Combination thermally sprayed antifouling metal coating and seal coat on a marine surface and method of preparing same
Assignee: Individual
•
Filing: 1988-08-29
•
Granted: 1990-07-03
•
Expires: 2008-08-29
Abstract
Abstract A combination thermally sprayed antifouling metal coating and seal coat on a marine surface and a method of preparing the same. The method comprises the steps of applying a resin coating on the marine surface, and thermally spraying molten metal particles on the resin coating to impinge and interlock with the resin coating and form one or more metal layers. The resin may be wet during the thermal spraying or be filled with hollow beads and spheres which are ruptured after curing to form locking sites for the metal coating. A seal overcoat is applied to the last one of the one or more metal layers. The seal overcoat when applied has low surface tension to permit wetting and penetration of the outer one of the one or more metal coatings, leveling and flattening properties to produce a smooth finish on the more metal coatings, thixotropic properties, abalative properties, and a high copper oxide content for antifouling.
Inventors
- 👤 Louis M. Riccio
- 👤 Alexander A. Bosna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:12
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/16; C09D5/1693; B; B05; B05D; B05D5/00; B63; B63B; B63B59/00; B63B59/04; Y; Y10; Y10S; Y10S428/00; Y10S428/907; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24364; Y10T428/24372; Y10T428/25; Y10T428/252
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
176 words
In an antifouling coating on a base surface comprising, in combination, a resin adhesion layer on said surface and means forming, at the surface of said adhesion layer opposed to said base surface, a plurality of undercuts and surface roughness, one or more thermally sprayed melted layers of a metal selected from the group consisting of copper and copper based alloys wherein molten particles of said thermally sprayed melted layers shape themselves to lock to said undercuts and surface roughness due to the impact velocity of said molten particles, the improvement comprising: a seal overcoat applied to the outer surfaces of said one or more thermally sprayed layers, said seal overcoat when applied having the following properties: a low surface tension to permit wetting and penetration of the outer one of said thermally sprayed metal layers, leveling and flattening properties to produce a smooth finish, abalative properties to result in a uniform leaching rate and a high copper oxide content for antifouling, and said overcoat including a thickening agent to provide thixotropic properties on vertical surfaces.
Claim 2
Dependent Claim
176 words
In an antifouling coating on a base surface comprising, in combination, a resin adhesion layer on said surface and means forming, at the surface of said adhesion layer opposed to said base surface, a plurality of undercuts and surface roughness, one or more thermally sprayed melted layers of a metal selected from the group consisting of copper and copper based alloys wherein molten particles of said thermally sprayed melted layers shape themselves to lock to said undercuts and surface roughness due to the impact velocity of said molten particles, the improvement comprising: a seal overcoat applied to the outer surfaces of said one or more thermally sprayed layers, said seal overcoat when applied having the following properties: a low surface tension to permit wetting and penetration of the outer one of said thermally sprayed metal layers, leveling and flattening properties to produce a smooth finish, abalative properties to result in a uniform leaching rate and a high copper oxide content for antifouling, and said overcoat including a thickening agent to provide thixotropic properties on vertical surfaces.
Claim 3
Independent Claim
130 words
A method of forming an antifouling metal coating on a marine surface comprising the steps of: A. applying a resin coating on said marine surface; B. thermally spraying molten metal particles on said resin coating to impinge and interlock with said resin coating, and form one or more metal layers; and C. applying a seal overcoat to the last one of said one or more metal layers, said seal overcoat when applied having low surface tension to permit wetting and penetration of the outer one of said one or more metal coatings, leveling and flattening properties to produce a smooth finish on said one or more metal coatings, thixotropic properties, and abalative properties to result in a uniform leaching rate, said overcoat having a high copper oxide content for antifouling.
Claim 4
Independent Claim
130 words
A method of forming an antifouling metal coating on a marine surface comprising the steps of: A. applying a resin coating on said marine surface; B. thermally spraying molten metal particles on said resin coating to impinge and interlock with said resin coating, and form one or more metal layers; and C. applying a seal overcoat to the last one of said one or more metal layers, said seal overcoat when applied having low surface tension to permit wetting and penetration of the outer one of said one or more metal coatings, leveling and flattening properties to produce a smooth finish on said one or more metal coatings, thixotropic properties, and abalative properties to result in a uniform leaching rate, said overcoat having a high copper oxide content for antifouling.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-02 | 1994-01-01 | 1994-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-02 | 1998-01-01 | 1998-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-02 | 2002-01-01 | 2002-07-03 | $7700.00 | Window Closed / Lapsed |