Vacuum bagging process for fiber reinforced thermoplastics

Claim 2

A process for simultaneously forming a plurality of flattened consolidated composite sheets, each of said sheets comprising a fiber reinforced thermoplastic resin, said process comprising the steps of: (A) supporting on a substantially flat, rigid substrate surface a stack comprising a plurality of interfacially adjacently arranged composite layers, at least two adjacent said layers being separated from one another by an interposed metallic sheet, said stack further including a metallic sheet positioned adjacent the outside surface of each of the topmost said layer and the bottommost said layer, each said layer comprising a thermoplastic resin and reinforcing fibers, said substrate surface being thermally stable at a temperature above the melting point of said thermoplastic resin, (B) overlaying said stack with an air-impermeable sheet and sealing said air-impermeable sheet peripherally around said stack to said substrate surface, said air-impermeable sheet being thermally stable to a temperature above the melting point of said thermoplastic resin, thereby to produce a layup comprised of said substrate surface, said stack, and said air-impermeable sheet, (C) heating said layup in a heating zone to a temperature sufficient to melt said thermoplastic resin, said heating being carried out by impinging heated gas against said layup, (D) applying suction between said air-impermeable sheet and said substrate surface, thereby to urge said sheet towards said substrate surface and achieve wet-out of said reinforcing fibers by said molten thermoplastic resin, and (E) cooling said layup in a cooling zone to a temperature below the melting point of said thermoplastic resin, said cooling being carried out by impinging gas cooled to below about 100° F. against the resulting said layup, thereby to form said plurality of consolidated composite sheets.

Claim 3

A process of claim 1 further comprising after step (A) and before step (B) moving said layup into a convection oven zone, wherein said heating step is carried out.

Claim 4

A process of claim 2 wherein said stack comprises from 2 to about 20 said layers.

Claim 5

A process of claim 3 wherein said metallic sheets separating said layers are each comprised of stainless steel.

Claim 6

A process of claim 4 wherein said stainless steel sheets each have a thickness in the range of from about 0.2 to about 2 millimeters and are formed from a 400 series stainless steel.

Claim 7

A process of claim 4 wherein said air-impermeable sheet is comprised of aluminum foil.

Claim 8

A process of claim 6 wherein layers of release cloth separate each of said layers from each of said stainless steel sheets, and layers of breather cloth separate each of said layers of release cloth from each of said stainless steel sheets.

Claim 9

A process of claim 7 wherein said reinforcing fibers are selected from the group consisting of glass fibers, carbon fibers, and aramid fibers, and said reinforcing fibers are in fabric form; and wherein said thermoplastic resin comprises a poly(arylene sulfide) resin initially in a sheetlike form.

Claim 10

A process of claim 2 wherein said convection oven zone utilizes a plurality of heating gas jets, wherein the gas from said heating jets has a temperature between about 850° F. and 1250° F. and, for said cooling step, a plurality of cooling gas jets are employed wherein the gas from said cooling jets has a temperature below about 100° F., and said thermoplastic resin is poly(arylene sulfide).

Claim 11

A process of claim 1 wherein said consolidated composite sheets each have a thickness in the range of from about 0.25 to about 25 millimeters.

Claim 12

A process for forming a flattened consolidated composite sheet which comprises a fiber reinforced thermoplastic resin, said process comprising the steps of (A) supporting on a substantially flat, rigid substrate surface a layer of a mixture, said mixture comprising on a 100 weight percent basis from about 20 to about 80 weight percent of thermoplastic resin, and correspondingly from about 80 to about 20 weight percent of reinforcing fibers having an average length greater than about 1 centimeter and a length to diameter ratio greater than about 20, and said substrate surface being thermally stable at a temperature above the melting point of said thermoplastic resin, (B) overlaying said layer with an air-impermeable sheet and sealing said air-permeable sheet peripherally around said layer to said substrate surface, said air-impermeable sheet being thermally stable at a temperature above the melting point of said thermoplastic resin, thereby to produce a layup comprised of said substrate surface, said layer, and said air-impermeable sheet, (C) heating said layup in a heating zone to a temperature sufficient to melt said thermoplastic resin, said heating being carried out by impinging heated gas against said layup, (D) applying suction between said air-impermeable sheet and said substrate surface, thereby to urge said air-impermeable sheet towards said substrate surface and achieve wet-out of said reinforcing fibers with said molten thermoplastic resin, and (E) cooling said layup in a cooling zone to a temperature below the melting point of said thermoplastic resin, said cooling being carried out by impinging gas cooled to below about 100° F. against said layup, thereby to form said consolidated composite sheet, wherein said substrate surface is defined by an upper surface of a stainless steel sheet, a second stainless steel sheet is positioned between said air-impermeable sheet and said layer, said air-impermeable sheet is formed by aluminum foil, said stainless steel sheets are each formed from a 400 series stainless steel and have a thickness in the range of about 0.2 to about 2 millimeters, and said aluminum foil forming said air-impermeable sheet is so sealed to said stainless steel sheet forming said substrate surface with a polymeric sealant and wherein said process further comprises cooling said polymeric sealant with a flow of cool gas during said heating.

Claim 13

A process for forming a flattened consolidated composite sheet which comprises a fiber reinforced thermoplastic resin, said process comprising the steps of (A) supporting on a substantially flat, rigid substrate surface a layer of a mixture, said mixture comprising on a 100 weight percent basis from about 20 to about 80 weight percent of thermoplastic resin, and correspondingly from about 80 to about 20 weight percent of reinforcing fibers having an average length greater than about 1 centimeter and a length to diameter ratio greater than about 20, and said substrate surface being thermally stable at a temperature above the melting point of said thermoplastic resin, (B) overlaying said layer with an air-impermeable sheet and sealing said air-permeable sheet peripherally around said layer to said substrate surface, said air-impermeable sheet being thermally stable at a temperature above the melting point of said thermoplastic resin, thereby to produce a layup comprised of said substrate surface, said layer, and said air-impermeable sheet, (C) heating said layup in a heating zone to a temperature sufficient to melt said thermoplastic resin, said heating being carried out by impinging heated gas against said layup, (D) applying suction between said air-impermeable sheet and said substrate surface, thereby to urge said air-impermeable sheet towards said substrate surface and achieve wet-out of said reinforcing fibers with said molten thermoplastic resin, and (E) cooling said layup in a cooling zone to a temperature below the melting point of said thermoplastic resin, said cooling being carried out by impinging gas cooled to below about 100° F. against said layup, thereby to form said consolidated composite sheet, wherein said substrate surface is defined by an upper surface of a stainless steel sheet, a second stainless steel sheet is positioned between said air-impermeable sheet and said layer, said air-impermeable sheet is formed by aluminum foil, said stainless steel sheets are each formed from a 400 series stainless steel and have a thickness in the range of about 0.2 to about 2 millimeters, and said aluminum foil forming said air-impermeable sheet is so sealed to said stainless steel sheet forming said substrate surface with a polymeric sealant and wherein said process further comprises cooling said polymeric sealant with a flow of cool gas during said heating.

Claim 14

A process of claim 11 further comprising positioning a first release cloth between said layer and said substrate surface and positioning a second release cloth between said layer and said second stainless steel sheet, and wherein said first release cloth and said second release cloth are each textured on the surface thereof facing said layer, thereby to provide a gas flow path between said layer and said release cloths.

Claim 15

A process of claim 12 further comprising positioning a first breather cloth between said first release cloth and said substrate surface and positioning a second breather cloth between said second stainless steel sheet and said second release cloth.

Claim 16

A process of claim 13 wherein said release cloth has a thickness ranging from about 0.2 to 1 millimeter and contains poly(tetrafluroethylene).

Claim 17

A process of claim 11 wherein said layer comprises at least one sheet of a poly(arylene sulfide) resin and at least one sheet of a fiber reinforcement in the form of a fabric.

Claim 18

A process of claim 15 wherein said mixture comprises a prepreg of poly(arylene sulfide) containing said reinforcing fibers.

Claim 19

A process of claim 11 wherein said heating is conducted at a temperature between about 850° F. and 1250° F. and said thermoplastic resin comprises poly(arylene sulfide).