US4923650A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Breathable microporous film and methods for making it
Assignee: Applied Extrusion Technologies Inc
•
Filing: 1988-07-27
•
Granted: 1990-05-08
•
Expires: 2008-07-27
Abstract
Abstract A soft, flexible, microporous film is provided having high tensile strength and good air and water vapor transmission rates therethrough while being substantially impenetrable to liquid water. This film is prepared by stretching a casting of a composition of a polyolefin and high levels of CaCO 3 or glass beads and calcium stearate in two directions from 1.5-7 times in each direction to produce a film having a Gurley porosity of from 0.1 to 85 seconds. This film is especially useful for disposable items such as feminine panty liners, diapers, bed sheets, and hospital gowns. When glass beads are substituted for the CaCO 3 , the film is useful for battery separators.
Inventors
- 👤 Mitchell K. Antoon, Jr.
- 👤 David J. Hill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 19:12
CPC Classifications
A; A61; A61F; A61F13/00; A61F13/15; A61F13/15577; A61F13/15707; A61F13/15731; C; C08; C08K; C08K3/00; C08K3/01; C08K3/013; A61F13/51; A61F13/514; A61F13/51456; A61F13/51458; A61F13/5146; A61F13/51462; A61L; A61L15/00; A61L15/16; A61L15/18; A61L15/22; A61L15/24; B; B29; B29C; B29C55/00; B29C55/005; C08J; C08J5/00; C08J5/18; C08K7/00; C08K7/16; C08K7/18; C08K7/20; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/489; A47; A47G; A47G9/00; A47G2009/001; A61F13/51401; A61F2013/51409; A61F2013/51411; A61F2013/51415; B29K; B29K2105/00; B29K2105/04; B29K2105/06; B29K2105/16; C08J2323/00; C08J2323/02; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10S; Y10S264/00; Y10S264/06
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
152 words
A method of preparing a breathable microporous polymeric film having the composition of 20-37% by weight of a polymer or copolymer of an α-olefin having 1-8 carbons or mixtures thereof, 60-75% by weight of calcium carbonate or glass beads, 0.1-3.0% by weight of calcium stearate and, optionally, 0-2% by weight of a UV light, oxygen, and heat stabilizer by preparing a melt blend of the ingredients, maintaining the moisture level in the melt blend below 700 ppm prior to extruding a casting, and based on the polymer or copolymer used, stretching the casting in two directions of from 1.5 to 7 times in each direction in a temperature range of from about 20° to about 160° C. thereby producing the breathable microporous film having a Gurley Porosity of from 0.1 to 85 seconds so that the film has good air and water vapor transmission rates but is substantially imPenetrable by liquid water.
Claim 2
Independent Claim
152 words
A method of preparing a breathable microporous polymeric film having the composition of 20-37% by weight of a polymer or copolymer of an α-olefin having 1-8 carbons or mixtures thereof, 60-75% by weight of calcium carbonate or glass beads, 0.1-3.0% by weight of calcium stearate and, optionally, 0-2% by weight of a UV light, oxygen, and heat stabilizer by preparing a melt blend of the ingredients, maintaining the moisture level in the melt blend below 700 ppm prior to extruding a casting, and based on the polymer or copolymer used, stretching the casting in two directions of from 1.5 to 7 times in each direction in a temperature range of from about 20° to about 160° C. thereby producing the breathable microporous film having a Gurley Porosity of from 0.1 to 85 seconds so that the film has good air and water vapor transmission rates but is substantially imPenetrable by liquid water.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the moisture level is maintained below 300 ppm.
Claim 4
Dependent Claim
15 words
The method of claim 2 wherein the composition has 65 to 75% of calcium carbonate.
Claim 5
Dependent Claim
40 words
The method of claim 3 wherein the polymer is polyethylene or polybutylene and the casting is stretched in two directions from 1.5 to 5 times in each direction in a temperature range of from about 20° to about 105° C.
Claim 6
Dependent Claim
38 words
The method of claim 3 wherein the polymer is polypropylene and the casting is stretched in two directions from 4 to 7 times in each direction in a temperature range of from about 130° to about 160° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |