Thermally stable diamond abrasive compact body
Assignee: Individual
•
Filing: 1989-08-04
•
Granted: 1990-07-10
•
Expires: 2009-08-04
Abstract
Abstract A method of producing a thermally stable diamond compact having a metal layer bonded to a surface thereof is provided. The thermally stable diamond compact comprises a mass of diamond particles containing diamond-to-diamond bonding and a second phase uniformly distributed through the diamond mass. The metal of the metallic layer is molybdenum, tantalum, titanium or like high melting refractory metal, nickel or an alloy containing a dominant amount of any one of these metals. The method includes the steps of: (i) preparing an assembly of a metallic layer, a mass of diamond particles on the metallic layer and a layer of the component or components necessary to form the second phase on the diamond particles, this component or these components having a melting point lower than that of the metallic layer; and (ii) placing the assembly in a canister and subjecting the assembly to conditions of elevated temperature and pressure for a period sufficient to produce the diamond abrasive compact, the temperature being first raised to a level where the component or components for the second phase are molten allowing their infiltration into the diamond mass and the compact to be produced, but the metallic layer is not molten, and thereafter raising it to a level where the metallic layer bonds to the thus formed compact.
Inventors
- 👤 Trevor J. Martell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:30
CPC Classifications
B; B24; B24D; B24D3/00; B24D3/02; B24D3/04; B24D3/14; B24D3/16; B24D99/00; B24D3/06; B24D3/10; C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B37/00; C04B37/02; C04B37/021; C04B37/023; C04B37/026; B22; B22F; B22F7/00; B22F7/06; B22F7/062; B22F7/064; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/122; C04B2237/123; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/363; C04B2237/40; C04B2237/401; C04B2237/403; C04B2237/405; C04B2237/50; C04B2237/61; Y; Y10; Y10S; Y10S76/00; Y10S76/12
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
173 words
A method of producing a thermally stable diamond compact having a metallic layer bonded to a surface thereof, the thermally stable diamond compact comprising a mass of diamond particles containing diamond-to-diamond bonding and a second phase uniformly distributed through the diamond mass, and the metal of the metallic layer being selected from the group of molybdenum, tantalum, titanium and like high melting refractory metal, nickel and an alloy containing a dominant amount of any one of these metals, includes the steps of: (i) preparing an assembly of a metallic layer, a mass of diamond particles on the metallic layer and a layer of the component or components necessary to form the second phase on the diamond particles, this component or these components having a melting point lower than that of the metallic layer; and (ii) subjecting the assembly to conditions of elevated temperature and pressure for a period sufficient to produce the diamond abrasive compact, the temperature being controlled such that there is minimal infiltration of the metallic layer into the diamond mass.
Claim 2
Independent Claim
173 words
A method of producing a thermally stable diamond compact having a metallic layer bonded to a surface thereof, the thermally stable diamond compact comprising a mass of diamond particles containing diamond-to-diamond bonding and a second phase uniformly distributed through the diamond mass, and the metal of the metallic layer being selected from the group of molybdenum, tantalum, titanium and like high melting refractory metal, nickel and an alloy containing a dominant amount of any one of these metals, includes the steps of: (i) preparing an assembly of a metallic layer, a mass of diamond particles on the metallic layer and a layer of the component or components necessary to form the second phase on the diamond particles, this component or these components having a melting point lower than that of the metallic layer; and (ii) subjecting the assembly to conditions of elevated temperature and pressure for a period sufficient to produce the diamond abrasive compact, the temperature being controlled such that there is minimal infiltration of the metallic layer into the diamond mass.
Claim 3
Dependent Claim
65 words
A method according to claim 1 wherein the temperature is first raised to a level where the component or components for the second phase are molten allowing their infiltration into the diamond mass and the compact to be produced, but the metallic layer is not molten, and the temperature is thereafter raised to a level where the metallic layer bonds to the thus formed compact.
Claim 4
Dependent Claim
36 words
A method according to claim 2 wherein the temperature in the first stage is in the range 1100° to 1350° C. and the temperature in the second stage is higher than that of the first stage.
Claim 5
Dependent Claim
22 words
A method according to claim 3 wherein the temperature in the second stage is in the range 1300° C. to 1900° C.
Claim 6
Dependent Claim
15 words
A method according to claim 1 wherein the metal of the metallic layer is molybdenum.
Claim 7
Dependent Claim
22 words
A method according to claim 1 wherein the elevated pressure which is applied is in the range 27 kilobars to 70 kilobars.
Claim 8
Dependent Claim
30 words
A method according to claim 1 wherein the assembly includes a cemented carbide substrate and the metallic layer is placed on, and in contact with, a surface of the substrate.
Claim 9
Dependent Claim
15 words
A method according to claim 1 wherein the component for the second phase is silicon.
Claim 10
Independent Claim
237 words
A method of producing a thermally stable diamond compact having a metallic layer bonded to a surface thereof, the thermally stable diamond compact comprising a mass of diamond particles containing diamond-to-diamond bonding and a second phase uniformly distributed through the diamond mass, and the metal of the metallic layer being selected from the group of molybdenum, tantalum, titanium and like high melting refractory metal, nickel and an alloy containing a dominant amount of any one of these metals, includes the steps of: (i) preparing an assembly of a metallic layer, a mass of diamond particles on the metallic layer and a layer of the component or components necessary to form the second phase on the diamond particles, this component or these components having a melting point lower than that of the metallic layer; and (ii) subjecting the assembly to conditions of elevated temperature and pressure for a period sufficient to produce the diamond abrasive compact, the temperature being first raised to a level in the range 1100° to 1350° C. where the component or components for the second phase are molten allowing their infiltration into the diamond mass and the compact to be produced, but the metallic layer is not molten, and the temperature is thereafter raised to a level higher than that of the first stage and in the range 1300° C. to 1900° C. at which the metallic layer bonds to the thus formed compact.
Claim 11
Independent Claim
237 words
A method of producing a thermally stable diamond compact having a metallic layer bonded to a surface thereof, the thermally stable diamond compact comprising a mass of diamond particles containing diamond-to-diamond bonding and a second phase uniformly distributed through the diamond mass, and the metal of the metallic layer being selected from the group of molybdenum, tantalum, titanium and like high melting refractory metal, nickel and an alloy containing a dominant amount of any one of these metals, includes the steps of: (i) preparing an assembly of a metallic layer, a mass of diamond particles on the metallic layer and a layer of the component or components necessary to form the second phase on the diamond particles, this component or these components having a melting point lower than that of the metallic layer; and (ii) subjecting the assembly to conditions of elevated temperature and pressure for a period sufficient to produce the diamond abrasive compact, the temperature being first raised to a level in the range 1100° to 1350° C. where the component or components for the second phase are molten allowing their infiltration into the diamond mass and the compact to be produced, but the metallic layer is not molten, and the temperature is thereafter raised to a level higher than that of the first stage and in the range 1300° C. to 1900° C. at which the metallic layer bonds to the thus formed compact.
Claim 12
Dependent Claim
15 words
A method according to claim 9 wherein the metal of the metallic layer is molybdenum.
References Cited (Backward Citations)
US4241135A
Cited
JPS5711877A
Cited
JPS5756382A
Cited
EP0185537A2
Cited
US4766040A
Cited
US4776862A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-09 | 1994-01-08 | 1994-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-09 | 1998-01-08 | 1998-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-09 | 2002-01-08 | 2002-07-10 | $7700.00 | Window Closed / Lapsed |