Stable solutions of prepolymers of thiodi(phenylcyanate) and laminating method employing same
Assignee: Huntsman Advanced Materials Americas LLC
•
Filing: 1988-11-10
•
Granted: 1990-07-10
•
Expires: 2008-11-10
Abstract
Abstract Stable prepolymer solutions are made from partially cyclotrimerized 4,4'-thiodi(phenylcyanate) dissolved in cyclopentanone. The prepolymer solutions are used to make flame retardant and thermally stable laminates.
Inventors
- 👤 David A. Shimp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:37
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/0622; C08G73/0638; C08G73/065; C08G73/0655; C08J; C08J3/00; C08J3/02; C08J3/09; C08J3/091; C08J5/00; C08J5/24; C08J5/241; C08J5/244; C08J5/249; C08L; C08L79/00; C08L79/04; C08J2379/00; C08J2379/04; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0346
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
53 words
A stable solution of a prepolymer of thiodi(phenylcyanate) comprising: (A) a prepolymer of thiodi(phenylcyanate) wherein about 20 to about 65 percent of the cyanate groups are cyclotrimerized; and (B) as a solvent, cyclopentanone, wherein about 25 to about 90 weight percent of the prepolymer is present in the total weight of the solution.
Claim 2
Dependent Claim
53 words
A stable solution of a prepolymer of thiodi(phenylcyanate) comprising: (A) a prepolymer of thiodi(phenylcyanate) wherein about 20 to about 65 percent of the cyanate groups are cyclotrimerized; and (B) as a solvent, cyclopentanone, wherein about 25 to about 90 weight percent of the prepolymer is present in the total weight of the solution.
Claim 3
Dependent Claim
25 words
The solution of claim 1 wherein about 40 to about 80 weight percent of the prepolymer is present in the total weight of the solution.
Claim 4
Dependent Claim
18 words
The solution of claim 2 wherein the viscosity at 25° C. is about 30 to about 5,000 centipoise.
Claim 5
Dependent Claim
18 words
The solution of claim 1 wherein about 30 to about 60 percent of the cyanate groups are cyclotrimerized
Claim 6
Dependent Claim
109 words
In a process for preparing flame retardant laminates by the steps of: (a) impregnating fibers with a solution of a prepolymer of a polycyanate ester; (b) heating the impregnated fibers to remove solvent and to "B" stage the prepolymer, and; (c) heating under pressure one or more plies of the "B" staged impregnated fibers to cure the prepolymer, the improvement which comprises using a solution of a prepolymer of thiodi(phenylcyanate) in cyclopentanone solvent wherein the cyanate groups in the prepolymer are about 20 to about 65 percent trimerized and wherein about 25 to about 90 weight percent of the prepolymer is present in the total weight of the solution.
Claim 7
Dependent Claim
109 words
In a process for preparing flame retardant laminates by the steps of: (a) impregnating fibers with a solution of a prepolymer of a polycyanate ester; (b) heating the impregnated fibers to remove solvent and to "B" stage the prepolymer, and; (c) heating under pressure one or more plies of the "B" staged impregnated fibers to cure the prepolymer, the improvement which comprises using a solution of a prepolymer of thiodi(phenylcyanate) in cyclopentanone solvent wherein the cyanate groups in the prepolymer are about 20 to about 65 percent trimerized and wherein about 25 to about 90 weight percent of the prepolymer is present in the total weight of the solution.
Claim 8
Dependent Claim
33 words
The process of claim 5 wherein the prepolymer solution contains about 40 to about 80 weight percent of the prepolymer wherein said weight percent is based on the total weight of the solution.
Claim 9
Dependent Claim
19 words
The process of claim 5 wherein the viscosity of the prepolymer solution is about 30 to about 5,000 centipoise.
Claim 10
Dependent Claim
18 words
The process of claim 5 wherein about 30 to about 60 percent of the cyanate groups are cyclotrimerized.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-09 | 1994-01-08 | 1994-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-09 | 1998-01-08 | 1998-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-09 | 2002-01-08 | 2002-07-10 | $7700.00 | Window Closed / Lapsed |