight based on the total amount of the first organopolysiloxane and the second organopolysiloxane, the amount of the ammonia water being calculated for an ammonia water containing 27% by weight of ammonia.
Claim 8
Dependent Claim
36 words
The method for the preparation of a silicone-based pressure sensitive adhesive as claimed in claim 1 wherein the reaction mixture is agitated in step (b) at a temperature in the range from 30° to 60° C.
Claim 9
Dependent Claim
28 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 1 wherein in step (a) the reaction mixture is admixed with an organic solvent.
Claim 10
Dependent Claim
28 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 8 wherein the organic solvent is a solvent capable of azeotropically distilling with water.
Claim 11
Dependent Claim
44 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 1 wherein the ammonia water is removed from the reaction mixture in step (c) by heating the reaction mixture at a temperature in the range from 100° to 120° C.
Claim 12
Dependent Claim
35 words
The method for the preparation of a silicone-based pressure-sensitive adhesive as claimed in claim 1 which further comprises the step of admixing the reaction mixture after removal of the ammonia water with a crosslinking agent.
Claim 13
Dependent Claim
24 words
The method for the preparation of a silicone-based pressure sensitive adhesive as claimed in claim 11 wherein the crosslinking agent is an organic peroxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-23 | 1994-01-22 | 1994-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-23 | 1998-01-22 | 1998-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-23 | 2002-01-22 | 2002-07-24 | $7700.00 | Window Closed / Lapsed |