Method of manufacturing an optical fiber cable and a cable obtained by the method
Assignee: GENERALE Cie SA
•
Filing: 1988-10-17
•
Granted: 1990-05-29
•
Expires: 2008-10-17
Abstract
Abstract The method is intended to provide cables (10) having an optical fiber (1) and suitable for mechanically severe environments, while remaining small in section. Heretofore, the mechanical strength of optical fiber cables has been obtained by plastic structures of considerable cross-sectional area and reinforced by metal strands or by glass fibers. In the method of the present invention, the reinforcing is obtained by metal composites (3) having very high mechanical strength and very small diameter, said composites extending parallel to the fiber (1).
Inventors
- 👤 Patrick Dubots
- 👤 Denis Legat
- 👤 Raymond Vic
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:51
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/44; G02B6/4401; G02B6/4429; G02B6/443; G02B6/4432; G02B6/4402; G02B6/4479; G02B6/449; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/812; Y10S505/813; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2962
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
183 words
A method of manufacturing a cable comprising an assembly of at least one optical fiber and metal reinforcing elements extending parallel to said fiber, said assembly being coated with a coating of plastic material, the method including the improvements whereby: strands having a diameter of between 0.06 mm and 0.5 mm and constituted by elementary metal filaments are selected for the reinforcing elements; the optical fiber is coated with a substance preventing it from subsequently adhering to said plastic coating material; said fiber is placed between a plurality of strands parallel with said fiber to form a bundle of component parts; the bundle formed in this way is passed through a set of successive combs and dies in order to bring the component parts of said bundle closer together while maintaining a degree of longitudinal traction on said components; and a resin is deposited on said bundle by electrostatic powdering, and is then melted by passing through an oven at a temperature of less than 250 degrees C. for about 1 minute to form said plastic coating and solidified to encapsulate said bundle.
Claim 2
Independent Claim
183 words
A method of manufacturing a cable comprising an assembly of at least one optical fiber and metal reinforcing elements extending parallel to said fiber, said assembly being coated with a coating of plastic material, the method including the improvements whereby: strands having a diameter of between 0.06 mm and 0.5 mm and constituted by elementary metal filaments are selected for the reinforcing elements; the optical fiber is coated with a substance preventing it from subsequently adhering to said plastic coating material; said fiber is placed between a plurality of strands parallel with said fiber to form a bundle of component parts; the bundle formed in this way is passed through a set of successive combs and dies in order to bring the component parts of said bundle closer together while maintaining a degree of longitudinal traction on said components; and a resin is deposited on said bundle by electrostatic powdering, and is then melted by passing through an oven at a temperature of less than 250 degrees C. for about 1 minute to form said plastic coating and solidified to encapsulate said bundle.
Claim 3
Dependent Claim
59 words
A manufacturing method according to claim 1, wherein each of said elementary filaments is made of a material selected from the group consisting of niobium-titanium, tantalum, niobium, and stainless steel; embedded in a material selected from the group consisting of copper, cupronickel, and aluminum; and with the diameter of an elementary fiber lying between 0.1 microns and 0.5 microns.
Claim 4
Dependent Claim
22 words
A manufacturing method according to claim 1, wherein said optical fiber is a glass fiber and is initially coated with silicone oil.
Claim 5
Dependent Claim
37 words
A manufacturing method according to claim 1, wherein the longitudinal traction applied to said bundle while it is being passed through said combs, dies, and an electrostatic powdering enclosure corresponds substantially to 50% of its elastic limit.
Claim 6
Dependent Claim
26 words
A manufacturing method according to claim 1, wherein the resin is one material selected from the group consisting of a thermosetting resin and a thermoplastic resin.
Claim 7
Dependent Claim
26 words
A manufacturing method according to claim 5, wherein the resin comprises powder grains having a diameter lying in the range of 20 microns to 80 microns.
Claim 8
Dependent Claim
22 words
A manufacturing method according to claim 1, wherein the electrostatic powdering is performed with a charging voltage of more than 50K volts.
Claim 9
Dependent Claim
24 words
A cable obtained by the method of claim 1, wherein a diameter of the cable lies in a range 0.5 mm to 1 mm.
Claim 10
Dependent Claim
25 words
A cable according to claim 8, comprising an optical fiber surrounded by reinforcing strands having diameters lying in a range 0.08 mm to 0.2 mm.
Claim 11
Dependent Claim
25 words
A cable according to claim 9, wherein each strand comprises several tens of thousands of elementary filaments each having a diameter of about 0.5 microns.
Claim 12
Dependent Claim
25 words
A cable according to claim 9, wherein each strand comprises several hundreds of thousands of elementary filaments each having a diameter of about 0.1 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-28 | 1993-11-27 | 1994-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-28 | 1997-11-27 | 1998-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-28 | 2001-11-27 | 2002-05-29 | $7700.00 | Window Closed / Lapsed |