US4929662A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the preparation of polymer particles possessing, implanted on their surface, amphophilic molecules carrying ion-forming or reactive groups, and a process for the preparation of a latex comprising these particles
Assignee: Prolabo SA
•
Filing: 1988-05-06
•
Granted: 1990-05-29
•
Expires: 2008-05-06
Abstract
Abstract Polymer particles possessing, implanted on their surface, amphiphilic molecules carrying ion-forming or reactive groups, and dispersions thereof, prepared by diffusing, into a previously prepared aqueous seeding dispersion of polymer particles, an organosoluble polymerization initiator, swelling the particles of the dispersion thus obtained by introducing a monomer composition comprising at least one monomer and at least one amphiphilic compound, and polymerizing the monomer composition.
Inventors
- 👤 Roger Hogenmuller
- 👤 Bernard Chauvel
- 👤 Jean-Claude Daniel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:17
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; G; G01; G01N; G01N33/00; G01N33/48; G01N33/50; G01N33/53; G01N33/543; G01N33/54313; C08J3/02
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
266 words
A process for the preparation of an aqueous dispersion of polymer particles possessing, implanted on their surface, amphiphilic molecules carrying ion-forming or reactive groups, comprising the following steps: (1) diffusing, into a previously prepared aqueous seeding dispersion of polymer particles, an organosoluble polymerization initiator having a solubility in water of from about 10 -3 to 10 -2 g/liter of water, said diffusion being carried out at a temperature below the decomposition temperature of said initiator; (2) swelling said particles of said dispersion thus obtained by introducing a monomer composition comprising (a) at least one monomer and (b) at least one amphiphilic compound having an HLB greater than or equal to 10 and a molecular weight greater than or equal to 400, wherein the hydrophilic block of said amphiphilic compound is a hydrophilic oligomer block terminated by at least one ion-forming or reactive group, said swelling being carried out by the monomer component (a) with a quantity of monomer composition less than the maximum quantity of said composition which said seeding dispersion can absorb, at a temperature below the decomposition temperature of said initiator; and (3) polymerizing said at least one monomer of said monomer composition at a temperature at least equal to the decomposition temperature of said initiator, the nature of said seeding polymer and the nature of said at least one monomer of said monomer composition, being such that the final polymer has a glass transition temperature Tg above about 40° C., said polymerzation resulting in the implantation of said amphiphilic compound (b) of the monomer composition in the surface layer of the polymer particles.
Claim 2
Dependent Claim
266 words
A process for the preparation of an aqueous dispersion of polymer particles possessing, implanted on their surface, amphiphilic molecules carrying ion-forming or reactive groups, comprising the following steps: (1) diffusing, into a previously prepared aqueous seeding dispersion of polymer particles, an organosoluble polymerization initiator having a solubility in water of from about 10 -3 to 10 -2 g/liter of water, said diffusion being carried out at a temperature below the decomposition temperature of said initiator; (2) swelling said particles of said dispersion thus obtained by introducing a monomer composition comprising (a) at least one monomer and (b) at least one amphiphilic compound having an HLB greater than or equal to 10 and a molecular weight greater than or equal to 400, wherein the hydrophilic block of said amphiphilic compound is a hydrophilic oligomer block terminated by at least one ion-forming or reactive group, said swelling being carried out by the monomer component (a) with a quantity of monomer composition less than the maximum quantity of said composition which said seeding dispersion can absorb, at a temperature below the decomposition temperature of said initiator; and (3) polymerizing said at least one monomer of said monomer composition at a temperature at least equal to the decomposition temperature of said initiator, the nature of said seeding polymer and the nature of said at least one monomer of said monomer composition, being such that the final polymer has a glass transition temperature Tg above about 40° C., said polymerzation resulting in the implantation of said amphiphilic compound (b) of the monomer composition in the surface layer of the polymer particles.
Claim 3
Dependent Claim
34 words
The process of claim 1, comprising the further step of removing at least a portion of any amphiphilic compound not implanted on the surface of said aqueous dispersion particles obtained in said step (3).
Claim 4
Dependent Claim
31 words
The process of claim 1, comprising the further step of isolating the polymer particles obtained in said step (3), said particles possessing molecules of said amphiphilic compound implanted on their surface.
Claim 5
Dependent Claim
43 words
The process of claim 2, comprising, subsequent to said removal of at least a portion of said amphiphilic compound, the further step of isolating said particles obtained after said removal step, said particles possessing molecules of said amphiphilic compound implanted on their surface.
Claim 6
Dependent Claim
37 words
The process of claim 1, wherein said seeding polymer comprises units derived from vinylaromatic monomers, alkyl esters of α, β-unsaturated acids, unsaturated esters of carboxylic acids, vinyl chloride, vinylidene chloride, dienes or monomers possessing nitrile functional groups.
Claim 7
Dependent Claim
41 words
The process of claim 1, wherein said monomer or monomers polymerized in said polymerization step (3) are vinylaromatic monomers, alkyl esters of α, β-unsaturated acids, unsaturated esters of carboxylic acids, vinyl chloride, vinylinene chloride, dienes or monomers possessing nitrile functional groups.
Claim 8
Dependent Claim
35 words
The process of claim 1, wherein said aqueous seeding dispersion has a solids content of from about 1 to 40% by weight, and comprises particles having a diameter of from about 0.1 to 15 microns.
Claim 9
Dependent Claim
25 words
The process of claim 1, wherein said seeding polymer represents from 50 to 95% by weight of the final polymer obtained in said step (3).
Claim 10
Dependent Claim
15 words
The process of claim 1, wherein said particles of said aqueous seeding dispersion are magnetizable.
Claim 11
Dependent Claim
20 words
The process of claim 1, wherein said initiator is dioctanoyl, peroxide, didecanoyl peroxide, dioctanoyl peroxidicarbonate, didecyl peroxidicarbonate or didodecyl peroxidicarbonate.
Claim 12
Dependent Claim
28 words
The process of claim 1, wherein the quantity of said initiator employed corresponds to about 0.1 to 10% by weight relative to the weight of said monomer composition.
Claim 13
Dependent Claim
38 words
The process of claim 1, wherein said diffusion step (1) is carried out by bringing said aqueopus seeding dispersion into contact, while stirring, with said initiator, said initiator having been preemulsified by homogenization in water containing an emulsifier.
Claim 14
Dependent Claim
38 words
The process of claim 1, wherein said diffusion step (1) is carried out at a temperature which is below the decomposition temperature of said initiator, but is sufficiently high for said initiator to be in the liquid state.
Claim 15
Dependent Claim
98 words
The process of claim 1, wherein said amphiphilic compound comprises a hydrophilic polyoxyalkylene oligomer block comprising from 5 to 100 C 2 -C 3 oxyalkylene units or a hydrophilic polycarboxyethylene and/or polyamidoethylene and/or polycyanoethylene oligomer block comprising from 4 to pb 50 carboxyethylene and/or amidoethylene and/or cyanoethylene units, said hydrophilic oligomer block being terminated by at least one --OH, --SO 3 H, --COOH, --CHO, --φCH 2 C1, --NH 2 , --NR 2 , --NR 3 .sup.⊕ (R being a C 1 --C 2 --alkyl radical), --CONH 2 , --NH--NH 2 , --NH--CO--NH--NH 2 , --SH, or ##STR5## group.
Claim 16
Dependent Claim
31 words
The process of claim 1, wherein the quantity of said amphiphilic compound employed is such that it represents about 10 -5 to 10 -1 mole per 100 g of final polymer.
Claim 17
Dependent Claim
27 words
The process of claim 1, wherein said swelling step (2) is carried out at a temperature on the same order as that of said diffusion step (1).
Claim 18
Dependent Claim
23 words
The process of claim 1, wherein said polymerization step (3) is carried out at a temperature above the decomposition temperature of said initiator.
Claim 19
Dependent Claim
23 words
A method of using the polymer particles obtained by the process of claim 3, wherein said particles are employed in a biological application.
Claim 20
Dependent Claim
25 words
A method of using the dispersion of polymer particles obtained by the process of claim 1, wherein said dispersion is employed in a biological application.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-28 | 1993-11-27 | 1994-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-28 | 1997-11-27 | 1998-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-28 | 2001-11-27 | 2002-05-29 | $7700.00 | Window Closed / Lapsed |