US4916688A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Data storage method using state transformable materials
Assignee: International Business Machines Corp
•
Filing: 1988-03-31
•
Granted: 1990-04-10
•
Expires: 2008-03-31
Abstract
Abstract A unique method for recording, reading and erasing data bits in a data storage device is described. Using extended scanning tunneling microscopy (STM) techniques, a tunneling electron current by resistive heating selectively melts discrete areas of a state-transformable film; then heat is dissipated rapidly, writing data bits by changing the film in said areas from a first state to a second state wherein an electronic property, such as conductance, work function or band gap, in said areas is changed. Again, using extended STM techniques, the effect of this changed electronic property of said film on the tunneling current is measured for reading the written data bits. Minimizing the effect of blemishes on the material is effected, during operation in STM constant current mode by measuring dI/dV or dI/ds, and during operation in STM variable current (constant gap) mode by measuring (dI/dV)/I or (dI/ds)/I. Also by using extended STM techniques, data bits can be selectively erased by resistance heating the film to a temperature higher than the crystallization temperature for a sufficient period of time, restoring selected discrete areas to said first state and each affected electronic property substantially to its original condition.
Inventors
- 👤 John S. Foster
- 👤 Kurt A. Rubin
- 👤 Daniel Rugar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:16
CPC Classifications
G; G11; G11B; G11B9/00; G11B9/12; G11B9/14; G11B9/1463; G11B9/149; B; B82; B82Y; B82Y10/00; G11B9/1472; Y; Y10; Y10S; Y10S977/00; Y10S977/902; Y10S977/932; Y10S977/943; Y10S977/947
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
144 words
A method of recording and reading data bits in a data storage device, said method comprising the steps of: providing a storage medium comprising a substrate and a film of state-transformable material thereon; using an STM probe tip and voltage pulses that induce current pulses of sufficient magnitude, selectively heating discrete areas of the film to a preselected temperature, and then cooling said areas at a rapid rate for changing the material in said areas from a first state to a second state wherein an electronic property is changed in said discrete areas from one value to a substantially different value, for thereby causing data bits to be written at said areas; and using the probe tip and tunneling current sensing circuitry, sensing the film for reading data bits at said discrete areas where said electronic property had been changed to said different value.
Claim 2
Independent Claim
144 words
A method of recording and reading data bits in a data storage device, said method comprising the steps of: providing a storage medium comprising a substrate and a film of state-transformable material thereon; using an STM probe tip and voltage pulses that induce current pulses of sufficient magnitude, selectively heating discrete areas of the film to a preselected temperature, and then cooling said areas at a rapid rate for changing the material in said areas from a first state to a second state wherein an electronic property is changed in said discrete areas from one value to a substantially different value, for thereby causing data bits to be written at said areas; and using the probe tip and tunneling current sensing circuitry, sensing the film for reading data bits at said discrete areas where said electronic property had been changed to said different value.
Claim 3
Dependent Claim
79 words
The method of claim 1, further including the step of: using the probe tip and a voltage pulse that induces a current of sufficient magnitude, heating selected discrete areas of the film to a temperature lower than said preselected temperature for a period of time sufficient to allow the material to return to said first state and restore said electronic property to substantially said one value, for thereby causing selective erasure of data bits at said selected discrete areas.
Claim 4
Dependent Claim
34 words
The method of claim 1, wherein following each such selective heating, the material and substrate in combination inherently dissipate heat at said rapid rate to inhibit restoration of the material to its first state.
Claim 5
Dependent Claim
17 words
The method of claim 1, wherein said preselected temperature is above the melting temperature of the material.
Claim 6
Dependent Claim
24 words
The method of claim 1, wherein said film material is stable in one of said states and metastable in the other of said states.
Claim 7
Dependent Claim
24 words
The method of claim 1, wherein said film material is crystalline in one of said states and amorphous in the other of said states.
Claim 8
Dependent Claim
26 words
The method of claim 1, wherein said film material is stable crystalline in one of said states or metastable crystalline in the other of said states.
Claim 9
Dependent Claim
22 words
The method of claim 1, wherein the electronic property is taken from the group consisting of conductance, work function and band gap.
Claim 10
Dependent Claim
86 words
The method of claim 1, further including the steps, during the sensing step, of: applying to the tip a DC bias voltage at which the slope, dI/dV, of the current vs. voltage curve for the film differs significantly according to the state of the film; superimposing an AC voltage on the DC bias voltage; and sensing the amplitude of the AC component of the readout signal from the film, and hence the value of dI/dV, to determine the conductance and hence state of the discrete areas.
Claim 11
Dependent Claim
34 words
The method of claim 9, further including the step of: operating the STM probe in constant current mode, whereby the effect of blemishes in topography of the film on said readout signal is minimized.
Claim 12
Dependent Claim
34 words
The method of claim 9, further including the step, during amplitude sensing, of: mixing and then filtering the AC voltage signal and the readout signal from the film to provide the dI/dV readout signal.
Claim 13
Dependent Claim
62 words
The method of claim 9, further including the steps of: operating the STM probe in a variable current mode; sensing the STM tunneling current, I, as read from the film; and passing said current, I, and the dI/dV signal through divider circuitry to provide a (dI/dV)/I readout signal in which the effect of blemishes in the topography of the film is minimized.
Claim 14
Dependent Claim
53 words
The method of claim 1, further including the steps, during the sensing step, of: modulating the spacing, s, between the tip and film; measuring the tunneling current, I; and measuring dI/ds to provide a readout signal indicative of changes in work function of the film and hence the state of the discrete areas.
Claim 15
Dependent Claim
35 words
The method of claim 13, further including the step of: operating the STM probe in a constant current mode; whereby the effect of blemishes in topography of the film on said readout signal is minimized.
Claim 16
Dependent Claim
40 words
The method of claim 13, further including the steps of: operating the STM probe in a variable current mode; and measuring (dI/ds)/I to provide a readout signal in which the effect of blemishes in topography of the film is minimized.
Claim 17
Dependent Claim
18 words
The method of claim 1, wherein the probe tip is positive relative to the polarity of the film.
Claim 18
Dependent Claim
71 words
The method according to claim 1, wherein the film material is taken from the group consisting of GeTe, (GeTe) 100-z Sn z , where z is between 0 and 30, Sb 2 Te 3 , GaSb, Sb 2 Se, SnTe, PbTe, SbSe, BiSe, GeSe, Te 50 Ge.sub.(50-x) Sn x , where x is between 0 and 10, where y is between 0 and 100, and doped and undoped Ge and Si.
Claim 19
Dependent Claim
11 words
The method of claim 7, wherein the film material comprises AgZn.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-09 | 1993-10-09 | 1994-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-09 | 1997-10-09 | 1998-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-09 | 2001-10-09 | 2002-04-10 | $7700.00 | Window Closed / Lapsed |