Methods of making composite ceramic articles
Assignee: Lanxide Technology Co LP
•
Filing: 1988-11-01
•
Granted: 1990-04-10
•
Expires: 2008-11-01
Abstract
Abstract A method of making self-supporting ceramic composite structures having filler embedded therein includes infiltrating a permeable mass of filler with polycrystalline material comprising an oxidation reaction product obtained by oxidation of a parent metal such as aluminum and optionally containing therein non-oxidized constituents of the parent metal. The structure is formed by placing a parent metal adjacent to a permeable filler and heating the assembly to melt the parent metal and provide a molten body of parent metal which is contacted with a suitable vapor-phase oxidant. Within a certain temperature region and optionally aided by one or more dopants in or on the parent metal, molten parent metal will migrate through previously formed oxidation reaction product into contact with the oxidant, causing the oxidation reaction product to grow so as to embed the adjacent filler and provide the composite structure.
Inventors
- 👤 Marc S. Newkirk
- 👤 Andrew W. Urquhart
- 👤 Harry R. Zwicker
- 👤 H. Daniel Lesher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:52
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/119; C04B35/44; C04B35/443; C04B35/453; C04B35/457; C04B35/515; C04B35/58; C04B35/58007; C04B35/58014; C04B35/58028; C04B35/581; C04B35/584; C04B35/591; C04B35/622; C04B35/64; C04B35/65; C04B35/652; C04B35/71; C04B35/74; C04B35/76; C04B35/78; C04B35/80; C04B38/00; C04B38/009; C04B41/45; C04B41/50; C04B41/5025; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3205; C04B2235/3206; C04B2235/3215; C04B2235/3217; C04B2235/3222; C04B2235/3231; C04B2235/3232; C04B2235/3234; C04B2235/3236; C04B2235/34; C04B2235/3418; C04B2235/38; C04B2235/3804; C04B2235/3813; C04B2235/3817; C04B2235/3826; C04B2235/3852; C04B2235/3865; C04B2235/3886; C04B2235/40; C04B2235/401; C04B2235/402; C04B2235/404; C04B2235/407; C04B2235/42; C04B2235/428; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/522; C04B2235/5224; C04B2235/5236; C04B2235/524; C04B2235/5244; C04B2235/5252; C04B2235/5256; C04B2235/54; C04B2235/5418; C04B2235/5427; C04B2235/5436; C04B2235/5463; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/658; C04B2235/6582; C04B2235/6586; C04B2235/70; C04B2235/80; C04B2235/96; C04B2235/9669; C04B2235/9692
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
276 words
A method for producing a self-supporting ceramic composite structure comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with a vapor-phase oxidant; and (2) at least one filler embedded by said matrix, the method comprising the steps of: (a) positioning at least one parent metal comprising a material selected from the group consisting of aluminum, titanium, zirconium, silicon and tin adjacent to a permeable mass of filler and orienting said at least one parent metal and said filler relative to each other so that formation of said oxidation reaction product will occur in a direction towards and into said mass of filler, wherein least two dopant are alloyed with said parent metal; (b) heating said parent metal to a temperature above its melting point but below the melting point of its oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said temperature to form said oxidation reaction product, and at said temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten parent metal and said oxidant, to draw molten parent metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product; and (c) continuing said reacting for a time sufficient to embed at least a portion of the filler within said polycrystalline material.
Claim 2
Independent Claim
276 words
A method for producing a self-supporting ceramic composite structure comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with a vapor-phase oxidant; and (2) at least one filler embedded by said matrix, the method comprising the steps of: (a) positioning at least one parent metal comprising a material selected from the group consisting of aluminum, titanium, zirconium, silicon and tin adjacent to a permeable mass of filler and orienting said at least one parent metal and said filler relative to each other so that formation of said oxidation reaction product will occur in a direction towards and into said mass of filler, wherein least two dopant are alloyed with said parent metal; (b) heating said parent metal to a temperature above its melting point but below the melting point of its oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said temperature to form said oxidation reaction product, and at said temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten parent metal and said oxidant, to draw molten parent metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product; and (c) continuing said reacting for a time sufficient to embed at least a portion of the filler within said polycrystalline material.
Claim 3
Dependent Claim
14 words
The method of claim 1, wherein said at least one parent metal comprises aluminum.
Claim 4
Dependent Claim
38 words
The method of claim 2, wherein said at least two dopants comprise at least two materials selected from the group consisting of magnesium, zinc, silicon, germanium, tin, lead, boron, sodium, lithium, calcium, phosphorus, yttrium and rare earth metals.
Claim 5
Dependent Claim
44 words
The method of claim 2, wherein said at least two dopants comprise a source of at least one of magnesium and zinc, plus a source of at least one of silicon, lead, tin, germanium, sodium, lithium, calcium, boron, phosphorus, yttrium and rare earth metals.
Claim 6
Dependent Claim
30 words
The method of claim 1, wherein said at least one parent metal comprises aluminum and said at least two dopants comprise a source of magnesium and a source of silicon.
Claim 7
Dependent Claim
42 words
The method of claim 1, wherein said filler comprises at least one material selected from the group consisting of aluminum oxide, silicon carbide, silicon aluminum oxynitride, zirconium oxide, zirconium boride, titanium nitride, barium titanate, boron nitride, silicon nitride, iron-chromium-aluminum alloy and aluminum.
Claim 8
Dependent Claim
31 words
The method of claim 1, wherein said filler comprises at least one material selected from the group consisting of hollow bodies, particulates, fibers, whiskers, spheres, plates, aggregate, rods, bars, and platelets.
Claim 9
Dependent Claim
52 words
The method of claim 1, wherein said oxidant comprises at least one material selected from the group consisting of an oxygen-containing gas, a nitrogen-containing gas, a halogen, sulphur, phosphorus, arsenic, carbon, boron, selenium, tellurium an H 2 /H 2 O mixture, methane, ethane, propane, acetylene, ethylene, propylene, and a CO/CO 2 mixture.
Claim 10
Independent Claim
350 words
A method for producing a self-supporting ceramic composite structure comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with a vapor-phase oxidant; and (2) at least one filler embedded by said matrix, the method comprising the steps of: (a) positioning a parent metal comprising aluminum adjacent to a permeable mass of filler material which comprises at least one material selected from the group consisting of aluminum oxide, silicon carbide, silicon aluminum oxynitride, zirconium oxide, zirconium boride, titanium nitride, barium titanate, boron nitride, silicon nitride, iron-chromiumaluminum alloy and aluminum, said filler being in the form of at least one material selected from the group consisting of hollow bodies, particulates, fibers, whiskers, spheres, plates, aggregate, rods, bars, and platelets, said aluminum parent metal being oriented relative to said filler so that formation of said oxidation reaction product will occur in a direction towards and into said mass of filler, wherein said aluminum parent metal is combined with at least one dopant comprising a material selected from the group consisting of at least one of magnesium, zinc, silicon, germanium, tin, lead, boron, sodium, lithium, calcium, phosphorus, yttrium, and rare earth metals; (b) heating said aluminum parent metal to a temperature above its melting point but below the melting point of its oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said temperature to form said oxidation reaction product, and at said temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product; (c) continuing said reacting for a time sufficient to embed at least a portion of the filler within said polycrystalline material.
Claim 11
Independent Claim
350 words
A method for producing a self-supporting ceramic composite structure comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with a vapor-phase oxidant; and (2) at least one filler embedded by said matrix, the method comprising the steps of: (a) positioning a parent metal comprising aluminum adjacent to a permeable mass of filler material which comprises at least one material selected from the group consisting of aluminum oxide, silicon carbide, silicon aluminum oxynitride, zirconium oxide, zirconium boride, titanium nitride, barium titanate, boron nitride, silicon nitride, iron-chromiumaluminum alloy and aluminum, said filler being in the form of at least one material selected from the group consisting of hollow bodies, particulates, fibers, whiskers, spheres, plates, aggregate, rods, bars, and platelets, said aluminum parent metal being oriented relative to said filler so that formation of said oxidation reaction product will occur in a direction towards and into said mass of filler, wherein said aluminum parent metal is combined with at least one dopant comprising a material selected from the group consisting of at least one of magnesium, zinc, silicon, germanium, tin, lead, boron, sodium, lithium, calcium, phosphorus, yttrium, and rare earth metals; (b) heating said aluminum parent metal to a temperature above its melting point but below the melting point of its oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said temperature to form said oxidation reaction product, and at said temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product; (c) continuing said reacting for a time sufficient to embed at least a portion of the filler within said polycrystalline material.
Claim 12
Dependent Claim
52 words
The method of claim 9, wherein said oxidant comprises at least one material selected from the group consisting of an oxygen-containing gas, a nitrogen-containing gas, a halogen, sulphur, phosphorus, arsenic, carbon, boron, selenium, tellurium, an H 2 /H 2 O mixture, methane, ethane, propane, acetylene, ethylene, propylene, and a CO/CO 2 mixture.
References Cited (Backward Citations)
US1362237A
Cited
US2741822A
Cited
US3108887A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3262763A
Cited
US3419404A
Cited
US3473987A
Cited
US3551101A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3514271A
Cited
US3649310A
Cited
US3669695A
Cited
US3864154A
Cited
US3973977A
Cited
US4354991A
Cited
US4591537A
Cited
EP0116809A1
Cited
US4478785A
Cited
EP0155831A2
Cited
EP0169067A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-09 | 1993-10-09 | 1994-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-09 | 1997-10-09 | 1998-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-09 | 2001-10-09 | 2002-04-10 | $7700.00 | Window Closed / Lapsed |