Ceramic bodies formed from partially stabilized zirconia
Assignee: Selee Corp
•
Filing: 1989-09-18
•
Granted: 1990-05-08
•
Expires: 2009-09-18
Abstract
Abstract The present invention relates to ceramic bodies suitable for use in high temperature applications such as molten metal filters and kiln furniture. The ceramic bodies are formed from partially stabilized zirconia and are characterized by the presence of from about 12% to about 80% by weight zirconia in a monoclinic phase and the balance essentially in a cubic phase at room temperature. The ceramic bodies possess an excellent combination of physical properties including high temperature strength and thermal shock resistance. The invention also relates to the process for forming the ceramic bodies and the thixotropic ceramic slurry used therein.
Inventors
- 👤 Richard Everhart
- 👤 Paul Bosomworth
- 👤 Kenneth Butcher
- 👤 Matthias Hoffmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:20
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/06; C04B35/00; C04B35/01; C04B35/48; C04B35/486; B; B01; B01D; B01D39/00; B01D39/14; B01D39/20; B01D39/2068; B01D39/2093; C04B35/49; C04B38/0615; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T428/24165
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
161 words
A process for preparing a high temperature resistant ceramic body which comprises: forming an aqueous thixotropic slurry having a solids content consisting of essentially of from about 30% to about 98% by weight monoclinic zirconia, from about 0.5% to about 5% by weight of a stabilizing material and up to about 8.5% by weight of a binder material and the balance water; impregnating a porous body with said slurry by immersing said body in said slurry; drying said impregnated body; heating said impregnated porous body at an elevated temperature of less than or equal to about 2000° C. for about 15 minutes to about 10 hours and thereby producing a ceramic body from about 12% to about 80% by weight of said zirconia in a monoclinic phase and from about 20% to about 88% by weight of said zirconia in a cubic phase at room temperature so as to at least partially stabilize said zirconia and to form said ceramic body.
Claim 2
Dependent Claim
161 words
A process for preparing a high temperature resistant ceramic body which comprises: forming an aqueous thixotropic slurry having a solids content consisting of essentially of from about 30% to about 98% by weight monoclinic zirconia, from about 0.5% to about 5% by weight of a stabilizing material and up to about 8.5% by weight of a binder material and the balance water; impregnating a porous body with said slurry by immersing said body in said slurry; drying said impregnated body; heating said impregnated porous body at an elevated temperature of less than or equal to about 2000° C. for about 15 minutes to about 10 hours and thereby producing a ceramic body from about 12% to about 80% by weight of said zirconia in a monoclinic phase and from about 20% to about 88% by weight of said zirconia in a cubic phase at room temperature so as to at least partially stabilize said zirconia and to form said ceramic body.
Claim 3
Dependent Claim
28 words
A process according to claim 1 wherein said heating step comprises heating said body to a temperature in the range of about 1500° C. to about 1700° C.
Claim 4
Dependent Claim
38 words
A process according to claim 2 wherein said slurry forming step comprises: dry blending said monoclinic zirconia and said stabilizing material; and adding a water solution to said dry blended zirconia and stabilizing material to form said slurry.
Claim 5
Dependent Claim
67 words
A process according to claim 3 wherein said slurry forming step further comprises: dispersing said binder material in water at a temperature in the range of from about 20° C. to about 90° C. so as to form an aqueous solution; mixing said aqueous solution for up to 5 minutes; and said adding step comprises adding said aqueous solution to said dry blended zirconia and stabilizing material.
Claim 6
Dependent Claim
25 words
A process according to claim 3 wherein said slurry forming step further comprises: agitating said slurry for from about 1 minute to about 30 minutes.
Claim 7
Dependent Claim
57 words
A process according to claim 4 wherein: said dry blending step comprises blending said zirconia with a material selected from the group consisting of magnesia, calcia, ceria, titania, and mixtures thereof; and said dispersing step comprises dispersing a material selected from the group consisting of a starch, a gum, magnesium acetate, and mixtures thereof in said water.
References Cited (Backward Citations)
US3946039A
Cited
US3947363A
Cited
US4035191A
Cited
US4024212A
Cited
US4298385A
Cited
US4265659A
Cited
US4391918A
Cited
US4748138A
Cited
US4760038A
Cited
US4568595A
Cited
US4610832A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |