Manufactured articles based on isotactic polypropylene having a highly oriented structure
Assignee: Montedison SpA
•
Filing: 1987-12-21
•
Granted: 1990-06-05
•
Expires: 2007-12-21
Abstract
Abstract This invention relates to composite manufactured articles formed by a set of uniaxially oriented isotatic polypropylene films, having a resistance to delamination of at least 0.4 kg/cm are prepared by heating under pressure a plurality of isotatic polypropylene films superimposed to each other and separated from each other by a non oriented polypropylene films. The oriented films show an orientation of the crystalline phase such as to produce X-ray scattering angles Δ× equal to or lower than 10°. The non oriented film show an orientation of the crystalline phase such as to produce X-ray scattering angles higher than 20°, at a temperature between a temperature equal to or higher than the melting temperature, measured in non restrain conditions, of the non oriented film and a temperature lower than the melting temperature, measured in restrained conditions, of the oriented films.
Inventors
- 👤 Paolo Corradini
- 👤 Claudio De Rosa
- 👤 Gaetano Guerra
- 👤 Luigi Nicolais
- 👤 Vittorio Petraccone
- 👤 Giancarlo Attalla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:32
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B29; B29C; B29C55/00; B29C55/02; B29C55/023; B29C55/04; B29C70/00; B29C70/04; B32B27/32; B29K; B29K2023/00; B29K2023/10; B29K2023/12; B32B2307/00; B32B2307/50; B32B2307/514; B32B2307/516; B32B2323/00; B32B2323/10; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
106 words
Multilayer thermoformed articles in the form of plates, sheets and tubes, consisting essentially of alternating superimposed layers made of uniaxially oriented polypropylene films and unoriented polypropylene films melt bonded to said uniaxially oriented films, said uniaxially oriented films having an orientation of their crystalline phase characterized by X-ray scattering angles (ΔX) equal to or lower than 10° and said unoriented films having an X-ray scattering angle equal to or greater than 20°, said multilayer thermoformed article having on the whole a high orientation characterized by an X-ray scattering angle equal to or lower than 10° and a delamination strength of at least 0.4 kg/cm 2 .
Claim 2
Dependent Claim
106 words
Multilayer thermoformed articles in the form of plates, sheets and tubes, consisting essentially of alternating superimposed layers made of uniaxially oriented polypropylene films and unoriented polypropylene films melt bonded to said uniaxially oriented films, said uniaxially oriented films having an orientation of their crystalline phase characterized by X-ray scattering angles (ΔX) equal to or lower than 10° and said unoriented films having an X-ray scattering angle equal to or greater than 20°, said multilayer thermoformed article having on the whole a high orientation characterized by an X-ray scattering angle equal to or lower than 10° and a delamination strength of at least 0.4 kg/cm 2 .
Claim 3
Dependent Claim
23 words
An article according to claim 1 wherein pairs of said uniaxially oriented films are separated by one or more of said unoriented films.
Claim 4
Dependent Claim
24 words
An article according to claim 2 wherein said pairs of uniaxially oriented films are arranged to as to be oriented in mutually perpendicular directions.
Claim 5
Dependent Claim
24 words
An article according to claim 2 wherein said pairs of uniaxially oriented films are arranged so as to be oriented in the same direction.
Claim 6
Dependent Claim
125 words
A multilayer thermoformed article in the form of plates, sheets and tubes having a high orientation characterized by an X-ray scattering angle equal to or lower than 10° and a delamination strength of at least 0.4 kg/cm 2 , which has been prepared by superimposing alternating layers of uniaxially oriented polypropylene films having an X-ray scattering angle equal to or lower than 10° and of unoriented polypropylene films having an X-ray scattering angle equal to or greater than 20°, and melt bonding said superimposed alternating layers by heating under a pressure of from 10 to 100 kg/cm 2 at a temperature between the melting temperature, measured in unrestrained conditions, of the unoriented films and the melting temperature, measured in restrained conditions, of the oriented films.
Claim 7
Dependent Claim
125 words
A multilayer thermoformed article in the form of plates, sheets and tubes having a high orientation characterized by an X-ray scattering angle equal to or lower than 10° and a delamination strength of at least 0.4 kg/cm 2 , which has been prepared by superimposing alternating layers of uniaxially oriented polypropylene films having an X-ray scattering angle equal to or lower than 10° and of unoriented polypropylene films having an X-ray scattering angle equal to or greater than 20°, and melt bonding said superimposed alternating layers by heating under a pressure of from 10 to 100 kg/cm 2 at a temperature between the melting temperature, measured in unrestrained conditions, of the unoriented films and the melting temperature, measured in restrained conditions, of the oriented films.
Claim 8
Dependent Claim
46 words
A multilayer article according to claim 5 wherein in said preparation process said heating has been carried out at a temperature ranging from about 5° C. above said melting temperature of the unoriented films to about 10° C. below said melting temperature of the oriented films.
Claim 9
Dependent Claim
19 words
A multilayer article according to claim 5 wherein in said preparation process said pressure is an applied external pressure.
Claim 10
Dependent Claim
22 words
A multilayer article according to claim 5 wherein in said preparation process said pressure is generated by tensions developed during said thermoforming.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-04 | 1993-12-04 | 1994-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-04 | 1997-12-04 | 1998-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-04 | 2001-12-04 | 2002-06-05 | $7700.00 | Window Closed / Lapsed |