Method for production of copper indium diselenide
Assignee: Panasonic Holdings Corp
•
Filing: 1988-09-02
•
Granted: 1990-07-10
•
Expires: 2008-09-02
Abstract
Abstract A polycrystalline CuInSe2 film is produced by adding a liquid cooling medium to a mixture of Cu, In and Se powders, grinding the resulting composition by means of a ball-mill to provide a slurry containing CuInSe2 of low crystallinity, drying and adding a binding agent to the slurry to form a paste, coating a substrate with the paste, and sintering the paste so applied under a nitrogen atmosphere. The starting materials that can be used are not limited to respective powders of the above-mentioned elements but may be Cu-Se and In-Se compounds and the method provides CuInSe2 of excellent quality on a mass production scale at low cost.
Inventors
- 👤 Naoki Suyama
- 👤 Noriyuki Ueno
- 👤 Kuniyoshi Omura
- 👤 Hazime Takada
- 👤 Yuutaro Kita
- 👤 Mikio Murozono
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:55
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F77/00; H10F77/10; H10F77/12; H10F77/126; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
109 words
A method of producing a copper indium diselenide film which comprises adding a liquid cooling medium to a mixture of Cu, In and Se powders, said liquid cooling medium being selected from the group consisting of water, ethylene glycol monophenyl ether, propylene glycol and perfluorobutyltetrahydrofuran, grinding the resulting mixture using a mill to give a slurry containing a ground powder including CuInSe 2 of low crystallinity, drying and adding a binding agent to said slurry to give a paste, wherein said binding agent is propylene glycol, coating a substrate with said paste, and sintering the paste so applied under a nitrogen atmosphere to form a polycrystalline CuInSe 2 film.
Claim 2
Independent Claim
109 words
A method of producing a copper indium diselenide film which comprises adding a liquid cooling medium to a mixture of Cu, In and Se powders, said liquid cooling medium being selected from the group consisting of water, ethylene glycol monophenyl ether, propylene glycol and perfluorobutyltetrahydrofuran, grinding the resulting mixture using a mill to give a slurry containing a ground powder including CuInSe 2 of low crystallinity, drying and adding a binding agent to said slurry to give a paste, wherein said binding agent is propylene glycol, coating a substrate with said paste, and sintering the paste so applied under a nitrogen atmosphere to form a polycrystalline CuInSe 2 film.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein the ratio of said Cu, In and Se powders is 24:25:51.
Claim 4
Dependent Claim
12 words
The method of claim 1, wherein said mill is an agitated ball-mill.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein each of said material Cu, In and Se powders has a grain size not exceeding 500 μm.
Claim 6
Dependent Claim
22 words
The method of claim 1, wherein the ground powder prior to sintering has a median grain size of 1.5 to 5.0 μm.
Claim 7
Dependent Claim
30 words
The method of claim 1, wherein the coating of said substrate with said paste containing CuInSe 2 of low crystallinity is carried out by a screen printing or writing machine.
Claim 8
Dependent Claim
22 words
The method of claim 1, wherein the sintering is performed at a temperature below the melting point of polycrystalline CuInSe 2 .
References Cited (Backward Citations)
JPS63285974A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-09 | 1994-01-08 | 1994-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-09 | 1998-01-08 | 1998-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-09 | 2002-01-08 | 2002-07-10 | $7700.00 | Window Closed / Lapsed |