Process of bonding an electrical device package to a mounting surface
Assignee: Raytheon Co
•
Filing: 1986-10-08
•
Granted: 1990-06-19
•
Expires: 2006-10-08
Abstract
Abstract A thermally conductive adhesive, and processes for formulating the same, are provided for bonding an electrical device package, such as an integrated circuit (IC) package, to a surface of a substrate, such as a printed circuit board. The thermally conductive adhesive comprises a polyurethane-based resin material and a predetermined amount of thermally conducting, electrically insulating material, such as alumina, mixed therewith. With such arrangement, a thermally conductive adhesive is provided having a low modulus of elasticity. Thus, such adhesive is soft and pliable rather than rigid, and thus deforms in response to the different amounts of thermal expansion, or contraction, of the IC package and PCB against, or away from, the thermally-conductive adhesive, thereby preventing damage to either the IC package or PCB, or separation of solder joints therebetween, due to such thermal expansion or contraction. Additionally, such adhesive has a low bond strength, thus allowing an IC package to be removed from a PCB without damaging either the IC package or PCB. Also, such adhesive is found to have low outgassing properties. The thermally conductive adhesive may be formed into a film, mixed with a solvent and sprayed into a film, or applied directly to the PCB as paste-like substance.
Inventors
- 👤 Thomas E. Baker
- 👤 Nicki S. Girouard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:48
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/30; H05K3/303; H05K3/305; C; C09; C09J; C09J175/00; C09J175/04; C08; C08L; C08L2666/00; C08L2666/54; H05K1/00; H05K1/02; H05K1/0201; H05K1/0203; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0209; H05K2201/09; H05K2201/09209; H05K2201/09654; H05K2201/09781; H05K2201/10; H05K2201/10613; H05K2201/10621; H05K2201/10689; Y; Y02; Y02P; Y02P70/00; Y02P70/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/4913
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
145 words
A process of bonding an integrated circuit package to a mounting surface, such process comprising the steps of: (a) providing a polyurethane-based resin material; (b) mixing a thermally conductive material with such polyurethane-based resin material; (c) curing said mixture while forming a film having a predetermined thickness from said mixture; (d) cutting such film into a section, the section having the approximate size of the integrated circuit package; (e) applying a predetermined amount of said polyurethane-based resin material to first and second surfaces of the film section; (f) placing the film section on the mounting surface, with the first surface of the film section contacting the mounting surface; (g) placing the integrated circuit package on the second surface of the film section; and (h) curing such polyurethane-based resin material while applying a predetermined amount of pressure to the integrated circuit package against the mounting surface.
Claim 2
Dependent Claim
145 words
A process of bonding an integrated circuit package to a mounting surface, such process comprising the steps of: (a) providing a polyurethane-based resin material; (b) mixing a thermally conductive material with such polyurethane-based resin material; (c) curing said mixture while forming a film having a predetermined thickness from said mixture; (d) cutting such film into a section, the section having the approximate size of the integrated circuit package; (e) applying a predetermined amount of said polyurethane-based resin material to first and second surfaces of the film section; (f) placing the film section on the mounting surface, with the first surface of the film section contacting the mounting surface; (g) placing the integrated circuit package on the second surface of the film section; and (h) curing such polyurethane-based resin material while applying a predetermined amount of pressure to the integrated circuit package against the mounting surface.
Claim 3
Dependent Claim
90 words
A process of bonding an integrated circuit package to a mounting surface, such process comprising the steps of: (a) providing a polyurethane-based resin material; (b) mixing a thermally conductive, electrically insulating material with the resin material; (c) adding a curing agent to the mixture; (d) applying a portion of the mixture to the mounting surface; (e) placing the integrated circuit package on the mounting surface and over the mixture portion; and (f) applying pressure between the integrated circuit package and the mounting surface while allowing said mixture portion to cure.
Claim 4
Dependent Claim
90 words
A process of bonding an integrated circuit package to a mounting surface, such process comprising the steps of: (a) providing a polyurethane-based resin material; (b) mixing a thermally conductive, electrically insulating material with the resin material; (c) adding a curing agent to the mixture; (d) applying a portion of the mixture to the mounting surface; (e) placing the integrated circuit package on the mounting surface and over the mixture portion; and (f) applying pressure between the integrated circuit package and the mounting surface while allowing said mixture portion to cure.
Claim 5
Dependent Claim
24 words
The process of claim 2 wherein the polyurethane-based resin material has a modulus of elasticity on the order of 2,000 psi at room temperature.
Claim 6
Dependent Claim
25 words
The process of claim 3 wherein the polyurethane-based resin material maintains such modulus of elasticity on the order of 2,000 psi at temperatures below -50°C.
Claim 7
Dependent Claim
33 words
The process of claim 2 wherein the mixing step comprises the step of mixing the thermally conductive, electrically insulating material to a concentration of approximatly 70% by weight of the polyurethane-based resin material.
Claim 8
Dependent Claim
14 words
The process of claim 2 wherein the thermally conductive, electrically insulating material comprises alumina.
Claim 9
Dependent Claim
33 words
The process of claim 2 comprising the additional step of adding a predetermined amount of a colloidal silica to the mixture prior to the step of applying the curing agent to the mixture.
Claim 10
Dependent Claim
180 words
A process of bonding an electrical device package to a mounting surface, such process comprising the steps of: (a) providing a polyurethane-based resin material; (b) mixing a thermally conductive, electrically insulating material with the resin material; (c) adding a curing agent to the mixture; (d) subsequently adding a solvent to the mixture to form a liquid; (e) spraying the liquid onto a surface to a predetermined thickness and allowing such liquid to cure as a film; (f) cutting the cured film into a section having the approximate size of the electrical device package; (g) applying a predetermined amount of said polyurethane-based resin material to first and second surfaces of the section of film; (h) subsequently placing the section of film on the mounting surface, with the first surface of the section of film contacting the mounting surface; (i) placing the electrical device package on the second surface of the section of film; and (j) curing the applied polyurethane-based resin material while applying a predetermined amount of pressure to the electrical device package against the section of film and mounting surface.
Claim 11
Dependent Claim
180 words
A process of bonding an electrical device package to a mounting surface, such process comprising the steps of: (a) providing a polyurethane-based resin material; (b) mixing a thermally conductive, electrically insulating material with the resin material; (c) adding a curing agent to the mixture; (d) subsequently adding a solvent to the mixture to form a liquid; (e) spraying the liquid onto a surface to a predetermined thickness and allowing such liquid to cure as a film; (f) cutting the cured film into a section having the approximate size of the electrical device package; (g) applying a predetermined amount of said polyurethane-based resin material to first and second surfaces of the section of film; (h) subsequently placing the section of film on the mounting surface, with the first surface of the section of film contacting the mounting surface; (i) placing the electrical device package on the second surface of the section of film; and (j) curing the applied polyurethane-based resin material while applying a predetermined amount of pressure to the electrical device package against the section of film and mounting surface.
Claim 12
Dependent Claim
24 words
The process of claim 8 wherein the polyurethane-based resin material has a modulus of elasticity on the order of 2,000 psi at room temperature.
Claim 13
Dependent Claim
25 words
The process of claim 9 wherein the polyurethane-based resin material maintains such modulus of elasticity on the order of 2,000 psi at temperatures below -50°C.
Claim 14
Dependent Claim
33 words
The process of claim 8 wherein the mixing step comprises the step of mixing the thermally conductive, electrically insulating material to a concentration of approximately 70% by weight of the polyurethane-based resin material.
Claim 15
Dependent Claim
14 words
The process of claim 8 wherein the thermally conductive, electrically insulating material comprises alumina.
References Cited (Backward Citations)
US3538038A
Cited
US3891594A
Cited
US3813361A
Cited
US4016130A
Cited
JPS559634A
Cited
US4259412A
Cited
US4353958A
Cited
SU905230A1
Cited
US4555533A
Cited
US4489487A
Cited
JPS57212223A
Cited
JPS57212222A
Cited
US4543366A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-18 | 1993-12-18 | 1994-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-18 | 1997-12-18 | 1998-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-18 | 2001-12-18 | 2002-06-19 | $7700.00 | Window Closed / Lapsed |