Method for preparing superconducting oxide films by seeding formation and heat treatment
Assignee: Siemens AG
•
Filing: 1989-01-26
•
Granted: 1990-07-10
•
Expires: 2009-01-26
Abstract
Abstract A superconducting oxide film is prepared by a method of seeding formation and heat treatment which comprises depositing a layer of a metal-oxide precursor on a predetermined substrate, forming a seed of a predetermined superconducting phase only in a locally limited region of the metal-oxide precursor at a boundary surface to the substrate by means of a solid-state reaction triggered by pulsed energy radiation, and then at least partially converting the metal-oxide precursor into the desired superconducting metal-oxide phase by a heat treatment in the oxygen atmosphere at a temperature below 800° C.
Inventors
- 👤 Ludwig Schultz
- 👤 Joachim Wecker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:54
CPC Classifications
C; C30; C30B; C30B1/00; C30B1/02; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/225; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0548; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/729; Y10S505/73; Y10S505/742
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
140 words
In a method for the preparation of at least one layer of a copper oxide based superconductor with a high transition temperature, comprising applying a layer on a predetermined substrate of a metal-oxide precursor of the components of the system with a structure still exhibiting faults with respect to a superconducting metal oxide phase to be formed and subsequently forming the desired superconducting metal-oxide phase using a heat treatment in an oxygen atmosphere, the improvement comprising forming a seed of the superconducting phase only in a locally limited region of the metal-oxide precursor at a boundary surface to the substrate by means of a solid-state reaction triggered by pulsed energy radiation, and then at least partially converting the preliminary product into the desired superconducting metal-oxide phase by heat treatment in the oxygen atmosphere at a predetermined temperature below 800° C.
Claim 2
Dependent Claim
140 words
In a method for the preparation of at least one layer of a copper oxide based superconductor with a high transition temperature, comprising applying a layer on a predetermined substrate of a metal-oxide precursor of the components of the system with a structure still exhibiting faults with respect to a superconducting metal oxide phase to be formed and subsequently forming the desired superconducting metal-oxide phase using a heat treatment in an oxygen atmosphere, the improvement comprising forming a seed of the superconducting phase only in a locally limited region of the metal-oxide precursor at a boundary surface to the substrate by means of a solid-state reaction triggered by pulsed energy radiation, and then at least partially converting the preliminary product into the desired superconducting metal-oxide phase by heat treatment in the oxygen atmosphere at a predetermined temperature below 800° C.
Claim 3
Dependent Claim
20 words
The method recited in claim 1 wherein the heat treatment comprises heating at a temperature between 500° and 700° c.
Claim 4
Dependent Claim
52 words
The method recited in claim 1, wherein the seed formation is caused by the radiation of at least one light pulse of a laser, at least one of said substrate and said metal-oxide precursor being transparent, said light pulse being transmitted through said optically transparent substrate or said optically transparent metal-oxide precursor.
Claim 5
Dependent Claim
20 words
The method recited in claim 1, wherein the pulsed energy radiation takes place during the deposition of the metal-oxide precursor.
Claim 6
Dependent Claim
42 words
The method recited in claim 1, wherein a material is chosen for the substrate having lattice constants or unit cells having dimensions which are adapted at least approximately to the corresponding sizes of the crystals of the superconducting metal-oxide phase formed thereon.
Claim 7
Dependent Claim
12 words
The method recited in claim 1, wherein a monocrystalline substrate is provided.
Claim 8
Dependent Claim
32 words
The method recited in claim 1, wherein a substrate is provided which contains at least one of Al 2 O 3 , ZrO 2 , MgO, SrTiO 3 or BaTiO 3 .
Claim 9
Dependent Claim
21 words
The method recited in claim 1, wherein at least a thin layer of the substrate material is provided on a carrier.
Claim 10
Dependent Claim
51 words
The method recited in claim 1, wherein a physical or chemical process is provided for depositing the metal-oxide precursor, said physical or chemical process comprising at least one of a laser evaporation process, a sputtering process, a vapor deposition process by an electron beam source and a chemical vapor deposition process.
Claim 11
Dependent Claim
37 words
The method recited in claim 1, wherein an RF-aided laser evaporation of the separate metallic components of the system is provided as a physical deposition process while oxygen is being provided as gas and/or an ion stream.
Claim 12
Dependent Claim
40 words
The method recited in claim 1, wherein evaporation of the separate metallic components with the aid of suitable electron beam sources while oxygen is being supplied as a gas and/or an ion stream is provided as a physical deposition process.
Claim 13
Dependent Claim
21 words
The method recited in claim 1, wherein a metal-oxide precursor with a layer thickness of at most 100 μm is deposited.
Claim 14
Dependent Claim
15 words
The method recited in claim 12, wherein the layer thickness is at most 10 μm.
Claim 15
Dependent Claim
15 words
The method recited in claim 12, wherein the layer thickness is at most 1 μm.
Claim 16
Dependent Claim
19 words
The method recited in claim 1, wherein first, a metal-oxide precursor with a polycrystalline or amorphous structure, is formed.
Claim 17
Dependent Claim
38 words
The method recited in claim 1, wherein at least one layer of a superconducting Me1-Me2-Cu-O material is produced, wherein said component Me1 comprises a rare earth metal or yttrium and said component Me2 comprises an alkaline earth metal.
Claim 18
Dependent Claim
20 words
The method recited in claim 16, wherein the first metallic component Me1 is partially substituted by another rare earth metal.
Claim 19
Dependent Claim
20 words
The method recited in claim 16, wherein the second metallic component Me2 is substituted partially by another alkaline earth metal.
Claim 20
Dependent Claim
20 words
The method recited in claim 17, wherein the second metallic component Me2 is substituted partially by another alkaline earth metal.
Claim 21
Dependent Claim
17 words
The method recited in claim 16, wherein the copper or the oxygen is partially substituted by F.
Claim 22
Dependent Claim
17 words
The method recited in claim 17, wherein the copper or the oxygen is partially substituted by F.
Claim 23
Dependent Claim
17 words
The method recited in claim 18, wherein the copper or the oxygen is partially substituted by F.
Claim 24
Dependent Claim
19 words
The method recited in claim 16, wherein a metal-oxide superconducting Y-Ba-Cu-O system with an orthorhombic crystal structure is produced.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-09 | 1994-01-08 | 1994-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-09 | 1998-01-08 | 1998-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-09 | 2002-01-08 | 2002-07-10 | $7700.00 | Window Closed / Lapsed |